Aging Performance of Low Surface Energy Coating
摘 要
合成了全氟丙烯酸酯类聚合物, 添加到涂料中制成低表面能涂层; 将低表面能涂层暴露在室外或紫外灯下, 发现全氟丙烯酸酯类低表面能材料疏水性能会迅速失效, 利用红外光谱仪和X射线光电子能谱研究低表面能涂层的失效规律, 涂层表面的羟基或双键等活性基团氧化可能是失效的主要原因。
Abstract
The low surface energy coating is prepared by adding synthesis of perfluorinated acrylic polymer into paint. The low surface energy coating is exposed in outdoor or ultraviolet lamp. The results show that the hydrophobic properties of perfluorinated acrylic acid esters of low surface energy materials become invalid rapidly. Infrared spectrometer and X-ray photoelectron spectroscopy were used to study the failure law of low surface energy coating. The main reason of the failure is the oxidation of oxhydryl and other active group in the surface.
中图分类号 TG174.46
所属栏目 试验研究
基金项目
收稿日期 2011/9/6
修改稿日期
网络出版日期
作者单位点击查看
引用该论文: HU Yi-jun,LIU Lan-xuan,MIAO Yi,ZHANG Ying-ping,LIU Xiu-sheng. Aging Performance of Low Surface Energy Coating[J]. Corrosion & Protection, 2012, 33(8): 680
共有人对该论文发表了看法,其中:
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】边蕴静. 发展迅速的特种功能涂料[J]. 现代涂料与涂装, 2007(9):6-10.
【2】Ashok K. Self-healing coatings for steel[J]. Progress in Organic Coatings, 2006, 55(3):244-253.
【3】杜泰江, 刘希燕. 自修复材料及在涂料中的应用[J]. 现代涂料与涂装, 2007, 10(12):29-31.
【4】Valerie S M. Self-healing coatings an alternative route for anticorrosion protection[J]. Progress in Organic Coatings, 2008, 63(3):307-315.
【5】Liu X S, Wang C, Liu L X, et al. Properties of low surface energy fluorocarbon polymers with fluoro-acrylic resins[J]. Journal of Wuhan University of Technology-Materials Science Edition, 2008, 23(3):285-288.
【6】Miriam P. Cupric tannate:A low copper content antifouling pigment[J]. Progress in Organic Coatings, 2006, 55(4):311-315.
【2】Ashok K. Self-healing coatings for steel[J]. Progress in Organic Coatings, 2006, 55(3):244-253.
【3】杜泰江, 刘希燕. 自修复材料及在涂料中的应用[J]. 现代涂料与涂装, 2007, 10(12):29-31.
【4】Valerie S M. Self-healing coatings an alternative route for anticorrosion protection[J]. Progress in Organic Coatings, 2008, 63(3):307-315.
【5】Liu X S, Wang C, Liu L X, et al. Properties of low surface energy fluorocarbon polymers with fluoro-acrylic resins[J]. Journal of Wuhan University of Technology-Materials Science Edition, 2008, 23(3):285-288.
【6】Miriam P. Cupric tannate:A low copper content antifouling pigment[J]. Progress in Organic Coatings, 2006, 55(4):311-315.
相关信息