铝含量对SiCp/Ti基复合材料组织与性能的影响
Effect of Al Content on Microstructure and Property of SiC Particles Reinforced Ti Matrix Composites
摘 要
利用空心阴极烧结工艺制备了SiCp/Ti基复合材料, 研究了铝含量对复合材料组织和性能的影响。结果表明: 铝的加入并未使复合材料形成新相, 但可以促进烧结和Ti3SiC2相的形成; 随着铝含量的增多, 复合材料的致密度一直降低, 而抗弯强度和硬度均呈先降低后上升再降低的趋势; 当铝的体积分数为6%时, 材料的相对密度为92.5%, 抗弯强度为400 MPa, 硬度为54 HRC。
组织
性能
Ti matrix composite
microstructure
property
Abstract
SiC particles reinforced Ti matrix composites were prepared using the hollow cathode plasma sintering. The effect of Al content on the microstructure and properties of the composites was investigated. The results show that no new phase formed in the composites after adding of Al, but could improve the sintering and the formation of Ti3SiC2 phase. With the increase of Al content, the density of the composites decreased, both the bending strength and hardness decreased firstly, then increased and finally decreased. When the Al content was 6vol%, the relative density, bending strength and hardness of the composites were about 92.5%, 400 MPa and 54 HRC.
中图分类号 TG146.2
所属栏目
基金项目
收稿日期 2010/9/30
修改稿日期 2011/5/13
网络出版日期
作者单位点击查看
备注陈丹丹(1986-), 女, 江苏淮安人, 硕士研究生。
引用该论文: CHEN Dan-dan,YAO Zheng-jun. Effect of Al Content on Microstructure and Property of SiC Particles Reinforced Ti Matrix Composites[J]. Materials for mechancial engineering, 2011, 35(10): 19～21
陈丹丹,姚正军. 铝含量对SiCp/Ti基复合材料组织与性能的影响[J]. 机械工程材料, 2011, 35(10): 19～21
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】毛小南,赵永庆,杨冠军.国外航空发动机用钛合金的发展现状[J].稀有金属快报,2007,26(5):1-7.
【2】于化顺.金属基复合材料及其制备技术[M].北京:化学工业出版社,2006.
【3】梅运旺,杨廷清,罗贤,等.SiC纤维增强Ti600复合材料界面研究[J].稀有金属材料与工程,2008,37(10):1839-1841.
【4】吕祥鸿,杨延清,马志军,等.SiC连续纤维增强Ti基复合材料界面反应扩散研究进展[J].稀有金属材料与工程,2006,35(1):164-167.
【5】SUN Zheng-ming,YANG Song-lan, HASHIMOTO H. Effect of Al on the synthesis of Ti3SiC2 by reactively sintering Ti-SiC-C powder mixtures[J]. Journal of Alloys and Compounds,2007,439:321-325.
【6】望军,刘颖,叶金文,等.Ti(C,N)基金属陶瓷抗弯强度的研究[J].硬质合金,2008,25(3):140-142.
【7】胡超杰.空心阴极烧结原位合成TiC/Ti基复合材料的工艺研究[D].南京:南京航空航天大学,2010.
【2】于化顺.金属基复合材料及其制备技术[M].北京:化学工业出版社,2006.
【3】梅运旺,杨廷清,罗贤,等.SiC纤维增强Ti600复合材料界面研究[J].稀有金属材料与工程,2008,37(10):1839-1841.
【4】吕祥鸿,杨延清,马志军,等.SiC连续纤维增强Ti基复合材料界面反应扩散研究进展[J].稀有金属材料与工程,2006,35(1):164-167.
【5】SUN Zheng-ming,YANG Song-lan, HASHIMOTO H. Effect of Al on the synthesis of Ti3SiC2 by reactively sintering Ti-SiC-C powder mixtures[J]. Journal of Alloys and Compounds,2007,439:321-325.
【6】望军,刘颖,叶金文,等.Ti(C,N)基金属陶瓷抗弯强度的研究[J].硬质合金,2008,25(3):140-142.
【7】胡超杰.空心阴极烧结原位合成TiC/Ti基复合材料的工艺研究[D].南京:南京航空航天大学,2010.
相关信息