Stress Corrosion Cracking Properties of a New-type High Performance Corrosion Resistant Alloy Produced Domestically
摘 要
针对西南酸性油气田腐蚀环境, 采用高温高压腐蚀试验、应力腐蚀试验和电化学测试等方法, 对商业牌号3YC61新型耐蚀合金在各种酸性环境下的腐蚀性能进行了研究。结果表明该合金在试验条件下均具有很好的耐均匀腐蚀与耐应力腐蚀性能, 平均腐蚀速率优于标准要求, 满足酸性油气井对金属材料的使用要求。
Abstract
According to the environments of the sour oil and gas field in south-west area of China, high temperature and high pressure autoclave, electrochemical and stress corrosion cracking (SCC) tests were used to evaluate the corrosion resistant properties of the new-type alloy 3YC61 produced domestically in wet H2S Media. The results showed that the alloy has good resistance to general corrosion and SCC, the mean corrosion rate is superior to the requirement of corresponding standards for the metal materials used in sour oil and gas fields.
中图分类号 TG172.9
所属栏目 试验研究
基金项目 重庆仪表材料研究所博士后项目(No.10091032); 重庆市科技攻关计划项目(CSTC2010AB4054)
收稿日期 2011/1/10
修改稿日期 2011/3/1
网络出版日期
作者单位点击查看
联系人作者张玉碧(ybzhg@126.com)
备注张玉碧, 工程师, 博士,
引用该论文: ZHANG Yu-bi,WANG Dong-zhe,LIU Hai-ding,ZHANG Hua-li,YIN Qiang,LI Chang-rong. Stress Corrosion Cracking Properties of a New-type High Performance Corrosion Resistant Alloy Produced Domestically[J]. Corrosion & Protection, 2011, 32(12): 939
共有人对该论文发表了看法,其中:
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】刘金玮, 林久刚. 国内外油气勘探开发形势及发展趋势[J]. 西部探矿工程, 2009(6):81-84.
【2】钱伯章, 朱建芳. 世界原油质量趋势及非常规石油资源开发前景[J]. 天然气与石油, 2007, 3(25):40-45.
【3】Ramesh R, Pomeroy M J, Chub H, et al. Effect of gaseous environment on the corrosion of β-Salon Materials[J]. J Euro Cera Soci, 1995, 15:1007-1014.
【4】Sayed S M, Ashour E A, Youssef G I. Effect of sulde ions on the corrosion behavior of Al-brass and Cu10Ni alloys in salt water[J]. Mater Chem Phys, 2003, 78:825-834.
【5】Palumbo G. Metal alloys having improved resistance to intergranular stress corrosion cracking[P]. US 005817193A, 1998, No.5817193.
【6】Radd F J, Wolfe L H. Process and product for improved resistance to stress corrosion[P]. US 33 57458, 1967, 12:12-17.
【7】ASTM B 637-2006, Standard specification for precipitation-hardening nickel alloy bars, forgings, and forging stock for high-temperature service[S].
【8】NACE RP0775-2005, Preparation, installation, analysis, and interpretation of corrosion coupons in oilfield operations[S].
【9】McCoy S A, Puckett B C, Hibner E L. High performance age-hardenable nickel alloys solve problems in sour oil and gas service[J]. Corros, 2001:1102-1115.
【10】Li Q A, Bai Z Q, Huang D Z, et al. Predictive model for corrosion rate of oil tubes in CO2/H2S coexistent environment[J]. J Southwest Jiaotong Univer, 2004, 12(2):141-148.
【11】Ma H Y, Cheng X L, Li G Q, et al. The influence of hydrogen sulfide on corrosion of iron under different conditions[J]. Corrosion Science, 2000, 42:1669-1710.
【12】Videm K, Kvarekval J. Corrosion of carbon steel in carbon dioxide saturated solutions containing small amounts of hydrogen sulfide[J]. Corrosion, 1995, 51(5):260-268.
【2】钱伯章, 朱建芳. 世界原油质量趋势及非常规石油资源开发前景[J]. 天然气与石油, 2007, 3(25):40-45.
【3】Ramesh R, Pomeroy M J, Chub H, et al. Effect of gaseous environment on the corrosion of β-Salon Materials[J]. J Euro Cera Soci, 1995, 15:1007-1014.
【4】Sayed S M, Ashour E A, Youssef G I. Effect of sulde ions on the corrosion behavior of Al-brass and Cu10Ni alloys in salt water[J]. Mater Chem Phys, 2003, 78:825-834.
【5】Palumbo G. Metal alloys having improved resistance to intergranular stress corrosion cracking[P]. US 005817193A, 1998, No.5817193.
【6】Radd F J, Wolfe L H. Process and product for improved resistance to stress corrosion[P]. US 33 57458, 1967, 12:12-17.
【7】ASTM B 637-2006, Standard specification for precipitation-hardening nickel alloy bars, forgings, and forging stock for high-temperature service[S].
【8】NACE RP0775-2005, Preparation, installation, analysis, and interpretation of corrosion coupons in oilfield operations[S].
【9】McCoy S A, Puckett B C, Hibner E L. High performance age-hardenable nickel alloys solve problems in sour oil and gas service[J]. Corros, 2001:1102-1115.
【10】Li Q A, Bai Z Q, Huang D Z, et al. Predictive model for corrosion rate of oil tubes in CO2/H2S coexistent environment[J]. J Southwest Jiaotong Univer, 2004, 12(2):141-148.
【11】Ma H Y, Cheng X L, Li G Q, et al. The influence of hydrogen sulfide on corrosion of iron under different conditions[J]. Corrosion Science, 2000, 42:1669-1710.
【12】Videm K, Kvarekval J. Corrosion of carbon steel in carbon dioxide saturated solutions containing small amounts of hydrogen sulfide[J]. Corrosion, 1995, 51(5):260-268.
相关信息