控冷工艺对热轧TRIP钢组织和性能的影响
Effect of Cooling Process on Microstructure and Mechanical Properties of Hot Rolled TRIP Steels
摘 要
采用光学显微镜、X射线衍射仪和拉伸试验机等研究了轧后冷却工艺对热轧TRIP钢组织和性能的影响。结果表明: 弛豫时间对热轧TRIP钢组织影响较大, 随弛豫时间增加, 带状组织等级越来越高, 铁素体组织也略显粗大; 模拟卷取制备的热轧TRIP钢组织中残余奥氏体含量和残余奥氏体中碳含量均较高; 贝氏体区停留时间延长, 则屈服强度和伸长率增大, 但抗拉强度下降。
残余奥氏体
弛豫时间
显微组织
力学性能
hot rolled TRIP steel
retained austenite
relaxation time
microstructure
mechanical property
Abstract
The effects of cooling process after rolling on the microstructure and mechanical properties of hot rolled transformation-induced plasticity (TRIP) steels were investigated by means of optical microscopy, X-ray diffractometer, and tensile test machine. The results show that relaxation time had greater impact on the microstructure of hot rolled TRIP steels, the banded structure grade increased with relaxation time, at the same time, ferrite grain grew slightly. The hot rolled coiled TRIP steels had more retained austenite, as well as carbon content in retained austenite. The yield strength and elongation increased, tensile strength decreased with prolongating residence time in Bainite zone.
中图分类号 TG335.3
所属栏目
基金项目 “十一五”国家科技支撑计划项目(2006BAE03A06); 北京市科委重大项目(D07010300700701)
收稿日期 2010/11/1
修改稿日期 2011/5/9
网络出版日期
作者单位点击查看
备注高绪涛(1976-), 男, 辽宁鞍山人, 博士研究生。
引用该论文: GAO Xu-tao,ZHANG Ming-ming,ZHAO Ai-min,ZHAO Zheng-zhi,CHEN Yong. Effect of Cooling Process on Microstructure and Mechanical Properties of Hot Rolled TRIP Steels[J]. Materials for mechancial engineering, 2011, 35(11): 24～27
高绪涛,张明明,赵爱民,赵征志,陈永. 控冷工艺对热轧TRIP钢组织和性能的影响[J]. 机械工程材料, 2011, 35(11): 24～27
被引情况:
【1】宋进英,齐祥羽,陈连生,田亚强,郑小平,赵定国, "冷却工艺对热轧65Mn钢显微组织和力学性能的影响",机械工程材料 39, 92-95(2015)
【2】孙军,倪培相,邵诗波,于晓东,吕世杰, "48MnV非调质钢曲轴断裂的原因分析",机械工程材料 40, 107-110(2016)
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】唐代明.TRIP钢TMP和热处理过程中的组织演变[J]. 特殊钢,2007,28(2):36-38.
【2】马世良.金属X射线衍射学[M]. 西安:西北工业大学出版社,1987.
【3】方琪,孙伟,王丙兴,等.“分段冷却”工艺对C-Mn钢中板带状组织的影响[J]. 轧钢,2008,25(1):13-15.
【4】OHTSUKA H, UMEMOTO M, TAMURA I.Effect of holding after deformation on the subsequent γ→α transformation behavior in a HSLA steel[C]//THERMEC 88.Warrendale:TMS,1988:352-359.
【5】翁宇庆.超细晶钢-钢的组织细化理论与控制技术[M]. 北京:冶金工业出版社,2003.
【6】方鸿生.贝氏体相变[M]. 北京:科学出版社,1999.
【2】马世良.金属X射线衍射学[M]. 西安:西北工业大学出版社,1987.
【3】方琪,孙伟,王丙兴,等.“分段冷却”工艺对C-Mn钢中板带状组织的影响[J]. 轧钢,2008,25(1):13-15.
【4】OHTSUKA H, UMEMOTO M, TAMURA I.Effect of holding after deformation on the subsequent γ→α transformation behavior in a HSLA steel[C]//THERMEC 88.Warrendale:TMS,1988:352-359.
【5】翁宇庆.超细晶钢-钢的组织细化理论与控制技术[M]. 北京:冶金工业出版社,2003.
【6】方鸿生.贝氏体相变[M]. 北京:科学出版社,1999.
相关信息