Evaluation of Pitting Corrosion Performance of 13Cr Series Martensitic Stainless Steels
摘 要
采用动电位扫描、FeCl3溶液浸泡和模拟油井井下环境的CO2腐蚀试验等方法研究了四种不同成分的13Cr马氏体不锈钢的点蚀性能。结果表明, 动电位扫描和模拟井况腐蚀试验结果一致, 随耐点蚀当量指数(PRE)的增大, 材料的耐点蚀性能提高; 在FeCl3溶液中, PRE较低的材料发生均匀腐蚀,而PRE较高的材料发生点蚀。
Abstract
Pitting corrosion performance of four different 13Cr martensitic stainless steels were evaluated through the dynamic potential scanning method, FeCl3 solution immersion test and simulated downhole environment corrosion test. The results of dynamic potential scanning were agreement with those of the simulated corrosion. The pitting corrosion resistance increased with the increase of PRE, however, in the FeCl3 solution only general corrosion occurred for the lower PRE 13Cr materials while severe pitting appeared for the higher PRE 13Cr materials.
中图分类号 TG174
所属栏目 试验研究
基金项目
收稿日期 2012/11/27
修改稿日期
网络出版日期
作者单位点击查看
备注马朝晖,高级工程师,
引用该论文: MA Zhao-hui. Evaluation of Pitting Corrosion Performance of 13Cr Series Martensitic Stainless Steels[J]. Corrosion & Protection, 2013, 34(9): 819
被引情况:
【1】朱培珂,邓金根,闫伟,李明洋,吴山,彭程, "3Cr钢和13Cr钢在高矿化度CO2环境中的腐蚀行为",腐蚀与防护 35, 1221-1225(2014)
共有人对该论文发表了看法,其中:
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】Denpo K,Ogawa H. Fluid flow effects on CO2 corrosion resistance of oil well materials[J]. Corrosion,1993,49(6):442.
【2】Pereda M D,Gerrasi C A,Llorente C L,et al. Microelectoochemical corrosion study of super martensitic welds in chloride-containing media[J]. Corrosion Science,2011,52(12):3934-3941.
【3】Hara T,Asahi H,Suehiro Y,et al, Effect of flow velocity on carbon dioxide corrosion behavior in oil and gas environments[J]. Corrosion,1994,56(8):860-865.
【2】Pereda M D,Gerrasi C A,Llorente C L,et al. Microelectoochemical corrosion study of super martensitic welds in chloride-containing media[J]. Corrosion Science,2011,52(12):3934-3941.
【3】Hara T,Asahi H,Suehiro Y,et al, Effect of flow velocity on carbon dioxide corrosion behavior in oil and gas environments[J]. Corrosion,1994,56(8):860-865.
相关信息