Al-Zn-In-Si牺牲阳极材料的电化学性能
Electrochemical Performance of Al-Zn-In-Si Sacrificial Anode Material
摘 要
通过正交试验筛选确定了Al-Zn-In-Si牺牲阳极材料的最佳配比为Zn 5.5%,In 0.020%,Si 0.11%,Fe 0.12%。并对其电化学性能进行研究。结果表明,Al-5.5Zn-0.02In-0.11Si牺牲阳极材料的电化学性能指标包括开路电位、工作电位、实际电化学容量、电流效率、表面溶解形貌等, 均达到或超过国家标准。
Al-Zn-In-Si牺牲阳极材料
电化学性能
sacrificial anode
Al-Zn-In-Si
electrochemical performance
Abstract
The electrochemical performance of 9 types of Al-Zn-In-Si sacrificial anode materials with different amounts of Zn, In, Si and Fe were studied in natural seawater. The test results showed that the electrochemical performance of Al-Zn-In-Si meets and exceeds the national standard. The composition of Al-Zn-In-Si anode was optimized through orthogonal test. The optimum contents of alloy elements were as follows: Zn 5.5%; In 0.020%; Si 0.11%; Fe 0.12%.
中图分类号 TG174.41
所属栏目 试验研究
基金项目
收稿日期 2011/10/17
修改稿日期
网络出版日期
作者单位点击查看
引用该论文: ZHAO Cong-min,DU Min,HUANG Zhi-qiang,WANG Bin. Electrochemical Performance of Al-Zn-In-Si Sacrificial Anode Material[J]. Corrosion & Protection, 2012, 33(9): 780
被引情况:
【1】庞天照,郑文杰,吴玉清,王菊琳, "船用设备牺牲阳极的失效原因",腐蚀与防护 37, 263-267(2016)
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】李异, 邓和平. 铝合金牺牲阳极在南海海泥中的性能研究[J]. 腐蚀科学与防护技术,1991,3(1):22-26.
【2】李异, 李永广. 铝牺牲阳极在热海泥中得电化学性能[J]. 材料开发与应用,2001,16(3):19-22.
【3】李威力,闫永贵,陈光,等. Al-Zn-In系牺牲阳极低温电化学性能研究[J]. 腐蚀科学与防护技术,2009,21(2):121-124.
【4】廖海星, 朱鸿赫, 齐公台. 温度对铝合金牺牲阳极活化溶解行为的影响[J]. 华中科技大学学报,2004,32(2):114.
【5】马丽杰, 宋曰海, 郭忠诚, 等. Al-Zn-In-Cd牺牲阳极材料的电化学性能研究[J]. 材料开发与应用,2004,32(1):3.
【6】赵月红,林乐耘. 铝合金牺牲阳极微观组织的不均匀性对其腐蚀影响[J]. 稀有金属,2000,24(5):341.
【2】李异, 李永广. 铝牺牲阳极在热海泥中得电化学性能[J]. 材料开发与应用,2001,16(3):19-22.
【3】李威力,闫永贵,陈光,等. Al-Zn-In系牺牲阳极低温电化学性能研究[J]. 腐蚀科学与防护技术,2009,21(2):121-124.
【4】廖海星, 朱鸿赫, 齐公台. 温度对铝合金牺牲阳极活化溶解行为的影响[J]. 华中科技大学学报,2004,32(2):114.
【5】马丽杰, 宋曰海, 郭忠诚, 等. Al-Zn-In-Cd牺牲阳极材料的电化学性能研究[J]. 材料开发与应用,2004,32(1):3.
【6】赵月红,林乐耘. 铝合金牺牲阳极微观组织的不均匀性对其腐蚀影响[J]. 稀有金属,2000,24(5):341.
相关信息