GH4169高温合金腐蚀加工速度的影响因素
Influencing Factors of Corrosion Processing Rate for GH4169 Super Alloy
摘 要
研究了GH4169高温合金在含三氯化铁的腐蚀液中腐蚀加工速度的影响因素。结果表明, 腐蚀加工速度主要取决于HF、HNO3、HCl、FeCl3的浓度和加工温度。随着酸浓度的增加, 腐蚀加工速度加快; 温度每升高10 ℃, 腐蚀速度增加4.35 μm/min。FeCl3不仅能够提高腐蚀速度且能降低加工表面的粗糙度; 溶液中Ni2+的存在会影响腐蚀速率, 随着Ni2+浓度增加, 腐蚀速率逐步降低。
腐蚀加工
腐蚀速度
GH4169 super alloy
corrosion processing
corrosion rate
Abstract
The factors affecting the corrosion processing rate of GH4169 super alloy in corrosion processing solution containing FeCl3 were studied. The corrosion processing rate mainly depended on the concentration of HF, HNO3, HCl, FeCl3 and the processing temperature. The corrosion processing rate showed an increasing trend with the rise of concentration of acid. When the temperature increased 10 ℃, the processing rate increased 4.35 μm/min. FeCl3 could not only increase the corrosion processing rate, but also reduce the surface roughness. The existence of Ni2+ in the solution could influence corrosion processing rate. with the increase of Ni2+ concentration, the corrosion processing rate decreased gradually.
中图分类号 TG176
所属栏目 试验研究
基金项目
收稿日期 2011/12/13
修改稿日期
网络出版日期
作者单位点击查看
联系人作者林翠(lincwi@sohu.com)
备注林翠, 教授, 博士,
引用该论文: ZHANG Xiao-feng,LIN Cui,ZHAO Qing,YUAN Liang. Influencing Factors of Corrosion Processing Rate for GH4169 Super Alloy[J]. Corrosion & Protection, 2012, 33(5): 397
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】黄乾尧. 高温合金[M]. 北京:冶金工业出版社, 2004:1-6.
【2】中国材料研究学会. 中国新材料产业发展报告-航空航天材料[M]. 北京:化学工业出版社, 2006:37-49.
【3】杨丁. 金属刻蚀技术[M]. 北京:国防工业出版社, 2008:2-4.
【4】沈连桂. 化学铣切[M]. 北京: 国防工业出版社, 1984:15-20.
【5】《航空制造工程手册》总编委会. 航空制造工程手册-特种加工[M]. 北京:航空工业出版社, 1993:600-645.
【2】中国材料研究学会. 中国新材料产业发展报告-航空航天材料[M]. 北京:化学工业出版社, 2006:37-49.
【3】杨丁. 金属刻蚀技术[M]. 北京:国防工业出版社, 2008:2-4.
【4】沈连桂. 化学铣切[M]. 北京: 国防工业出版社, 1984:15-20.
【5】《航空制造工程手册》总编委会. 航空制造工程手册-特种加工[M]. 北京:航空工业出版社, 1993:600-645.
相关信息