Effect of T4 Heat Treatment on Microstructure and Mechanical Properties of AM60 Magnesium Alloys with Different Nd Contents
摘 要
用真空电阻炉、在氩气保护下制备了不同钕含量的AM60合金, 用箱式电阻炉对其进行了T4热处理; 研究了两种状态合金显微组织和力学性能随钕元素含量的变化规律。结果表明: 铸态合金的显微组织均主要由α-Mg基体相、β-Mg17Al12相和Al11Nd3相组成; T4热处理后, β-Mg17Al12相溶解到α-Mg基体相中, 合金晶粒明显细化, Al11Nd3相形貌上有较大的变化; 随钕含量的增加, 合金的抗拉强度、屈服强度和伸长率均先升后降, 峰值时钕含量由铸态的0.9%降到T4态的0.3%, T4态的分别达239, 138 MPa和8%, 显微硬度峰值出现在0.6%Nd, 为70.5 HV。
Abstract
AM60 alloys with different Nd contents were prepared in vacuum resistance furnace under Ar atmosphere, and then T4 heat treatment was carried out in box-type resistance furnace. The change law of the microstructure and mechanical properties of two state alloys was studied. The results show that the microstructure of as-cast alloys mainly consisted of α-Mg matrix phase, β-Mg17Al12 phase and Al11Nd3 phase. After T4 heat treatment, the β-Mg17Al12 phase decomposed and dissolved into the α-Mg matrix phase. The grain size of alloys was refined obviously and the morphology of Al11Nd3 phase changed greatly. With the increase of Nd content, the tensile strength, yield strength and elongation increased first and then decreased. The peak values of the mechanical properties changed from 0.9%Nd in as-cast state to 0.3%Nd in T4 state, which reached 239 MPa, 138 MPa and 8%, respectively. The microhardness of the 0.6%Nd alloy reached 70.5 HV.
中图分类号 TG146.2
所属栏目
基金项目 山西省留学基金资助项目(2008-39)
收稿日期 2010/4/22
修改稿日期 2011/1/10
网络出版日期
作者单位点击查看
备注郭端阳(1964-), 女, 山西临猗人, 工程师, 学士。
引用该论文: GUO Rui-yang,WANG Guo-jun,WANG She-bin,ZHANG Jin-ling,CHEN Gang,XU Bing-she. Effect of T4 Heat Treatment on Microstructure and Mechanical Properties of AM60 Magnesium Alloys with Different Nd Contents[J]. Materials for mechancial engineering, 2011, 35(4): 32~37
郭端阳,王国军,王社斌,张金玲,陈刚,许并社. T4热处理对不同钕含量AM60镁合金显微组织和力学性能的影响[J]. 机械工程材料, 2011, 35(4): 32~37
共有人对该论文发表了看法,其中:
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】王渠东, 曾小勤.镁合金在汽车上的应用状况[J].汽车技术,1999(8):28-31.
【2】田政,宋波,刘勇兵.AM系镁合金在汽车工业中的应用与发展[J ].汽车工艺与材料,2004(7):21-24.
【3】张景怀,唐定骧,张洪杰,等.稀土元素在镁合金中的作用及其应用[J].稀有金属,2008,32(5):659-667.
【4】WEI L Y, DUMLOP G L, WESTENGEN H. Development of microstructure in cast Mg-Al-rare earth alloys [J].Materials Science and Technology,1996,12(9):741-750.
【5】王社斌,张金玲,张俊远,等.AZ91镁合金中La的吸收率及其影响因素[J].中国有色金属学报, 2007,17(6): 968-972.
【6】王社斌,李晓斌,范晋平,等.Mg-5Al-0.8Ca-0.2La-xSr合金的显微组织及高温力学性能[J].中国有色金属学报, 2009,19(5): 826-832.
【7】ZHANG Jin-wang, WANG She-bin, ZHANG Jun-yuan. Effects of Nd on microstructures and mechanical properties of AM60 magnesium alloy in vacuum melting[J].Rare Metal Materials and Engineering,2009,38(7):1141-1145.
【8】王社斌, 张金玲,卫英慧,等.真空熔炼AZ91镁合金过程中Mg元素的蒸发行为[J].稀有金属与工程, 2007,36(9):1601-1604.
【9】王帅,王社斌,李晓斌,等.Sb对AE42镁合金中稀土元素的替代作用[J].太原理工大学学报, 2009,40(1):56-59.
【10】曾书峰,夏鹏举,袁森,等.Nd变质处理对AM60合金组织细化的影响[J].铸造技术,2008,29(9):1210-1213.
【11】宋波,刘勇兵,安健.钕及固溶处理对AM60合金组织的力学性能的影响[J].铸造技术, 2006,27(12): 1299-1302.
【12】张青辉, 黄维刚, 郑天群,等.热处理对Mg-Zn-Al合金力学性能的影响[J].热加工工艺,2007,36(8):62-64.
【13】王小强,李全安,张兴渊,等.Y, Nd 复合稀土对AZ81镁合金组织和力学性能的影响[J].稀有材料与工程,2008, 37(1):63-65.
【14】张俊远,王社斌,王帅,等.真空条件下Nd对AM60镁合金组织与性能的影响[J].太原理工大学学报,2009,40(1):51-55.
【15】黄晓锋,付彭怀,卢晨,等.Nd对AM50 力学性能及高温性能的影响[J].材料研究学报,2004,18(6):593-596.
【16】杨友,刘勇兵,方懿.AZ91D+xNd压铸镁合金拉伸和疲劳断裂模式[J].铸造,2007,56(1): 41-45.
【2】田政,宋波,刘勇兵.AM系镁合金在汽车工业中的应用与发展[J ].汽车工艺与材料,2004(7):21-24.
【3】张景怀,唐定骧,张洪杰,等.稀土元素在镁合金中的作用及其应用[J].稀有金属,2008,32(5):659-667.
【4】WEI L Y, DUMLOP G L, WESTENGEN H. Development of microstructure in cast Mg-Al-rare earth alloys [J].Materials Science and Technology,1996,12(9):741-750.
【5】王社斌,张金玲,张俊远,等.AZ91镁合金中La的吸收率及其影响因素[J].中国有色金属学报, 2007,17(6): 968-972.
【6】王社斌,李晓斌,范晋平,等.Mg-5Al-0.8Ca-0.2La-xSr合金的显微组织及高温力学性能[J].中国有色金属学报, 2009,19(5): 826-832.
【7】ZHANG Jin-wang, WANG She-bin, ZHANG Jun-yuan. Effects of Nd on microstructures and mechanical properties of AM60 magnesium alloy in vacuum melting[J].Rare Metal Materials and Engineering,2009,38(7):1141-1145.
【8】王社斌, 张金玲,卫英慧,等.真空熔炼AZ91镁合金过程中Mg元素的蒸发行为[J].稀有金属与工程, 2007,36(9):1601-1604.
【9】王帅,王社斌,李晓斌,等.Sb对AE42镁合金中稀土元素的替代作用[J].太原理工大学学报, 2009,40(1):56-59.
【10】曾书峰,夏鹏举,袁森,等.Nd变质处理对AM60合金组织细化的影响[J].铸造技术,2008,29(9):1210-1213.
【11】宋波,刘勇兵,安健.钕及固溶处理对AM60合金组织的力学性能的影响[J].铸造技术, 2006,27(12): 1299-1302.
【12】张青辉, 黄维刚, 郑天群,等.热处理对Mg-Zn-Al合金力学性能的影响[J].热加工工艺,2007,36(8):62-64.
【13】王小强,李全安,张兴渊,等.Y, Nd 复合稀土对AZ81镁合金组织和力学性能的影响[J].稀有材料与工程,2008, 37(1):63-65.
【14】张俊远,王社斌,王帅,等.真空条件下Nd对AM60镁合金组织与性能的影响[J].太原理工大学学报,2009,40(1):51-55.
【15】黄晓锋,付彭怀,卢晨,等.Nd对AM50 力学性能及高温性能的影响[J].材料研究学报,2004,18(6):593-596.
【16】杨友,刘勇兵,方懿.AZ91D+xNd压铸镁合金拉伸和疲劳断裂模式[J].铸造,2007,56(1): 41-45.
相关信息