Effect of Temperature on Corrosion Behavior of Coiled Tubing QT-900 in CO2 Environment
摘 要
模拟某油田腐蚀环境, 通过高温高压CO2腐蚀试验, 采用SEM、EDS和XRD等测试手段, 研究了连续油管QT-900在CO2环境中的腐蚀行为。结果表明, 随着温度的升高, 连续油管的均匀腐蚀速率和局部腐蚀速率均先减小后增大、再减小, 分别在40 ℃和100 ℃时出现极大值。在承受最大拉伸应力时, 平均腐蚀速率和局部腐蚀速率与不受力时相比均明显增加。在本试验条件下, 局部腐蚀严重, 最大可达4.635 5 mm·a-1。腐蚀产物的主要成分为FeCO3。
Abstract
The corrosion behaviors of coiled tubing in CO2 corrosion environment were studied by using SEM, EDS and XRD testing methods. The results showed that with increasing temperature, the uniform corrosion rate and the localized corrosion rate of coiled tubing decreased first, then increased, and decreased again. The maximum variation appeared at 40℃ and 100℃. Under the maximum tensile stress, the uniform corrosion rate and the localized corrosion rate both increased more clearly than no tensile stress. In the present expersmental conditions, the localized corrosion was very severe, the maximum rate was up to 4.635 5 mm·a-1. The corrosion products mostly were FeCO3.
中图分类号 TG172.8TG172.8
所属栏目 试验研究
基金项目
收稿日期 2012/8/29
修改稿日期
网络出版日期
作者单位点击查看
备注赵国仙, 教授, 博士,
引用该论文: ZHU Cheng-long,ZHAO Guo-xian,XUE Yan,LI Dan-ping,LIU Yan-zhao. Effect of Temperature on Corrosion Behavior of Coiled Tubing QT-900 in CO2 Environment[J]. Corrosion & Protection, 2013, 34(3): 232
被引情况:
【1】许爱华,张靖,院振刚,崔兰德,谢宽涯,张鲲鹏,李岩, "迪那2凝析气田集输管线腐蚀机理与防护技术",腐蚀与防护 36, 1090-1095(2015)
共有人对该论文发表了看法,其中:
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】毕宗岳, 张鹏, 井晓天, 等.连续油管在川东气田的腐蚀行为研究[J].焊管, 2011, 34(4):26-29.
【2】Ken Newman. Coiled tubing technology continues its rapid growth [J].World Oil, 1998, 219( 1) : 64-70.
【3】刘海浪, 柯仲华, 赵振峰.小井眼和连续油管技术的进展与应用[M].北京:石油工业出版社, 1998.
【4】鲜宁, 姜放, 荣明, 等.连续油管在酸性环境下的腐蚀与防护及其研究进展[J].天然气工业, 2011, 31(4):113-116.
【5】王优强.连续油管腐蚀可靠性研究初探[J].石油矿场机械, 2002, 31(6):10-12.
【6】王优强, 张嗣伟, 方爱国.连续油管的失效形式和原因概述[J].石油矿场机械, 1999, 28(4):15-18.
【7】俞芳, 高克玮, 乔利杰, 等.温度对N80 钢CO2腐蚀产物膜结构和力学性能的影响[J].腐蚀与防护, 2009, 30(3):145-148.
【8】张清, 李全安, 文九巴, 等.CO2/H2S对油气管材的腐蚀规律及研究进展[J].腐蚀与防护, 2003, 24(7):277-281.
【2】Ken Newman. Coiled tubing technology continues its rapid growth [J].World Oil, 1998, 219( 1) : 64-70.
【3】刘海浪, 柯仲华, 赵振峰.小井眼和连续油管技术的进展与应用[M].北京:石油工业出版社, 1998.
【4】鲜宁, 姜放, 荣明, 等.连续油管在酸性环境下的腐蚀与防护及其研究进展[J].天然气工业, 2011, 31(4):113-116.
【5】王优强.连续油管腐蚀可靠性研究初探[J].石油矿场机械, 2002, 31(6):10-12.
【6】王优强, 张嗣伟, 方爱国.连续油管的失效形式和原因概述[J].石油矿场机械, 1999, 28(4):15-18.
【7】俞芳, 高克玮, 乔利杰, 等.温度对N80 钢CO2腐蚀产物膜结构和力学性能的影响[J].腐蚀与防护, 2009, 30(3):145-148.
【8】张清, 李全安, 文九巴, 等.CO2/H2S对油气管材的腐蚀规律及研究进展[J].腐蚀与防护, 2003, 24(7):277-281.
相关信息