Performance Comparison between Complex Anodic Oxidation Film with n-SiC Addition and Hard Anodic Oxidation Film
摘 要
采用金相显微镜、测厚仪对铝合金硬质阳极氧化膜和添加n-SiC复合阳极氧化膜的横截面组织、纵截面组织进行分析和研究, 采用扫描电镜和X射线能谱仪证实n-SiC进入了氧化膜中, 运用磨损试验对复合阳极氧化膜性能进行了性能检测, 结果表明, 添加n-SiC铝合金复合阳极氧化膜的耐磨性能较好。
Abstract
Optical microscopy and thickness gauge were used to study the interface structure of cross section and longitudinal section of hard anodic oxidation film and complex anodic oxidation film with n-SiC addition. The results of SEM and EDS show that n-SiC entered into the oxide film. Performance of the complex anodic oxidation film was tested by friction and abrasion testing and salt-fog corrosion testing. The results show that the complex anodic oxidation film with n-SiC addition had better properties.
中图分类号 TG174.451
所属栏目 试验研究
基金项目
收稿日期 2011/9/28
修改稿日期
网络出版日期
作者单位点击查看
联系人作者马骏(mjsdy@126.com)
备注马骏,讲师,硕士,
引用该论文: MA Jun,SU Dong-yun,ZOU Dong-lin. Performance Comparison between Complex Anodic Oxidation Film with n-SiC Addition and Hard Anodic Oxidation Film[J]. Corrosion & Protection, 2012, 33(9): 784
共有人对该论文发表了看法,其中:
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】刁玉辉,韦安和. 自润滑活塞环的摩擦摩损分析[J]. 润滑与密封,2004,165(5):103-106.
【2】马骏,赵占西,苏冬云. 铸铝合金硬质阳极氧化工艺分析及改进[J]. 表面技术,2006,35(6): 30-31.
【3】刘吉平,廖莉玲. 无机纳米材料[M]. 北京: 科学出版社, 2003.
【4】马骏, 苏冬云. 添加n-SiC的铝合金复合阳极氧化工艺[J]. 腐蚀与防护,2010,31(11): 893-895.
【5】刘世永,张会臣. 6063 铝合金复合硬质阳极氧化及摩擦行为研究[M]. 轻合金加工, 2004, 32(4):42-43.
【6】罗胜联. 铝及其合金电化学复合处理技术及研究进展[J]. 电镀与精饰, 2002, 24(3): 60-62.
【2】马骏,赵占西,苏冬云. 铸铝合金硬质阳极氧化工艺分析及改进[J]. 表面技术,2006,35(6): 30-31.
【3】刘吉平,廖莉玲. 无机纳米材料[M]. 北京: 科学出版社, 2003.
【4】马骏, 苏冬云. 添加n-SiC的铝合金复合阳极氧化工艺[J]. 腐蚀与防护,2010,31(11): 893-895.
【5】刘世永,张会臣. 6063 铝合金复合硬质阳极氧化及摩擦行为研究[M]. 轻合金加工, 2004, 32(4):42-43.
【6】罗胜联. 铝及其合金电化学复合处理技术及研究进展[J]. 电镀与精饰, 2002, 24(3): 60-62.
相关信息