常用典型齿轮钢渗碳层的组织与性能
Microstructure and Property of Carbonization Layer in Common and Typical Gear Steels
摘 要
通过对3种齿轮钢20CrNi2Mo、17CrNiMo6、20CrMnMo进行渗碳及热处理, 研究了不同渗碳时间后3种钢的表面碳含量及热处理前后的渗层硬度和组织。结果表明: 3种钢的合金系数从高到低依次为20CrMnMo钢、17CrNiMo6钢、20CrNi2Mo钢, 合金系数越大, 相同渗碳条件下表面碳含量越高; 高温回火前3种渗碳层的表面硬度均在45 HRC以上, 回火后均有所降低; 高温回火前渗碳层的组织为马氏体、残余奥氏体等非平衡态混合组织。
渗碳
热处理
gear steel
carburizing
heat treatment
Abstract
Three kinds of common and typical gear steels were carburized and heat treated, and the surface carbon contents of three kinds of steels after different carburizing times, and the hardness, microstructure of carbonization layers before and after heat treatment were studied. The results show that the alloy coefficients of three kinds steels were, from high to low, 20CrMnMo steel, 17CrNiMo6 steel and 20CrNiMo steel. The surface carbon contents increased with the increase of alloy coefficients under the same carbonization conditions. The surface hardness of three kinds of steels were all over 45 HRC before high-temperature tempering, and decreased after tempering. The microstructure before high-temperature were all nonequilibrium mixed microstructure of martensite and retained austenite.
中图分类号 TG156.8
所属栏目 试验研究
基金项目
收稿日期 2011/3/22
修改稿日期 2011/10/1
网络出版日期
作者单位点击查看
备注高金柱(1985-), 男, 吉林松原人, 博士研究生。
引用该论文: GAO Jin-zhu,GU Min,WANG Ai-xiang,XU Hong-xiang,ZHAO Shao-fu. Microstructure and Property of Carbonization Layer in Common and Typical Gear Steels[J]. Materials for mechancial engineering, 2012, 36(2): 49～51
高金柱,顾敏,王爱香,许鸿翔,赵少甫. 常用典型齿轮钢渗碳层的组织与性能[J]. 机械工程材料, 2012, 36(2): 49～51
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】陈国民.对我国齿轮渗碳淬火技术的评述[J].金属热处理, 2008, 33(1):25-33.
【2】孙广平, 杜之名, 刘长江, 等.大型齿轮渗碳时网状碳化物形成的原因及消除的方法[J].汽轮机技术, 2004:46(3):230-231.
【2】孙广平, 杜之名, 刘长江, 等.大型齿轮渗碳时网状碳化物形成的原因及消除的方法[J].汽轮机技术, 2004:46(3):230-231.
相关信息