xStructure and Dielectric Properties of xSrTiO3-(1-x)LaAlO3 Dielectric Ceramics
摘 要
采用固相反应法制备了xSrTiO3-(1-x)LaAlO3(x=0.4~0.7)介电陶瓷, 分析了不同x值陶瓷的结构和介电性能。结果表明: 该陶瓷主相为钙钛矿固溶体, x= 0.4~0.5时, 为正交钙钛矿结构, 在x=0.55~0.7时, 为赝立方钙钛矿结构; 赝立方结构的陶瓷具有较高的介电常数(ε>50)和低介电损耗(10-3~10-4)及近零的温度系数; 陶瓷从赝立方结构转变成正交结构时, 介电常数明显下降(ε=34~45), 介电损耗迅速增大(约10-2); x=0.6,0.7的陶瓷具有优良的介电性能, ε>55, tanδ在10-3~10-4之间(f=1 MHz);x=0.4时陶瓷具有优异的微波介电性能, ε =30.5, Qf=40 177 GHz, τf= -22.9×10- 6 ℃-1。
Abstract
xSrTiO3-(1-x) LaAlO3(x=0.4-0.7) dielectric ceramics were prepared by solid state reaction method, the structure and properties of ceramics with different x value were discussed. The results show that perovskite solid solution was the main phase of this ceramics. The perovskite were orthogonal structure and constrain cubic structure when x were 0.4-0.5 and 0.55-0.7 respectively. The ceramics with the pseudocubic structure exhibited the higher dielectric constant (ε>50), lower dielectric loss(10-3-10-4)and near-zero temperature coefficient. The dielectric constant decreased obviously (ε=35-45) and dielectric loss increased rapidly (about 10-2)when the ceramics transformed from orthogonal structure to the constrain cubic structure. Good dielectric properties (ε>55, tan δ of the ceramics was about 10-3-10-4 at 1 MHz)were achieved when x was 0.6 and 0.7. Excellent microwave dielectric properties of ceramic (x=0.4) were achieved as following: ε =30.5, Qf=40 177 GHz, τf = -22.9×10- 6℃-1.
中图分类号 TQ174
所属栏目
基金项目 福建省高等学校新世纪优秀人才支持项目计划(XSJRC2007-16); 福建省发改委项目
收稿日期 2010/10/1
修改稿日期 2011/6/20
网络出版日期
作者单位点击查看
备注雷慎辉(1984-), 男, 陕西西安人, 硕士研究生。
引用该论文: LEI Shen-Hui,ZHENG Xing-hua,TANG De-ping,LIN Jia. xStructure and Dielectric Properties of xSrTiO3-(1-x)LaAlO3 Dielectric Ceramics[J]. Materials for mechancial engineering, 2011, 35(10): 84~87
雷慎辉,郑兴华,汤德平,林佳. xSrTiO3-(1-x)LaAlO3介电陶瓷的结构和介电性能[J]. 机械工程材料, 2011, 35(10): 84~87
被引情况:
【1】房明瑞,王卓,李海娟,王春, "Ba(Fe0.5Nb0.5)O3基复相陶瓷的制备与介电性能",机械工程材料 40, 59-64(2016)
共有人对该论文发表了看法,其中:
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】FREER R, AZOUGH F. Microstructural engineering of microwave dielectric ceramics[J]. J Eur Ceram Soc,2008,28:1433-1441.
【2】REANEY I M, IDDLES D. Microwave dielectric ceramics for resonators and filters in mobile phone networks[J]. J Am Ceram Soc,2006,89:2063-2072.
【3】BELOUS A G. Physicochemical aspects of the development of MW dielectrics and their use[J]. J Eur Ceram Soc,2001,21:2717-2722.
【4】KELL R C, GREENHAM A C, OLDS G C E. High-permittivity temperature-stable ceramic dielectrics with low microwave loss[J]. J Am Ceram Soc,1973,56:352-354.
【5】SHIMADA T, KURA K, OHTSUKI S. Dielectric properties and far infrared reflectivity of lanthanum aluminate-strontium titanate ceramics[J]. J Eur Ceram Soc,2006,26:2017-2021.
【6】CHO S Y, KIM I T, HONG K S. Microwave dielectric properties and application of rare-earth aluminates[J]. J Mater Res,1999,41(1):114-119.
【7】HAKKI B W, COLEMAN P D. A dielectric resonantor method of measuring inductive capacities in the millimeter range[J]. IRE Transactions on Microwave Theory and Techniques,1960,8(7):402-410.
【8】SUN P H, NAKAMURA T, SHAN Y J, et al. Dielectric behavior of (1-x)LaAlO3-xSrTiO3 solid solution system at microwave frequencies[J]. Jpn J Appl Phys,1998,37(10):5625-5629.
【9】SCHWINGENSCHLOGL U, SCHUSTER C. Exponential decay of relaxation effects at LaAlO3/SrTiO3 heterointerfaces[J]. Chem Phys Lett,2009,467:354-357.
【10】CHO S Y, HONG K S, KO K H.Mixture-like behavior in the microwave dielectric properties of the (1-x)LaAlO3-xSrTiO3 system[J]. Mater Res Bull,1999,34(4):511-516.
【2】REANEY I M, IDDLES D. Microwave dielectric ceramics for resonators and filters in mobile phone networks[J]. J Am Ceram Soc,2006,89:2063-2072.
【3】BELOUS A G. Physicochemical aspects of the development of MW dielectrics and their use[J]. J Eur Ceram Soc,2001,21:2717-2722.
【4】KELL R C, GREENHAM A C, OLDS G C E. High-permittivity temperature-stable ceramic dielectrics with low microwave loss[J]. J Am Ceram Soc,1973,56:352-354.
【5】SHIMADA T, KURA K, OHTSUKI S. Dielectric properties and far infrared reflectivity of lanthanum aluminate-strontium titanate ceramics[J]. J Eur Ceram Soc,2006,26:2017-2021.
【6】CHO S Y, KIM I T, HONG K S. Microwave dielectric properties and application of rare-earth aluminates[J]. J Mater Res,1999,41(1):114-119.
【7】HAKKI B W, COLEMAN P D. A dielectric resonantor method of measuring inductive capacities in the millimeter range[J]. IRE Transactions on Microwave Theory and Techniques,1960,8(7):402-410.
【8】SUN P H, NAKAMURA T, SHAN Y J, et al. Dielectric behavior of (1-x)LaAlO3-xSrTiO3 solid solution system at microwave frequencies[J]. Jpn J Appl Phys,1998,37(10):5625-5629.
【9】SCHWINGENSCHLOGL U, SCHUSTER C. Exponential decay of relaxation effects at LaAlO3/SrTiO3 heterointerfaces[J]. Chem Phys Lett,2009,467:354-357.
【10】CHO S Y, HONG K S, KO K H.Mixture-like behavior in the microwave dielectric properties of the (1-x)LaAlO3-xSrTiO3 system[J]. Mater Res Bull,1999,34(4):511-516.
相关信息