石油储罐用含铜高强钢的组织与力学性能
Microstructure and Mechanical Properties of A Cu-Containing High-Strength Steel for Oil Storage Tank
摘 要
运用光学显微镜、扫描电镜、透射电镜、拉伸试验机和冲击试验机等对石油储罐用含铜高强钢的显微组织和力学性能进行了分析。结果表明: 该钢的组织由大量的针状铁素体构成, 呈板条亚结构, 且位错密度较高; 钢中含有大量的第二相析出物, 主要以(Nbx, Ti1－x)(Cy, N1-y)的形式存在; 经过650 ℃回火后, 铜以固溶态存在于基体中, 仅起到固溶强化作用; 该钢有较好的强度和韧性,可满足石油储罐用钢的要求。
铜
析出物
针状铁素体
高强钢
oil storage tank
copper
precipitate
acicular ferrite
high-strength steel
Abstract
The microstructure and mechanical properties of a Cu-containing high-strength steel for oil storage tank were investigated by using optical microscopy, scanning electron microscopy, transmission electron microscopy, tensile tester and impact tester. The results show that the microstructure of the steel consisted of large amount of acicular ferrite(AF). The AF had substructure of ferrite laths and high dislocation density. The second phase precipitates were mainly in the form of (Nbx, Ti1－x)(Cy,N1-y). After tempering at 650 ℃, the copper which solid solved completely in matrix played a role of solid solution strengthening. The steel had good strength and toughness, and could meet the specific requirement for oil storage tank.
中图分类号 TG335.3
所属栏目
基金项目 国家“十一五”科技支撑计划项目(2006BAE03A06)
收稿日期 2010/12/24
修改稿日期 2011/8/24
网络出版日期
作者单位点击查看
备注齐亮(1980-), 男, 黑龙江海伦人, 讲师, 博士研究生。
引用该论文: QI Liang,ZHAO Ai-min,ZHAO Zheng-zhi,WU Hui-bin,ZHAO Wen-long. Microstructure and Mechanical Properties of A Cu-Containing High-Strength Steel for Oil Storage Tank[J]. Materials for mechancial engineering, 2011, 35(12): 74～76
齐亮,赵爱民,赵征志,武会宾,赵文龙. 石油储罐用含铜高强钢的组织与力学性能[J]. 机械工程材料, 2011, 35(12): 74～76
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】章小浒,王正东,涂善东.原油储罐用钢的开发与应用最新进展[J]. 压力容器,2006,23(3):38-43.
【2】梁福鸿,丛津功,胡昕明.石油储罐用08MnNiVR钢板组织和性能研究[J]. 鞍钢技术,2009(5): 32-35.
【3】肖桂枝, 朱伏先, 邸洪双.610 MPa级大型石油储罐用高强度钢板的开发[J]. 钢铁研究学报,2008,20(11):55-58.
【4】方鸿生.贝氏体相变[M]. 北京:科学出版社,1999.
【5】SHIN S Y, HAN S Y, HWANG B,et al.Effects of Cu and B addition on microstructure and mechanical properties of high-strength bainitic steels[J]. Materials Science & Engineering A,2009,517:212-214.
【6】李广敏,颜慧成,仇圣桃.Cu在贝氏体钢铁素体中的比界面能及熟化速率计算[J]. 特殊钢,2009,29(5):16-18.
【7】雍岐龙.钢铁材料中的第二相[M]. 北京:冶金工业出版社,2006.
【2】梁福鸿,丛津功,胡昕明.石油储罐用08MnNiVR钢板组织和性能研究[J]. 鞍钢技术,2009(5): 32-35.
【3】肖桂枝, 朱伏先, 邸洪双.610 MPa级大型石油储罐用高强度钢板的开发[J]. 钢铁研究学报,2008,20(11):55-58.
【4】方鸿生.贝氏体相变[M]. 北京:科学出版社,1999.
【5】SHIN S Y, HAN S Y, HWANG B,et al.Effects of Cu and B addition on microstructure and mechanical properties of high-strength bainitic steels[J]. Materials Science & Engineering A,2009,517:212-214.
【6】李广敏,颜慧成,仇圣桃.Cu在贝氏体钢铁素体中的比界面能及熟化速率计算[J]. 特殊钢,2009,29(5):16-18.
【7】雍岐龙.钢铁材料中的第二相[M]. 北京:冶金工业出版社,2006.
相关信息