大功率风力发电机增速齿轮断裂原因分析
Failure Analysis on Boost Gear of A Large Capacity Wind Power Generator
摘 要
通过断口宏微观形貌观察、化学成分分析、显微组织观察以及硬度测试等方法, 系统分析了某大功率风力发电机增速齿轮断裂的原因。结果表明: 轮齿外表面存在密集分布的点蚀坑及微孔缺陷, 是裂纹源;在较高水平的冲击与弯曲载荷共同作用下使微裂纹扩展, 从而最终导致齿轮疲劳断裂。
增速器
疲劳断裂
失效分析
wind power generator
boost gearbox
fatigue fracture
failure analysis
Abstract
By means of macro and micro fracture morphology observation, chemical composition analysis, microstructure observation and hardness test, the failure causes of the boost gear of a large capacity wind power generator were investigated systemically. The results show that densely distributed pits and micro-voids existed on the external surface of the gear, which were the crack origins, caused the mirco cracks propagation under the combined action of severe impact and bending load, and finally resulted in the fatigue fracture.
中图分类号 TK83
所属栏目
基金项目
收稿日期 2010/6/16
修改稿日期 2011/4/8
网络出版日期
作者单位点击查看
备注马小明(1962-), 男, 甘肃天水人, 副教授。
引用该论文: MA Xiao-ming,WU Nie-xiu. Failure Analysis on Boost Gear of A Large Capacity Wind Power Generator[J]. Materials for mechancial engineering, 2011, 35(7): 93～95
马小明,伍聂修. 大功率风力发电机增速齿轮断裂原因分析[J]. 机械工程材料, 2011, 35(7): 93～95
被引情况:
【1】秦林,赵琪,杨昆昆,唐宾, "TC4钛合金齿轮表面渗钼合金化后的组织与性能",机械工程材料 37, 74-78(2013)
【2】马小明,黄志华, "聚丙烯挤出机螺杆轴断裂失效分析",机械工程材料 38, 97-100(2014)
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】刘正义, 吴连生, 许麟康, 等.机械装备失效分析图谱[M].广州: 广东科技出版社, 1990.
【2】任颂赞, 张静江, 陈质如, 等.钢铁金相图谱[M].上海: 上海科学技术文献出版社, 2003.
【3】机械设计手册联合编写组.机械设计手册[M].北京: 化学工业出版社, 2008.
【4】唐定国, 袁和相.齿轮设计中的强度安全系数[J].机械传动, 1994(3): 18-20.
【5】黄华梁, 彭文山.机械设计基础[M].北京: 高等教育出版社, 2001.
【2】任颂赞, 张静江, 陈质如, 等.钢铁金相图谱[M].上海: 上海科学技术文献出版社, 2003.
【3】机械设计手册联合编写组.机械设计手册[M].北京: 化学工业出版社, 2008.
【4】唐定国, 袁和相.齿轮设计中的强度安全系数[J].机械传动, 1994(3): 18-20.
【5】黄华梁, 彭文山.机械设计基础[M].北京: 高等教育出版社, 2001.
相关信息