镍基合金6690换热管应力腐蚀开裂
SCC Behaviour of Nickel Base Alloy 6690 Heat Exchange Tubes
摘 要
为检验核电蒸汽发生器换热管管材应力腐蚀开裂(SCC)敏感性, 将管材制成C型环试样, 施加不同的环向应力, 按ASTM标准在沸腾氯化镁溶液(沸点155 ℃)中进行加速SCC试验, 来表征此管材的应力腐蚀行为, 并计算C型环平均腐蚀速率。最后对换热管耐蚀性能进行综合评价。
C型环
应力腐蚀开裂(SCC)
腐蚀速率
nickel base alloy
C-ring
SCC
corrosion rate
Abstract
To inspect the SCC susceptibility of heat exchanger tubes of steam generator, an accelerated SCC test was performed. C-ring samples with different circumferential stresses were tested in boiling magnesium chloride solution with a boiling point of 155 ℃ according to ASTM standards. The average corrosion rate of C-ring samples was calculated. The corrosion resistance of heat exchanger tubes were evaluated.
中图分类号 TG174
所属栏目 试验研究
基金项目
收稿日期 2012/6/12
修改稿日期
网络出版日期
作者单位点击查看
备注马小明, 副教授, 博士,
引用该论文: MA Xiao-ming,CHEN Cheng. SCC Behaviour of Nickel Base Alloy 6690 Heat Exchange Tubes[J]. Corrosion & Protection, 2013, 34(3): 239
被引情况:
【1】张志宏,张江江,孙海礁,肖雯雯,邵晓东,刘琰, "塔河油田某深井钻杆断裂原因",腐蚀与防护 35, 192-195(2014)
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】ASTM G38-07 Standard practice for making and using C-ring stress-corrosion test specimens[S].
【2】胡彬.不锈钢波纹管换热器的腐蚀与防护[J].江汉石油职工大学学报, 2004, 17(4):45-46.
【3】ASTM G1-03 Standard practice for preparing, cleaning and evaluating corrosion test specimens[S].
【4】盛永平.1Cr18Ni9Ti钢的特性分析[J].包头职业技术学院学报, 2004, 5(4):16-17.
【5】钱建刚, 李荻, 郭宝兰.10X11H23T3MP-BⅡ不锈钢材料的耐蚀性能[J].腐蚀科学与防护技术, 2004, 16(6):363-366.
【2】胡彬.不锈钢波纹管换热器的腐蚀与防护[J].江汉石油职工大学学报, 2004, 17(4):45-46.
【3】ASTM G1-03 Standard practice for preparing, cleaning and evaluating corrosion test specimens[S].
【4】盛永平.1Cr18Ni9Ti钢的特性分析[J].包头职业技术学院学报, 2004, 5(4):16-17.
【5】钱建刚, 李荻, 郭宝兰.10X11H23T3MP-BⅡ不锈钢材料的耐蚀性能[J].腐蚀科学与防护技术, 2004, 16(6):363-366.
相关信息