等通道转角挤压对铬青铜腐蚀行为的影响
Effect of Equal Channel Angular Pressing on Corrrosion Behavior of Chromiun Bronze
摘 要
采用电化学测试和浸泡腐蚀试验研究了12道次等通道转角挤压(ECAP)处理前后铬青铜在氢氧化钠溶液中的腐蚀行为。结果表明: ECAP对铬青铜的自腐蚀电位有降低作用; 挤压后铬青铜在浸泡过程中的质量损失速率高于未进行挤压粗晶铬青铜的; ECAP并未从根本上改变其电化学腐蚀机制, 但却显著改变了其腐蚀形式, 未挤压铬青铜的腐蚀形式为沿晶腐蚀, 挤压后的腐蚀形式为均匀腐蚀。
铬青铜
电化学
浸泡试验
equal-channel angular pressing(ECAP)
chromium bronze
electrochemistry
immersion test
Abstract
Corrosion behaviors of chromium bronze in NaOH solution before and after equal channel angular pressing (ECAP) for 12 passes were studied by electrochemical and immersion corrosion tests. The results show that Ecorr value of chromiun bronze was decreased by ECAP. The mass loss ratio of ECAP treated chromium bronze during immersion was higher than that of untreated coarse-grain chromium bronze. The ECAP didn′t fundamentally change the electrochemical corrosion mechanism of chromiun bronze, but dramatically change the corrosion mode. For un-pressed and pressed chromium bronze, the corrosion mode of the former was intergranular corrosion, and that of the latter was uniform corrosion.
中图分类号 TH117.3
所属栏目 材料性能及其应用
基金项目 国家高技术研究发展计划资助项目(2002AA331110)
收稿日期 2011/2/10
修改稿日期 2011/9/10
网络出版日期
作者单位点击查看
备注张雅妮(1977-), 女, 陕西户县人, 讲师, 博士。
引用该论文: ZHANG Ya-ni,ZHANG Yong,LUO Jin-heng,HUANG Min. Effect of Equal Channel Angular Pressing on Corrrosion Behavior of Chromiun Bronze[J]. Materials for mechancial engineering, 2012, 36(3): 65～68
张雅妮,张勇,罗金恒,黄敏. 等通道转角挤压对铬青铜腐蚀行为的影响[J]. 机械工程材料, 2012, 36(3): 65～68
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】VINOGRADOV A, MIMAKI T, HASHIMOTO S, et al. On the corrosion behavior of ultra-frain copper[J].Scripta Mater,1999,41(3):319-326.
【2】ROFAGHA A, LANGER R, EL-SHERIK A M, et al. The corrosion behavior of nanocrystalline nickel[J].Scripta Metallurgica et Materialia,1991,25(12):2867-2872.
【3】ROFAGHA R, ERB U, OSTANDER D, et al. The effect of grain size and phosphorus on the corrosion of nanocrystalline Ni-P alloys[J].Nanostructured Materials,1993,2(1):1-10.
【4】THORPE S J, RAMASWAMI B, AUST A T. Corrosion and auger studies of nickel-base metal-metalloid glass[J].J Electrochem Soc,1988,135:2162-2174.
【2】ROFAGHA A, LANGER R, EL-SHERIK A M, et al. The corrosion behavior of nanocrystalline nickel[J].Scripta Metallurgica et Materialia,1991,25(12):2867-2872.
【3】ROFAGHA R, ERB U, OSTANDER D, et al. The effect of grain size and phosphorus on the corrosion of nanocrystalline Ni-P alloys[J].Nanostructured Materials,1993,2(1):1-10.
【4】THORPE S J, RAMASWAMI B, AUST A T. Corrosion and auger studies of nickel-base metal-metalloid glass[J].J Electrochem Soc,1988,135:2162-2174.
相关信息