Effect of Temperature on Cathodic Reaction of 2205 Duplex Stainless Steel Corrosion in Brine
摘 要
利用电化学方法, 在不同温度下研究了2205双相不锈钢在卤水中腐蚀阴极反应的特性, 结果表明, 温度对氧在2205双相不锈钢表面的极限扩散电流密度影响显著, 极限扩散电流密度随温度的升高先增大后减小, 在76 ℃时达到最大值12.3 μA/cm2; 高温下的高盐度卤水对处于阴极保护电位下的2205双相不锈钢仍具有破坏性。
Abstract
Electrochemical methods were used to study the cathodic reaction characteristic of 2205 duplex stainless steel in brine at different temperatures. The results showed that temperature had an obvious effect on limiting current density which increased initially and decreased latter as the temperature raised, the maximum limiting current density of 12.3 μA/cm2 was attained at temperature of 76 ℃. Brine of high salinity at high temperatures had the ability to attack 2205 duplex stainless steel with the potential below the Ecorr.
中图分类号 TG174.3+6
所属栏目 试验研究
基金项目 四川省科技厅应用基础研究项目(2008JY0091-2); 四川理工学院创新基金项目(y2009019)
收稿日期 2010/10/14
修改稿日期 2010/12/16
网络出版日期
作者单位点击查看
备注龚敏, 教授,
引用该论文: FENG Min,GONG Min,ZHANG Yu,ZHANG Guo-hu. Effect of Temperature on Cathodic Reaction of 2205 Duplex Stainless Steel Corrosion in Brine[J]. Corrosion & Protection, 2011, 32(9): 691
共有人对该论文发表了看法,其中:
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】于辉, 孙明先, 马焱, 等. 活性氯在316L不锈钢电极表面的阴极行为研究[J]. 电化学, 2003, 9(1): 66-70.
【2】宋诗哲. 腐蚀电化学研究方法[M]. 北京:化学工业出版社, 1987.
【3】郭浩, 李光福, 蔡珣. 外加电位对X70管线钢在近中性pH溶液中的应力腐蚀破裂的影响[J]. 中国腐蚀与防护学报, 2004, 24(4):208-212.
【4】宋诗哲. 腐蚀电化学研究方法[M]. 北京:化学工业出版社, 1987.
【5】郭浩, 李光福, 蔡珣. 外加电位对X70管线钢在近中性pH溶液中的应力腐蚀破裂的影响[J]. 中国腐蚀与防护学报, 2004, 24(4):208-212.
【6】阿伦.J.巴德, 拉里.R.福克纳. 电化学方法原理和应用[M]. 北京:化学工业出版社, 2005.
【2】宋诗哲. 腐蚀电化学研究方法[M]. 北京:化学工业出版社, 1987.
【3】郭浩, 李光福, 蔡珣. 外加电位对X70管线钢在近中性pH溶液中的应力腐蚀破裂的影响[J]. 中国腐蚀与防护学报, 2004, 24(4):208-212.
【4】宋诗哲. 腐蚀电化学研究方法[M]. 北京:化学工业出版社, 1987.
【5】郭浩, 李光福, 蔡珣. 外加电位对X70管线钢在近中性pH溶液中的应力腐蚀破裂的影响[J]. 中国腐蚀与防护学报, 2004, 24(4):208-212.
【6】阿伦.J.巴德, 拉里.R.福克纳. 电化学方法原理和应用[M]. 北京:化学工业出版社, 2005.
相关信息