聚乙烯反应器夹套管的腐蚀与防护
Corrosion and Protection of Jacket Tubes in LDPE Reactor
摘 要
某高压聚乙烯装置反应器夹套管多次发生穿孔泄漏, 通过腐蚀形貌观察、材料化学成分分析以及ANSYS CFX模拟计算等方法对其进行失效分析, 发现氧腐蚀和气蚀是造成穿孔泄漏的主要原因。同时, 对预防该类腐蚀事件的再次发生提出了防护措施。
氧腐蚀
气蚀
jacket tube
oxygen corrosion
cavitation corrosion
Abstract
The perforation and corrosion of jacket tubes in a low-density polyethylene (LDPE) reactor occured repeatedly. By corrosion morphology, chemical component analysis and ANSYS CFX’s simulation calculation, it was revealed that oxygen corrosion and cavitation corrosion were the main reasons of the leakage. Based on the analysis result, some anticorrosion methords were proposed.
中图分类号 TG174
所属栏目 失效分析
基金项目
收稿日期 2012/7/14
修改稿日期
网络出版日期
作者单位点击查看
备注曾科烽, 助理工程师, 硕士,
引用该论文: ZENG Ke-feng. Corrosion and Protection of Jacket Tubes in LDPE Reactor[J]. Corrosion & Protection, 2013, 34(5): 455
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】余斯宽.供暖管道内壁的腐蚀与防护[J].腐蚀与防护, 1999, 20(2): 86-89.
【2】刘洁, 方彦凯.生物柴油原料中溶解氧对20R钢的腐蚀[J].腐蚀与防护, 2009, 30(10): 711-712.
【3】环久峰, 王栋, 陈贵军, 等.空冷换热器水质诊断及腐蚀控制对策[J].腐蚀与防护, 2006, 27(4): 208-211.
【4】马桂军, 杜敏, 刘福国等.G105钻具刚在含有溶解氧条件下的腐蚀规律[J].中国腐蚀与防护学报, 2008, 28(2): 108-110.
【5】刘瑛.电厂除氧器的腐蚀原因分析及其热喷涂防护[J].全面腐蚀控制, 2006, 20(5): 15-18.
【6】袁永军.高压锅炉补给水系统管道的腐蚀[J].石油化工腐蚀与防护, 2002, 19(5): 20-21.
【7】杨卫国, 徐君铭.溶氧腐蚀—一种容易被忽视的腐蚀形式[J].广州化工, 2005, 33(3): 74-75.
【8】陈志军.蒸汽冷凝水管线频繁腐蚀穿孔问题的研究与解决对策[J].化工设备与管道, 2008, 45(4): 68-70.
【9】田峰, 高岩, 孙承华.化学除氧在防腐蚀中的应用[J].橡胶技术与装备, 2000, 26(1): 59-60.
【2】刘洁, 方彦凯.生物柴油原料中溶解氧对20R钢的腐蚀[J].腐蚀与防护, 2009, 30(10): 711-712.
【3】环久峰, 王栋, 陈贵军, 等.空冷换热器水质诊断及腐蚀控制对策[J].腐蚀与防护, 2006, 27(4): 208-211.
【4】马桂军, 杜敏, 刘福国等.G105钻具刚在含有溶解氧条件下的腐蚀规律[J].中国腐蚀与防护学报, 2008, 28(2): 108-110.
【5】刘瑛.电厂除氧器的腐蚀原因分析及其热喷涂防护[J].全面腐蚀控制, 2006, 20(5): 15-18.
【6】袁永军.高压锅炉补给水系统管道的腐蚀[J].石油化工腐蚀与防护, 2002, 19(5): 20-21.
【7】杨卫国, 徐君铭.溶氧腐蚀—一种容易被忽视的腐蚀形式[J].广州化工, 2005, 33(3): 74-75.
【8】陈志军.蒸汽冷凝水管线频繁腐蚀穿孔问题的研究与解决对策[J].化工设备与管道, 2008, 45(4): 68-70.
【9】田峰, 高岩, 孙承华.化学除氧在防腐蚀中的应用[J].橡胶技术与装备, 2000, 26(1): 59-60.
相关信息