Atmospheric Corrosion of Metal Coatings
摘 要
对铜镀银、铜镀镍、铜喷铝和铜镀锌等材料在富含H2S,SO2和NH3等腐蚀性气体环境中进行了腐蚀试验和盐雾腐蚀试验。结果表明,氨对铜基材表面镀层破坏程度最大,硫化氢和二氧化硫次之; 在试验条件下,四种材料的耐蚀性能强弱依次为铜喷铝、铜镀锌、铜镀银和铜镀镍。铜表面镀层一旦腐蚀,会很快在腐蚀部位发生大面积加速腐蚀,因此,在部件的运输和安装施工中尽量减少对保护层的破坏。
Abstract
Sliver plated copper, nickel plated copper, aluminum sprayed copper and zinc plated copper were choosed to study the effect of atmospheric environment on metal material corrosion by means of corrosion testing in simulation corrosive gas environments containing H2S, SO2 and NH3, and salt spray testing. The results show that the corrosion of surface coatings on copper substrate caused by ammonia was the most serious and the next were by hydrogen sulfide and sulfur dioxide. The corrosion resistance of four materials in turn is as follows: Al sprayed Cu> Zn plated Cu> Ag plated Cu> Ni plated Cu. Once the coatings on the Cu was corroded, large area corrosion will occur around it, so the destroy by materials transportation and setting must be reduced.
中图分类号 TG174
所属栏目 试验研究
基金项目
收稿日期 2012/12/25
修改稿日期
网络出版日期
作者单位点击查看
联系人作者王平(hbdyywp@126.com)
备注王平,高级工程师,
引用该论文: WANG Ping,ZHOU Hui-bo,LIU Qiang. Atmospheric Corrosion of Metal Coatings[J]. Corrosion & Protection, 2013, 34(10): 926
被引情况:
【1】任汉涛,银朝晖,王平,周慧波,柳森,徐松,朱志平, "电网铜材在含H2S大气中的腐蚀研究现状",腐蚀与防护 35, 1074-1077(2014)
共有人对该论文发表了看法,其中:
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
相关信息