海洋工程结构防护涂层体系中漆膜的润湿性与抗氯离子渗透性
Wetting Property and Resistance to Chloride Ion Permeability of Paint Films in Engineering Structure Protective Coating Systems under Marine Climate Condition
摘 要
选择典型防护涂层体系中涂料产品, 实验室测试了漆膜的润湿性和抗氯离子渗透性。结果表明, 氯离子的渗透量与涂层厚度有关; 涂层成膜物及涂料中的颜、填料都影响涂层的润湿性, 颜、填料的形状影响氯离子渗透的情况还需要进一步试验和讨论。
防护涂层
润湿性
抗氯离子渗透性
engineering structure
protective coating
wetting property
resistance to chloride ion permeability
Abstract
The paint was selected from in the typical protective coating system. Wettability and resistance to chloride ion penetration of the film were tested. The results showed that the amount of chloride ion penetration is related to the thickness of coating. Further experiments and discussion are needed to study on the coating film-forming material and coating pigments, filler shape affecting on the penetration of chloride ion.
中图分类号 TG174.4
所属栏目 试验研究
基金项目
收稿日期 2011/9/5
修改稿日期
网络出版日期
作者单位点击查看
备注常玉鑫, 高工,
引用该论文: CHANG Yu-xin,LI Jing,CHANG Wei. Wetting Property and Resistance to Chloride Ion Permeability of Paint Films in Engineering Structure Protective Coating Systems under Marine Climate Condition[J]. Corrosion & Protection, 2012, 33(8): 686
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】JT/T 733-2008港口机械钢结构表面防腐涂层技术条件[S].
【2】JT/T 695-2007混凝土桥梁结构表面涂层防腐技术条件[S].
【3】杜文琴, 巫莹柱. 接触角测量的量高法和量角法的比较[J]. 纺织学报, 2007, 28(7):29-32.
【4】陈刚, 周湘玲, 吴璇. 防腐涂料-抗氯离子渗透性测试方法[J]. 上海涂料, 2008, 46(6):30-31.
【2】JT/T 695-2007混凝土桥梁结构表面涂层防腐技术条件[S].
【3】杜文琴, 巫莹柱. 接触角测量的量高法和量角法的比较[J]. 纺织学报, 2007, 28(7):29-32.
【4】陈刚, 周湘玲, 吴璇. 防腐涂料-抗氯离子渗透性测试方法[J]. 上海涂料, 2008, 46(6):30-31.
相关信息