低掺量钢筋阻锈剂的性能及机理
Inhibition Efficiency and Mechanism of Low Adding Amount Inhibitors
摘 要
在钢筋阻锈剂设计准则的基础上, 研制出JD系列钢筋阻锈剂, 探讨了其阻锈机理, 采用硬化砂浆的方法检测了JD系列钢筋阻锈剂的阻锈效果, 研究了添加该阻锈剂对混凝土凝结时间和抗压强度的影响。结果表明, JD系列钢筋阻锈剂在0.3%掺量下, 就能具有优良的阻锈效果, 同时对混凝土的力学性能没有不良影响。
低掺量
阻锈效果
力学性能
steel reinforced concrete
low adding amount
inhibition performance
mechanical property
Abstract
Based on the design criteria of inhibitors, JD series inhibitors were developed. The inhibition mechanism and efficiency in the environment of chloride were investigated. The effects of the inhibitors on the setting time and compression strength of concrete were also studied. The results showed that JD series inhibitors have good inhibition performance, and no adverse effect on the concrete performance.
中图分类号 TG174.42
所属栏目 应用技术
基金项目 国家科技支撑计划(No.2011BAB02B05)
收稿日期 2011/5/2
修改稿日期 2011/6/5
网络出版日期
作者单位点击查看
备注耿春雷, 工程师,
引用该论文: GENG Chun-lei. Inhibition Efficiency and Mechanism of Low Adding Amount Inhibitors[J]. Corrosion & Protection, 2011, 32(11): 908
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】洪定海. 混凝土中钢筋的腐蚀与保护[M]. 北京:中国铁道出版社, 1998:1-184.
【2】Saraswathya V, Song H W. Improving the durability of concrete by using inhibitors[J]. Building and Environment, 2007(42):464-472.
【3】Ormellese M, Berra M, Bolzoni F, et al. Corrosion inhibitors for chlorides induced corrosion in reinforced concrete structures[J]. Cement and Concrete Research, 2006(36):536-547.
【4】GB 8076-1997. 混凝土外加剂[S].
【5】JT/T 537-2004. 钢筋混凝土阻锈剂[S].
【6】仲朝明, 邵正明, 高汉青, 等. 亚硝酸盐类钢筋阻锈剂应用技术问题探讨[J]. 混凝土, 2009(12):46-48.
【7】王嵬, 张大全, 张万友, 等. 国内外混凝土钢筋阻锈剂研究进展[J]. 腐蚀与防护, 2006, 27(7):369-373.
【8】柳俊哲, 巴恒静. 掺防冻剂混凝土钢筋腐蚀程度的评价[J]. 混凝土, 2004(1):19-21.
【9】Geng C L, Xu Y M, Weng D. A new method to quickly assess inhibitor efficiency[J]. Journal of Wuhan University of Technology-Materials Science, 2008, 23(6):950-954.
【10】封孝信, 阚欣荣. 新型钢筋阻锈剂的作用机理[J]. 河北理工大学学报(自然科学版), 2009, 31(4):90-93.
【2】Saraswathya V, Song H W. Improving the durability of concrete by using inhibitors[J]. Building and Environment, 2007(42):464-472.
【3】Ormellese M, Berra M, Bolzoni F, et al. Corrosion inhibitors for chlorides induced corrosion in reinforced concrete structures[J]. Cement and Concrete Research, 2006(36):536-547.
【4】GB 8076-1997. 混凝土外加剂[S].
【5】JT/T 537-2004. 钢筋混凝土阻锈剂[S].
【6】仲朝明, 邵正明, 高汉青, 等. 亚硝酸盐类钢筋阻锈剂应用技术问题探讨[J]. 混凝土, 2009(12):46-48.
【7】王嵬, 张大全, 张万友, 等. 国内外混凝土钢筋阻锈剂研究进展[J]. 腐蚀与防护, 2006, 27(7):369-373.
【8】柳俊哲, 巴恒静. 掺防冻剂混凝土钢筋腐蚀程度的评价[J]. 混凝土, 2004(1):19-21.
【9】Geng C L, Xu Y M, Weng D. A new method to quickly assess inhibitor efficiency[J]. Journal of Wuhan University of Technology-Materials Science, 2008, 23(6):950-954.
【10】封孝信, 阚欣荣. 新型钢筋阻锈剂的作用机理[J]. 河北理工大学学报(自然科学版), 2009, 31(4):90-93.
相关信息