Performance of Corrosion Inhibitor in High Temperature Multi-component Thermal Fluid
摘 要
多元热流体注采技术在渤海油田应用期间, 油管腐蚀问题严重, 针对该工艺研发出COSL-1缓蚀剂, 现场应用腐蚀抑制情况良好。利用失重法和电化学极化对COSL-1缓蚀剂在二氧化碳和氧气共存条件下进行了研究, 结果表明该缓蚀剂在90 ℃ 2 MPa CO2和0.02 MPa O2模拟注采溶液中的缓蚀率达到95%以上。动电位测试表明缓蚀剂主要通过改变阳极过程起缓蚀作用, 在N80钢表面的吸附满足Langmuir吸附等温式。
Abstract
Multi-component thermal fluid exploitation enhanced the recovery factor of thick oil greatly in Bohai Oilfield, but also caused severe corrosion of oil tubes. Corrosion inhibitor COSL-1 was developed to prevent the corrosion with good result in oil well. The inhibition performance of COSL-1 was investigated by weight loss and polarization curves. The inhibition efficiency can reach 95% in simulated solution with 2 MPa CO2 and 0.02 MPa O2 at 90 ℃. Electrochemical tests show that inhibitor COSL-1 belongs to mixed-type inhibitor and prohibits the corrosion anodic process principally, and the adsorption behavior of the inhibitor on steel N80 obeys the Langmuir isothermal equation.
中图分类号 TG174.42
所属栏目 应用技术
基金项目 国家重大科技专项(2011ZX05057-005-001)
收稿日期 2012/11/3
修改稿日期
网络出版日期
作者单位点击查看
备注付朝阳, 副教授, 博士,
引用该论文: ZHAO Li-chang,MA Zeng-hua,SUN Yong-tao,LIN tao,LIU Hai-tao,WANG Shao-hua,SUN Yu-bao,HE Jin-bei,WANG Jiang-shun,FU Chao-yang. Performance of Corrosion Inhibitor in High Temperature Multi-component Thermal Fluid[J]. Corrosion & Protection, 2013, 34(1): 64
共有人对该论文发表了看法,其中:
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】唐晓旭, 马跃, 孙永涛.海上稠油多元热流体吞吐工艺研究及现场试验[J].中国海上油气, 2011, 3(23):185-188.
【2】朱信刚, 龙媛媛, 杨为刚, 等.多元热流体对油气采输管线的腐蚀[J].腐蚀与防护, 2009, 5(30):316-317.
【3】孙永涛, 程鹏, 马增华, 等.高温多元热流体注采液中N80钢的腐蚀行为[J].腐蚀与防护, 2012, 3(33):218-221.
【4】孙永涛, 付朝阳, 杨秀兰.高温多元热流体注采中管材腐蚀分析[J].石油与天然气化工, 2012, 4(3):408-410.
【2】朱信刚, 龙媛媛, 杨为刚, 等.多元热流体对油气采输管线的腐蚀[J].腐蚀与防护, 2009, 5(30):316-317.
【3】孙永涛, 程鹏, 马增华, 等.高温多元热流体注采液中N80钢的腐蚀行为[J].腐蚀与防护, 2012, 3(33):218-221.
【4】孙永涛, 付朝阳, 杨秀兰.高温多元热流体注采中管材腐蚀分析[J].石油与天然气化工, 2012, 4(3):408-410.
相关信息