水性可剥离涂料研究
A Water-based Strippable Coating
摘 要
以聚氨酯乳液作为基料, 纳米碳酸钙为填料, 制备了一种新型水性可剥离保护涂料。研究了纳米碳酸钙对涂层性能的影响, 当其加入量为2%时, 涂层可剥离性最佳。此时涂层平均拉伸强度达5.74 MPa, 平均断裂伸长率达259.03%, 表明该可剥离保护涂料具有良好的可剥离性能。
聚氨酯
纳米碳酸钙
water-based strippable coating
polyurethane
nano-CaCO3
Abstract
A new water-based strippable protecting coating was prepared with polyurethane emulsion and nano-CaCO3. The influence of nano-CaCO3 on the coating was studied. When the dosage of nano-CaCO3 was 2%, the coating had the best strippable performance. The average tensile strength and average elongation at the break point of the coating was 5.74 MPa and 259.03% respectively, indicating that this protective coating has good strippable performance.
中图分类号 TG174.46
所属栏目 应用技术
基金项目
收稿日期 2010/12/17
修改稿日期 2011/1/1
网络出版日期
作者单位点击查看
备注刘宏宇, 工程师, 硕士,
引用该论文: LIU Hong-yu,ZHANG Song. A Water-based Strippable Coating[J]. Corrosion & Protection, 2011, 32(10): 836
被引情况:
【1】程国东,张有慧,贾红刚,易桂虎,王永兴,万举惠, "海洋石油钢结构物涂装防护技术现状和发展",腐蚀与防护 35, 590-592(2014)
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】Ron Joseph. The lowdown on peelable coatings specs and usage[J]. Metal Finishing, 2004(12):45-46.
【2】谷兵, 周元林, 付万发, 等. 可剥离保护涂料的制备及成膜体性能分析[J]. 化工新型材料, 2008, 36(3): 52-53.
【3】吕维华, 王荣民, 何玉凤. 新型室温固化水性可剥涂料的开发与应用[J]. 应用化工, 2008, 37(6): 701-704.
【4】李新跃, 严 杰, 何 勇. 液体可剥离胶的研究[J]. 四川理工学院学报(自然), 2004, 17(3/4): 120-123.
【2】谷兵, 周元林, 付万发, 等. 可剥离保护涂料的制备及成膜体性能分析[J]. 化工新型材料, 2008, 36(3): 52-53.
【3】吕维华, 王荣民, 何玉凤. 新型室温固化水性可剥涂料的开发与应用[J]. 应用化工, 2008, 37(6): 701-704.
【4】李新跃, 严 杰, 何 勇. 液体可剥离胶的研究[J]. 四川理工学院学报(自然), 2004, 17(3/4): 120-123.
相关信息