再热主汽门轴封蒸汽疏水管线失效分析
Failure Analysis of Gland Seal Steam Drain Pipe of Reheat Stop Valve
摘 要
秦山第三核电厂一根再热主汽门轴封蒸汽疏水管线发生断裂泄漏, 漏点位于靠近再热主汽门引出管嘴处。对该管段失效部位进行了宏观检查, 对母材、热影响区、焊缝区分别进行了化学成分、金相、腐蚀产物分析, 观察了断口形貌, 确定管线失效原因主要为:靠近再热主汽门阀体的管段内壁在高温水蒸汽中的氧化腐蚀导致壁厚显著减薄, 并由于管线在机组正常运行期间的振动产生腐蚀疲劳, 最终导致断裂泄漏。
失效分析
碳钢管
氧化腐蚀
腐蚀疲劳
nuclear power plant
failure analysis
carbon steel pipe
oxidation corrosion
corrosion fatigue
Abstract
Fracture and leakage happened at the gland seal steam drain pipe of a reheat stop valve in Third Qinshan Nuclear Power Co., Ltd. The failure location was near the nozzle of the valve. Examination was conducted on the failed section of the pipe. The chemical compositions, microstructure and corrosion products of the parent metal, heat affected zone and butt weld of the pipe were examined. The fracture surface was observed. It is concluded that the main failure causes should be as follows: (1) oxidation corrosion on the pipe inner surface near the valve caused by high temperature steam resulted in the pipe wall thinning significantly; (2) corrosion fatigue due to pipe vibration lead to the final fracture.
中图分类号 TG172
所属栏目 失效分析
基金项目
收稿日期 2013/1/5
修改稿日期
网络出版日期
作者单位点击查看
备注赵亮,工程师,硕士,
引用该论文: ZHAO Liang,ZHAO Ting,LI Guang-fu. Failure Analysis of Gland Seal Steam Drain Pipe of Reheat Stop Valve[J]. Corrosion & Protection, 2013, 34(5): 458
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】窦照英. 电力工业的腐蚀与防护[M]. 北京: 化学工业出版社, 1995.
【2】Pascale Vangeli. Oxidation of S35315 in water vapor containing atmospheres under cyclic and isothermal conditions[C]//Corrosion 2006[s.l.]:[s.n.],2006:6478.
【3】王志武, 邓芳, 王玉山, 等. 20G钢高温高压水蒸汽氧化行为研究[J]. 腐蚀科学与防护技术,2008, 20(3):170-172.
【4】耿波, 刘江南, 赵颜芬, 等. T91钢高温水蒸汽氧化层形成机理研究[J]. 铸造技术,2004, 25(12): 914-918.
【5】金耀华, 王正品, 刘江南, 等. T91钢在两种不同环境下的高温氧化层剥落机理研究[J]. 铸造技术,2005, 26(11):1039-1041.
【6】王正品, 张路, 刘江南, 等. 电站用T22及与T91管高温蒸汽氧化的失效分析[J]. 铸造技术,2004, 25(7):523-525.
【7】冯斌, 刘铁祥, 张玉福, 等. 过热器和再热器管内壁的高温水蒸汽腐蚀研究[J]. 湖南电力,2006,26(6):8-11.
【8】齐慧滨,郭英倬,何业东, 等. 燃煤火电厂锅炉四管的高温腐蚀[J]. 腐蚀科学与防护技术,2002, 14(2): 113-119.
【2】Pascale Vangeli. Oxidation of S35315 in water vapor containing atmospheres under cyclic and isothermal conditions[C]//Corrosion 2006[s.l.]:[s.n.],2006:6478.
【3】王志武, 邓芳, 王玉山, 等. 20G钢高温高压水蒸汽氧化行为研究[J]. 腐蚀科学与防护技术,2008, 20(3):170-172.
【4】耿波, 刘江南, 赵颜芬, 等. T91钢高温水蒸汽氧化层形成机理研究[J]. 铸造技术,2004, 25(12): 914-918.
【5】金耀华, 王正品, 刘江南, 等. T91钢在两种不同环境下的高温氧化层剥落机理研究[J]. 铸造技术,2005, 26(11):1039-1041.
【6】王正品, 张路, 刘江南, 等. 电站用T22及与T91管高温蒸汽氧化的失效分析[J]. 铸造技术,2004, 25(7):523-525.
【7】冯斌, 刘铁祥, 张玉福, 等. 过热器和再热器管内壁的高温水蒸汽腐蚀研究[J]. 湖南电力,2006,26(6):8-11.
【8】齐慧滨,郭英倬,何业东, 等. 燃煤火电厂锅炉四管的高温腐蚀[J]. 腐蚀科学与防护技术,2002, 14(2): 113-119.
相关信息