Causes of Corrosion and Leakage of High-pressure Heater Tubes in a Thermal Power Plant
摘 要
某电厂660MW机组高压加热器的换热管材质为TP304奥氏体不锈钢管,机组投运不到半年,该机组的三台高压加热器就分别出现了不同程度的泄漏。通过检测换热管材料的元素组成、力学性能和抗晶间腐蚀性能,排除腐蚀开裂是材料性能不达标造成的可能性。通过对材料表面的EDS分析和腐蚀开裂面的SEM分析,确定高压加热器短期腐蚀开裂的主要原因是在高压加热器汽侧高温高压条件下,侵蚀性介质氯离子在设备运行振动作用下,促进换热管快速发生腐蚀疲劳开裂。
Abstract
The high-pressure heater tubes of a 660MW thermal power plant are made of TP304 austenitic stainless steel. After half year operation, the different degree of leakage of three high-pressure heaters occurred. By testing of chemical composition, mechanical properties and intergranular corrosion of high-pressure heater materials, it is shown that the corrosion cracking was not caused by unqualified material. The results of EDS of tube surface and SEM of cracking surface reveal that corrosion fatigue caused leakage of high-pressure heater tubes, due to the high concentration of Cl- in vapor and vibration of equipment during operation.
中图分类号 TG174
所属栏目 失效分析
基金项目
收稿日期 2012/10/11
修改稿日期
网络出版日期
作者单位点击查看
备注林卫丽,讲师,硕士,
引用该论文: LIN Wei-li,DENG Yu-qiang,ZHAO Guang-sen,SONG Fei,LIU Feng,QI Dong-dong,NI Rui-tao. Causes of Corrosion and Leakage of High-pressure Heater Tubes in a Thermal Power Plant[J]. Corrosion & Protection, 2013, 34(8): 757
共有人对该论文发表了看法,其中:
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】马士东,袁洪涛. 600MW超临界汽轮机高压加热器泄漏原因分析及处理[J]. 电力技术,2010,19(6): 32-35.
【2】国金莲,张福君,王晓强. 高压加热器换热管破坏和预防[J]. 锅炉制造,2005,4(12): 43-44.
【3】吴剑. 不锈钢的腐蚀破坏与防蚀技术——(五)腐蚀疲劳[J]. 腐蚀与防护,1997,18(6): 37-39.
【2】国金莲,张福君,王晓强. 高压加热器换热管破坏和预防[J]. 锅炉制造,2005,4(12): 43-44.
【3】吴剑. 不锈钢的腐蚀破坏与防蚀技术——(五)腐蚀疲劳[J]. 腐蚀与防护,1997,18(6): 37-39.
相关信息