加氢管线泄漏原因分析
Failure Analysis of Cracking of Hydrogenation Pipeline
摘 要
采用宏微观形貌分析、渗透探伤、化学成分分析、显微组织分析、力学性能测试、EDS微区成分分析等手段, 分析了20钢加氢管线泄漏的原因。结果表明: 20钢加氢管线泄漏是因为管材存在锻造裂纹, 该裂纹在焊接残余应力和工作应力的作用下扩展, 同时管材内表面局部冲刷腐蚀减薄也加快了锻造裂纹的扩展, 最后导致开裂。
20钢
锻造裂纹
hydrogenation pipeline
20 steel
forging crack
Abstract
The leak reason of hydrogenation pipeline made of 20 steel was analyzed by means of macroscopic and microscopic morphology analysis, penetrant testing, chemical composition analysis, microstructure analysis, mechanical property testing and EDS micro area composition analysis. The results show that the leak of the 20 steel pipeline was caused by forging crack which grew under the welding residual stress and work stress. Local corrosion at the interface of the pipeline accelerated the growth of forging cracks.
中图分类号 TG157
所属栏目
基金项目
收稿日期 2010/7/1
修改稿日期 2010/12/10
网络出版日期
作者单位点击查看
备注丁毅(1965-), 男, 江苏溧阳人, 副教授。
引用该论文: DING Yi,MA Li-yang,ZHAI Chun-rong,SHI Hong-qi,MA Li-qun. Failure Analysis of Cracking of Hydrogenation Pipeline[J]. Materials for mechancial engineering, 2011, 35(7): 96～99
丁毅,马李洋,翟春荣,师红旗,马立群. 加氢管线泄漏原因分析[J]. 机械工程材料, 2011, 35(7): 96～99
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】张启芳.热加工工艺基础[M].南京: 东南大学出版社, 1996.
【2】陈裕川.焊接工艺设计与实例分析[M].北京: 机械工业出版社, 2010.
【2】陈裕川.焊接工艺设计与实例分析[M].北京: 机械工业出版社, 2010.
相关信息