钛合金表面柔性电极电火花强化层的组织与性能
Microstructure and Properties of Electrospark Strengthening Layer on Titanium Alloy Surface by Flexible Electrode
摘 要
采用旋转的柔性铜电极在空气中对钛合金表面进行强化处理, 并采用SEM、XRD、硬度计、表面粗糙度仪等对强化层进行了研究。结果表明: 试验条件下, 钛合金强化层由氧化物(TiO等)和金属间化合物(CuTi、Zn2TiO4、Cu4Ti3等)组成, 厚度达到13～110 μm, 且随电流密度的增大而增厚; 强化层晶粒得到细化, 甚至产生了纳米晶; 表面硬度相对基体提高195%~266%, 且表面硬度随放电能量密度的增大而提高; 表面强化处理对钛合金表面粗糙度影响较小。
柔性电极
电火花
表面强化
titanium alloy
flexible electrode
electrospark
surface strengthening
Abstract
By a revolving flexible copper electrode, titanium alloy surface was strengthening treated in air. The strengthening layer was researched by SEM, XRD, hardness tester and surface roughness tester. The results show that the titanium alloy strengthened layer consisted of oxides (TiO, etc) and intermetallic compounds (CuTi, Zn2TiO4, Cu4Ti3, etc). The thickness of the strengthened layer was 13-110 μm and increased with increasing the current density. Grains in the strengthened layer were refined and even nano-crystalline formed. Compared to the matrix hardness the surface hardness increased by 195% to 266%, and increased with increasing the discharge energy density. Surface strengthening treatment had little effect on surface roughness of the titanium alloy.
中图分类号 TG661
所属栏目
基金项目 国防“十一五”基础研究资助项目(A2520060235)
收稿日期 2010/2/25
修改稿日期 2010/12/10
网络出版日期
作者单位点击查看
备注徐安阳(1981-), 男, 河南驻马店人, 博士研究生。
引用该论文: XU An-yang,LIU Zhi-dong,WANG Zhen-xing,ZHANG Yan. Microstructure and Properties of Electrospark Strengthening Layer on Titanium Alloy Surface by Flexible Electrode[J]. Materials for mechancial engineering, 2011, 35(4): 46～48
徐安阳,刘志东,王振兴,张艳. 钛合金表面柔性电极电火花强化层的组织与性能[J]. 机械工程材料, 2011, 35(4): 46～48
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】GALINOV I V, LUBAN R B. Mass trends during electrospark alloying[J].Surface and Coatings Technology,1996,79:9-18.
【2】张春辉,游涛,闫平,等.钛合金表面电火花沉积强化研究现状[J].稀有金属快报,2007,26(2):1-6.
【3】中国航空材料手册编辑委员会.中国航空材料手册[M].北京:中国标准出版社,2001.
【2】张春辉,游涛,闫平,等.钛合金表面电火花沉积强化研究现状[J].稀有金属快报,2007,26(2):1-6.
【3】中国航空材料手册编辑委员会.中国航空材料手册[M].北京:中国标准出版社,2001.
相关信息