CO2环境下温度和S2-对X60管线钢电化学行为的影响
Influence of Temperature and Sulfur Ion on Electrochemical Behavior of X60 Pipeline Steel in CO2 Enviroment
摘 要
利用极化曲线和电化学阻抗测试研究了温度和硫离子对X60管线钢CO2腐蚀电化学行为的影响。结果表明, 在温度和硫离子交互作用下, 随温度的升高腐蚀电流密度不断增大。S2-加入后电极表面生成一层黑色的腐蚀产物膜, 随着S2-浓度的升高, 腐蚀电位明显负移, 腐蚀电流密度呈现下降-上升-下降的趋势, 电极过程主要受硫化物生长过程控制。
硫离子
极化曲线
电化学阻抗
X60 steel
sulfur ion
polarization curve
EIS
Abstract
The influence of temperature and sulfur ion on the electrochemical behaviors of X60 pipeline steel was studied by means of polarization curves and electrochemical impedance spectroscopy(EIS). The results showed that under the interaction of temperature and sulfur ion, the corrosion current of X60 pipeline steel increased gradually with increasing temperature. The electrode surface was covered with a dark corrosion scale after sulfur ion addition, and the corrosion potential of X60 pipeline steel became more negative with the increase of concentration of sulfur ions, and the corrosion current density showed the tendency of increase-decrease-increase. The electrode process was controlled by formation of sulfide film.
中图分类号 TG172 TE988
所属栏目 试验研究
基金项目
收稿日期 2011/4/18
修改稿日期
网络出版日期
作者单位点击查看
联系人作者彭伟华(pwh347@163.com)
备注彭伟华,硕士研究生,
引用该论文: PENG Wei-hua,MIAO Jian,GAO Wei,SHI Hao,ZHANG Juan-tao. Influence of Temperature and Sulfur Ion on Electrochemical Behavior of X60 Pipeline Steel in CO2 Enviroment[J]. Corrosion & Protection, 2012, 33(2): 123
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】白真权,李鹤林,刘新道,等. 模拟油田H2S/CO2环境中N80钢的腐蚀及影响因素研究[J]. 材料保护,2003,36(4):32-34.
【2】张学元. 油气开发中二氧化碳腐蚀的研究现状和趋势[J]. 油田化学,1997,14(2):190.
【3】周计明. 油管钢在含CO2/H2S高温高压水介质中的腐蚀行为及防护技术的作用[D]. 西安: 西北工业大学,2002.
【4】杨怀玉,陈家坚,曹楚南,等. H2S水溶液中的腐蚀与缓蚀作用机理的研究Ⅲ. 不同pH值H2S溶液中碳钢的腐蚀电化学行为[J]. 中国腐蚀与防护学报,2000,20(2):97-103.
【5】王凤平,康万利,敬和民,等. 腐蚀电化学原理、方法及应用[M]. 北京:化学工业出版社,2008:166-231.
【6】王丹,吴明,陈旭,等. 石油管线钢在H2S/CO2环境中腐蚀行为的电化学研究[J]. 试验研究,2011,28(1):1-6.
【7】杨怀玉,陈家坚,曹楚南,等. H2S水溶液中的腐蚀与缓蚀作用机理的研究Ⅰ. 酸性H2S溶液中碳钢的腐蚀行为及硫化物膜的生长[J]. 中国腐蚀与防护学报,2000,20(1):1-7.
【8】陈长风,路民旭,赵国仙,等. N80钢CO2腐蚀电极过程交流阻抗分析[J]. 金属学报,2002,7(32):770-774.
【9】French E C. Corrosion and hydrogen blistering control in sour water system[J]. Materials Performance,1978(3):20-25.
【10】Humphries M J,Sorell G. Corrosion control in crude oil distillation units[J]. Materials Performance,1976(2):13-18.
【11】Smith J S,Miller J D A. Nature of sulphides and their corrosive effect on ferrous metals[J]. Br Corros J,1975,10(3):136.
【2】张学元. 油气开发中二氧化碳腐蚀的研究现状和趋势[J]. 油田化学,1997,14(2):190.
【3】周计明. 油管钢在含CO2/H2S高温高压水介质中的腐蚀行为及防护技术的作用[D]. 西安: 西北工业大学,2002.
【4】杨怀玉,陈家坚,曹楚南,等. H2S水溶液中的腐蚀与缓蚀作用机理的研究Ⅲ. 不同pH值H2S溶液中碳钢的腐蚀电化学行为[J]. 中国腐蚀与防护学报,2000,20(2):97-103.
【5】王凤平,康万利,敬和民,等. 腐蚀电化学原理、方法及应用[M]. 北京:化学工业出版社,2008:166-231.
【6】王丹,吴明,陈旭,等. 石油管线钢在H2S/CO2环境中腐蚀行为的电化学研究[J]. 试验研究,2011,28(1):1-6.
【7】杨怀玉,陈家坚,曹楚南,等. H2S水溶液中的腐蚀与缓蚀作用机理的研究Ⅰ. 酸性H2S溶液中碳钢的腐蚀行为及硫化物膜的生长[J]. 中国腐蚀与防护学报,2000,20(1):1-7.
【8】陈长风,路民旭,赵国仙,等. N80钢CO2腐蚀电极过程交流阻抗分析[J]. 金属学报,2002,7(32):770-774.
【9】French E C. Corrosion and hydrogen blistering control in sour water system[J]. Materials Performance,1978(3):20-25.
【10】Humphries M J,Sorell G. Corrosion control in crude oil distillation units[J]. Materials Performance,1976(2):13-18.
【11】Smith J S,Miller J D A. Nature of sulphides and their corrosive effect on ferrous metals[J]. Br Corros J,1975,10(3):136.
相关信息