ETA水工况下SO2-4对690合金腐蚀行为的影响
Effect of SO42- Concentration on Corrosion Behaviors of Alloy 690 under ETA Water Chemistry Condition
摘 要
在PWR二回路乙醇胺(ETA)水工况下, 通过高温高压模拟试验和低温电化学试验研究了SO42-对690合金腐蚀行为的影响。结果表明, 在乙醇胺(ETA)水工况下,SO42-主要引发690合金的全面腐蚀和晶间腐蚀; 对基体元素中铬和铁的溶出有促进作用, 对镍的溶出有抑制作用; 铁的溶出量随着SO42-浓度的增大而增加, 铬和镍的溶出量受SO42-浓度的影响较小。
690合金
SO42-
腐蚀
ethanolamine(ETA)
alloy 690
SO42-
corrosion
Abstract
The corrosion behaviors of Alloy 690 in environments of ethanolamine (ETA) water chemistry condition were investigated by means of high temperature and high pressure simulated tests and low-temperature electrochemical tests, the effect of SO42- concentration was detailedly studied. The results showed that under the ETA water chemistry condition, SO42- mainly caused general corrosion and intergranular corrosion of alloy 690, the dissolution of the matrix elements Cr and Fe was promoted while the dissolution of Ni was inhibited. The dissolution of Fe increased with the increase of the concentration of SO42- while the dissolution of Ni and Cr was almost not affected.
中图分类号 TG174
所属栏目 试验研究
基金项目 电力与交通材料保护湖南省重点实验室开放基金资助项目(2010CL02)
收稿日期 2012/7/12
修改稿日期
网络出版日期
作者单位点击查看
联系人作者李宇春(iamlyc@263.net)
备注李宇春, 教授, 博士,
引用该论文: ZHANG Rui-feng,LI Yu-chun,PANG Fei-fei,LIU Xiao-wei. Effect of SO42- Concentration on Corrosion Behaviors of Alloy 690 under ETA Water Chemistry Condition[J]. Corrosion & Protection, 2013, 34(5): 413
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】朱志平.压水堆核电厂水工况及优化[M].北京: 原子能出版社, 2010.
【2】张孟琴, 陆玉成, 张宾永, 等.ETA对PER二回路设备材料抗蚀作用研究[J].中国原子能科学研究院年报,2002:98.
【3】丁训慎.核电站蒸汽发生器传热管的点腐蚀及其防护[J].腐蚀与防护.2007, 28(7):364-366.
【4】Wu Yang, Zhanpeng Lu, Delun Huang, et al. Caustic stress corrosion cracking of nickel-rich, chromium-bearing alloys [J]. Corrosion Science,2001,43(5): 963-977.
【5】龚正春, 孙永立, 孔繁革, 等.蒸汽发生器用690TT合金的组织结构和腐蚀性能[J].动力工程,2003,23(4): 2592-2596.
【6】丁训慎.核电站蒸汽发生器传热管二次侧晶间腐蚀和晶间应力腐蚀及防护[J].腐蚀与防护,2002.23(10): 441-444.
【2】张孟琴, 陆玉成, 张宾永, 等.ETA对PER二回路设备材料抗蚀作用研究[J].中国原子能科学研究院年报,2002:98.
【3】丁训慎.核电站蒸汽发生器传热管的点腐蚀及其防护[J].腐蚀与防护.2007, 28(7):364-366.
【4】Wu Yang, Zhanpeng Lu, Delun Huang, et al. Caustic stress corrosion cracking of nickel-rich, chromium-bearing alloys [J]. Corrosion Science,2001,43(5): 963-977.
【5】龚正春, 孙永立, 孔繁革, 等.蒸汽发生器用690TT合金的组织结构和腐蚀性能[J].动力工程,2003,23(4): 2592-2596.
【6】丁训慎.核电站蒸汽发生器传热管二次侧晶间腐蚀和晶间应力腐蚀及防护[J].腐蚀与防护,2002.23(10): 441-444.
相关信息