Ni-Fe-P镀层在H2S/CO2腐蚀环境中的腐蚀电化学研究
An Electrochemical Study on Ni-Fe-P Coating in Simulant Solutions with H2S/CO2
摘 要
在油管常用钢N80钢表面制备了Ni-Fe-P化学镀层, 采用SEM、EDS、XRD等分析手段, 对所制备镀层的成分、微观形貌、结构等性能进行了分析研究; 采用电化学方法评价了Ni-Fe-P镀层在H2S/CO2溶液中的耐蚀性。结果表明, N80钢表面经过化学镀Ni-Fe-P处理后, 其耐蚀性得到很大的提高, 镀层结构为非晶态; 电化学测试结果表明该镀层在H2S/CO2溶液中具有极强的钝化倾向和很好的耐酸性, 结果均证明Ni-Fe-P镀层具有良好的抗H2S/CO2腐蚀性能。
Ni-Fe-P镀层
H2S/CO2腐蚀
耐蚀性
N80 steel
Ni-Fe-P coating
H2S/CO2 corrosion
corrosion resistance
Abstract
A Ni-Fe-P electroless plating coating was prepared on N80 steel which is widely used. The composition, morphology, structure of the coating were analyzed by SEM,EDS,XRD, and so on. The corrosion resistance of the Ni-Fe-P coating in H2S/CO2 was evaluated by electrochemical methods. The results showed that the corrosion resistance of N80 steel was improved greatly after the treatment of electroless plating Ni-Fe-P. The structure of the Ni-Fe-P coating was amorphous and the results of electrochemical tests indicated that the coating had a strong passivation tendency in aqueous H2S/CO2 solution. These test results showed that the Ni-Fe-P coating had excellent resistance to H2S/CO2 corrosion.
中图分类号 TG142.7
所属栏目 试验研究
基金项目
收稿日期 2011/3/7
修改稿日期
网络出版日期
作者单位点击查看
联系人作者鲁亮(362733140@qq.com)
备注鲁亮,硕士研究生,
引用该论文: LU Liang,LI Chun-Fu,SUN Yan-An,RONG Jin-Fang. An Electrochemical Study on Ni-Fe-P Coating in Simulant Solutions with H2S/CO2[J]. Corrosion & Protection, 2012, 33(1): 42
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】任呈强. N80油管钢在含CO2/H2S高温高压两相介质中的电化学腐蚀行为及缓蚀机理研究[D]. 西北工业大学硕士论文,2003.
【2】Kuzyukov A N. How hydrogen effects operability of chemical and petrochemical equipment made of carbon and low alloy steel[J]. International Journal of Hyd-rogen Energy,2002,27:813-817.
【3】Siddiqui R A. Hydrogen embrittlement in 0.31% carbon steel used for petrochmi-cal applications[J]. Journal of Materials Processing Technology,2005,17:430-435.
【4】张清,李全安,文九巴. CO2/H2S对油气管材的腐蚀规律及研究进展[J]. 腐蚀与防护,2003,24(7):277-282.
【5】郑家燊. 二氧化碳腐蚀研究现状[J]. 断快油气田,1996,3(1):62-67.
【6】赵国仙,严密林,路民旭,等. 油田CO2腐蚀环境中的选材评价[J]. 腐蚀科学与防护技术,2000,12(4):240-242.
【7】张学元,邸超,雷良才. 二氧化碳腐蚀与控制[M]. 北京:化学工业出版社,2000.
【8】李宁,屠振密. 化学镀实用技术[M]. 北京:化学工业出版社,2004.
【9】李春福,王斌,代加林,等. Ni-Fe-P化学镀层结构及抗CO2腐蚀性能研究[J]. 表面技术,2004(3).
【10】涂抚洲,蒋汉瀛. Ni-Fe-P、Ni-W-P合金与镀层性能[J]. 材料保护,1999,32(10):12-13.
【11】高诚辉,周白杨. 不同成分Ni-Fe-P镀层的结构和性能[J]. 中国有色金属学报,1996(3):81-85.
【12】荣金仿,李春福,任强,等. Ni-Fe-P镀层与25-6Mo不锈钢高温高压抗CO2腐蚀性能比较及抗蚀机理研究[J]. 热加工工艺,2009,6:103-106.
【13】李春福. 油气开发过程中的CO2腐蚀机理及防护技术研究[D]. 西南石油学院,2005.
【2】Kuzyukov A N. How hydrogen effects operability of chemical and petrochemical equipment made of carbon and low alloy steel[J]. International Journal of Hyd-rogen Energy,2002,27:813-817.
【3】Siddiqui R A. Hydrogen embrittlement in 0.31% carbon steel used for petrochmi-cal applications[J]. Journal of Materials Processing Technology,2005,17:430-435.
【4】张清,李全安,文九巴. CO2/H2S对油气管材的腐蚀规律及研究进展[J]. 腐蚀与防护,2003,24(7):277-282.
【5】郑家燊. 二氧化碳腐蚀研究现状[J]. 断快油气田,1996,3(1):62-67.
【6】赵国仙,严密林,路民旭,等. 油田CO2腐蚀环境中的选材评价[J]. 腐蚀科学与防护技术,2000,12(4):240-242.
【7】张学元,邸超,雷良才. 二氧化碳腐蚀与控制[M]. 北京:化学工业出版社,2000.
【8】李宁,屠振密. 化学镀实用技术[M]. 北京:化学工业出版社,2004.
【9】李春福,王斌,代加林,等. Ni-Fe-P化学镀层结构及抗CO2腐蚀性能研究[J]. 表面技术,2004(3).
【10】涂抚洲,蒋汉瀛. Ni-Fe-P、Ni-W-P合金与镀层性能[J]. 材料保护,1999,32(10):12-13.
【11】高诚辉,周白杨. 不同成分Ni-Fe-P镀层的结构和性能[J]. 中国有色金属学报,1996(3):81-85.
【12】荣金仿,李春福,任强,等. Ni-Fe-P镀层与25-6Mo不锈钢高温高压抗CO2腐蚀性能比较及抗蚀机理研究[J]. 热加工工艺,2009,6:103-106.
【13】李春福. 油气开发过程中的CO2腐蚀机理及防护技术研究[D]. 西南石油学院,2005.
相关信息