贵金属氧化物涂层钛阳极的进展
Development of Noble Metal/Oxide Coated Titanium Anode
摘 要
贵金属氧化物涂层钛阳极采用导电的贵金属氧化物(如RuO2、IrO2)作为催化剂, 非导电的金属氧化物(如TiO2、Ta2O5、SnO2、ZrO2、CoOx等)作为分散剂或稳定剂, 将它们涂复在阀门金属(Ti、Ta、Zr、Nb等)上通过热分解法制备而成。RuO2-TiO2/Ti阳极1968年在氯碱电解工业中获得成功应用, IrO2-Ta2O5/Ti阳极作为析氧电极近20年来得到更多关注, 在电镀、阴极保护等众多领域获得了广泛的应用。本文重点介绍IrO2涂层钛阳极的成分、结构和电化学性能, 并对其应用前景和存在问题进行讨论。
氧的析出
电化学过程
metal oxide anode
oxygen evolution
electrochemical process
Abstract
The noble metal/oxide coated anodes use conductive precious metal oxides (RuO2, IrO2, etc.) as electrocatalysts and non-conductive metal oxides (TiO2, Ta2O5, SnO2, ZrO2, CoOx, etc.) as dispersing or stabilizing agents, which are coated on valve metal substrates (Ti, Ta, Zr, Nb, etc.) with a thermal decomposition method. RuO2-TiO2/Ti anode has successfuly used in industrial chlor-alkali electrolysis in 1968. In the last two decades, IrO2-Ta2O5/Ti anode as electrode for O2 evolution has received much attention and applied to many electrochimical processes, including electroplating, cathodic protection and so on. In this paper the composition, structure and electrochemical performance of IrO2 coated titanium anodes and existent problems are discussed.
中图分类号 TB303
所属栏目 专论
基金项目
收稿日期 2012/3/1
修改稿日期
网络出版日期
作者单位点击查看
备注黄永昌, 教授,
引用该论文: HUANG Yong-chang. Development of Noble Metal/Oxide Coated Titanium Anode[J]. Corrosion & Protection, 2012, 33(12): 1108
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】Hayfield P C S. Development of the noble metal/oxide coated titanium electrode part 1[J]. Platinum Metals Rev, 1988, 42(1):27-33.
【2】Hayfield P C S. Development of the noble metal/oxide coated titanium electrode part 2[J]. Platinum Metals Rev, 1988, 42(2):46-55.
【3】Hayfield P C S. Development of the noble metal/oxide coated titanium electrode part 3[J]. Platinum Metals Rev, 1988, 42(3):116-222.
【4】David H. Kroon MMO-coated titanium anodes for cathodic protection part 1[J]. Materials Performance, 2007(5):26-29.
【5】向前, 黄永昌, 卢洪, 等. 改性二氧化铱电极研制[J]. 无机盐工业, 1998(3): 16-17,
【6】张招贤. 钛电极工学(第二版)[M]. 冶金工业出版社, 2003.
【7】黄永昌, 向前. 不溶性电极和制备方法及用途[P]. 专利号ZL001 19691.X, 2004.
【8】黄永昌, 向前, 姜学文. 钛基二氧化铱电极及其在阴极保护应用中的研究[J]. 腐蚀科学与防护技术, 1998(2): 109-113.
【9】张萌萌, 林纪筠, 陈康宁. 钛钽氧化物阳极涂层的研究[J]. 无机材料学报, 1999, 14(2): 251-256.
【10】黄永昌, 徐文新. 钛基二氧化铱电极及其在CuSO4溶液中的工业应用[J]. 电子电镀, 2007(2): 43-46.
【11】张招贤, 李海涛, 黄斌. 氯化物硫酸盐混合体系电积金属镍中涂层钛阳极的研究[J]. 广东有色金属学报, 1994, 4(1): 49-53.
【12】张玉萍, 武志红, 鞠鹤, 等. 湿法冶炼中电沉积钴用钛阳极研究[J]. 稀有金属, 2009, 33(6): 898-901.
【13】Msindo Z S, Sibanda V, Potgieter J H. Electrochemical comparison to Ti-(70%)IrO2/(30%)Ta2O5 dimensionally stable anodes for use in copper electrowinning[J]. J Appl Electrochem, 2010, 40(6):691-699.
【14】袁令仪, 黄梅, 侯郁东. 在硫酸体系中高电流密度下活性涂层钛阳极的研究院[J]. 广东有色金属学报, 1995, 5(1): 58-65.
【15】David H. Kroon MMO-coated titanium anodes for cathodic protection part 2[J]. Materials Performance, 2007, 6(1):24-29.
【16】黄永昌. 金属氧化物阳极(MMO)及其在阴极保护中的应用[J]. 腐蚀与防护, 2008, 增刊: 32-40.
【17】冯骅, 冯洪臣. 网状阳极在储罐底板阴极保护中的应用[J]. 腐蚀与防护, 2001, 22(2): 69-71.
【18】蔡天晓, 陈航, 鞠鹤, 等. 钢筋混凝土阴极保护用高性能涂层钛阳极[J]. 腐蚀与防护, 2006, 27(10): 522-525.
【2】Hayfield P C S. Development of the noble metal/oxide coated titanium electrode part 2[J]. Platinum Metals Rev, 1988, 42(2):46-55.
【3】Hayfield P C S. Development of the noble metal/oxide coated titanium electrode part 3[J]. Platinum Metals Rev, 1988, 42(3):116-222.
【4】David H. Kroon MMO-coated titanium anodes for cathodic protection part 1[J]. Materials Performance, 2007(5):26-29.
【5】向前, 黄永昌, 卢洪, 等. 改性二氧化铱电极研制[J]. 无机盐工业, 1998(3): 16-17,
【6】张招贤. 钛电极工学(第二版)[M]. 冶金工业出版社, 2003.
【7】黄永昌, 向前. 不溶性电极和制备方法及用途[P]. 专利号ZL001 19691.X, 2004.
【8】黄永昌, 向前, 姜学文. 钛基二氧化铱电极及其在阴极保护应用中的研究[J]. 腐蚀科学与防护技术, 1998(2): 109-113.
【9】张萌萌, 林纪筠, 陈康宁. 钛钽氧化物阳极涂层的研究[J]. 无机材料学报, 1999, 14(2): 251-256.
【10】黄永昌, 徐文新. 钛基二氧化铱电极及其在CuSO4溶液中的工业应用[J]. 电子电镀, 2007(2): 43-46.
【11】张招贤, 李海涛, 黄斌. 氯化物硫酸盐混合体系电积金属镍中涂层钛阳极的研究[J]. 广东有色金属学报, 1994, 4(1): 49-53.
【12】张玉萍, 武志红, 鞠鹤, 等. 湿法冶炼中电沉积钴用钛阳极研究[J]. 稀有金属, 2009, 33(6): 898-901.
【13】Msindo Z S, Sibanda V, Potgieter J H. Electrochemical comparison to Ti-(70%)IrO2/(30%)Ta2O5 dimensionally stable anodes for use in copper electrowinning[J]. J Appl Electrochem, 2010, 40(6):691-699.
【14】袁令仪, 黄梅, 侯郁东. 在硫酸体系中高电流密度下活性涂层钛阳极的研究院[J]. 广东有色金属学报, 1995, 5(1): 58-65.
【15】David H. Kroon MMO-coated titanium anodes for cathodic protection part 2[J]. Materials Performance, 2007, 6(1):24-29.
【16】黄永昌. 金属氧化物阳极(MMO)及其在阴极保护中的应用[J]. 腐蚀与防护, 2008, 增刊: 32-40.
【17】冯骅, 冯洪臣. 网状阳极在储罐底板阴极保护中的应用[J]. 腐蚀与防护, 2001, 22(2): 69-71.
【18】蔡天晓, 陈航, 鞠鹤, 等. 钢筋混凝土阴极保护用高性能涂层钛阳极[J]. 腐蚀与防护, 2006, 27(10): 522-525.
相关信息
| 标题 | 相关频次 | |
 | Magnaplate“协和”涂层及其在镁合金上的应用 | 2 |