焦磷酸钠在混凝土模拟孔溶液中的缓蚀性能
Corrosion Inhibition Property of Sodium Pyrophosphate in Simulated Concrete Pore Solution
摘 要
采用动电位极化曲线和电化学阻抗谱研究了焦磷酸钠在模拟混凝土孔溶液中对钢筋的保护作用。焦磷酸钠的加入导致混凝土中钢筋的腐蚀电位正移, 主要通过抑制钢筋的阳极电化学过程起缓蚀作用。其缓蚀效果随焦磷酸钠浓度的增加而增大, 在含0.04 mol/L Cl-的混凝土模拟液中, 当焦磷酸钠浓度为0.03 mol/L时, 其缓蚀效率可达到97.5%。
缓蚀剂
极化曲线
电化学阻抗
sodium pyrophosphate
corrosion inhibitor
polarization curve
EIS
Abstract
The protection effect of sodium pyrophosphate in alkaline simulated concrete pore solution was studied by potentio dynamic polarization curves and electrochemical impedance spectroscopy (EIS). The corrosion potential of steel in concrete increased with the addtion of sodium pyrophosphate. Sodium pyrophosphate inhibited the corrosion of steel in concrete by suppressing the anodic reaction. And inhibiting rate increased with increasing the concentration of sodium pyrophosphate in the solution. The inhibition effect (IE) increased to 97.7% when the concentration of sodium pyrophosphate was 0.03 mol/L.
中图分类号 TG174.42
所属栏目 试验研究
基金项目 国家自然科学基金(No.50978085,No.50808066); 江苏省六大人才高峰项目2009年A类
收稿日期 2011/7/18
修改稿日期
网络出版日期
作者单位点击查看
备注蒋林华, 教授, 博士生导师,
引用该论文: CHEN Song,JIANG Lin-hua,XU Jin-xia,YOU Lu-shen,WANG Tao. Corrosion Inhibition Property of Sodium Pyrophosphate in Simulated Concrete Pore Solution[J]. Corrosion & Protection, 2012, 33(1): 5
被引情况:
【1】卢浩,, "羟丙基壳聚糖及其复配的缓蚀性",腐蚀与防护 36, 108-112(2015)
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】张大全,陆柱.各类缓蚀剂开发和应用过程中环境影响的探讨[J].腐蚀与防护,1999,20(3):99-102.
【2】仲朝明,邵正明,高汉青,等.亚硝酸盐类钢筋阻锈剂应用技术问题探讨[J].混凝土,2009(12):46-47.
【3】郭良生,黄霓裳.自来水中碳钢缓蚀剂研究的进展[J].腐蚀与防护,1999,20(8):337-338,372.
【4】Dhouibi L, Triki E, Salta M,et al. Studies on corrosion inhibition of steel reinforcement by phosphate and nitrite[J]. Mater.Struct, 2003, 36(10):530-540.
【5】Hime W G. Discussion of the paper: ‘Studies on corrosion inhibition of steel reinforcement by phosphate and nitrite’[J]. Mater.Struct, 2003, 36(11):663-667.
【2】仲朝明,邵正明,高汉青,等.亚硝酸盐类钢筋阻锈剂应用技术问题探讨[J].混凝土,2009(12):46-47.
【3】郭良生,黄霓裳.自来水中碳钢缓蚀剂研究的进展[J].腐蚀与防护,1999,20(8):337-338,372.
【4】Dhouibi L, Triki E, Salta M,et al. Studies on corrosion inhibition of steel reinforcement by phosphate and nitrite[J]. Mater.Struct, 2003, 36(10):530-540.
【5】Hime W G. Discussion of the paper: ‘Studies on corrosion inhibition of steel reinforcement by phosphate and nitrite’[J]. Mater.Struct, 2003, 36(11):663-667.
相关信息