Corrosion Control Technique for High-sulphur Gas Gathering and Transferring System in Puguang Gas Field
摘 要
普光气田集输系统共建有16座集气站、1座集气总站、38口开发井, 站外管线37.78 km。由于天然气中硫化氢含量15%左右, 二氧化碳含量8%~10%, 且采用湿气集输工艺, 因此集输系统存在较大腐蚀风险。通过电化学腐蚀试验、抗氢致开裂(HIC)和抗硫化物应力腐蚀(SSC)试验, 确定了集输系统抗硫材质, 采用“预涂膜+连续注入”的缓蚀剂加注工艺、阴极保护技术和智能清管技术等对设备实施保护。采用腐蚀挂片、电阻探针、线性极化探针和电指纹等多种腐蚀监测手段。普光气田集输系统腐蚀速率控制在0.044 mm/a以下。
Abstract
The gathering and transferring system in Puguang gas-field includes a central gas gathering station and 16 substations covering 38 gas wells and 37.78 km pipelines. The content of hydrogen sulfide in the natural gas is nearly 15% and carbon dioxide from 8% to 10%, so the wet high-sour gas makes great corrosion risk to transferring system. Based on tests of electrochemical corrosion, hydrogen-induced cracking (HIC), sulphide stress cracking (SSC), the materials of anti-sulphide-corrosion were studied and selected for pipelines and equipment. And injection technique of corrosion inhibitors is used to prevent the pipes from internal corrosion “pre-coating & continuous injecting”. Also, cathodic protection and intelligent pigging detection are applied as well. Furthermore, corrosion monitoring techniques including corrosion coupon (CC), electro-resistance (ER), linear polarization resistance (LPR) and field signature method (FSM) are introduced to monitor the corrosion development roundly. The monitoring results show that the average corrosion rate of Puguang gathering and transferring system is limited below 0.044 mm/a.
中图分类号 TG174
所属栏目 应用技术
基金项目 国家重大专项(No.2008ZX05017)
收稿日期 2011/5/16
修改稿日期
网络出版日期
作者单位点击查看
备注龚金海, 高级工程师,
引用该论文: GONG Jin-hai,LIU De-xu,WANG Xiao-lin. Corrosion Control Technique for High-sulphur Gas Gathering and Transferring System in Puguang Gas Field[J]. Corrosion & Protection, 2012, 33(4): 317
被引情况:
【1】陈惟国,张庆生,刘德绪,张诚,李长进,曾德志,宿彦京, "L360MCS钢在普光气田凝析水中的腐蚀行为",腐蚀与防护 35, 137-141(2014)
共有人对该论文发表了看法,其中:
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】岑芳, 李治平, 张彩, 等. 含硫气田硫化氢腐蚀[J]. 资源·产业, 2005, 7(4): 79-81.
【2】吕杉. 高含硫气田集输系统腐蚀和腐蚀控制[J]. 石油规划设计, 2002, 13(6): 34-43.
【3】聂仕荣. 高含硫气田集输与处理工艺[J]. 油气田地面工程, 2008, 27(6): 45-46.
【4】杜志敏. 国外高含硫气藏开发经验与启示[J]. 天然气工业, 2006, 26(12): 35-37.
【5】施岱艳, 杨朔, 杨诚, 等. 腐蚀监测技术在四川含硫气田的应用[J]. 天然气工业, 1998, 18(6):72-75.
【2】吕杉. 高含硫气田集输系统腐蚀和腐蚀控制[J]. 石油规划设计, 2002, 13(6): 34-43.
【3】聂仕荣. 高含硫气田集输与处理工艺[J]. 油气田地面工程, 2008, 27(6): 45-46.
【4】杜志敏. 国外高含硫气藏开发经验与启示[J]. 天然气工业, 2006, 26(12): 35-37.
【5】施岱艳, 杨朔, 杨诚, 等. 腐蚀监测技术在四川含硫气田的应用[J]. 天然气工业, 1998, 18(6):72-75.
相关信息