经济节约型Q420D钢板的生产技术
Production Technology for Economical Q420D Steel Plate
摘 要
通过热机械控制工艺(TMCP)将普通Q345B钢板升级为Q420D钢板, 研究了不同热轧工艺下试验钢的显微组织和力学性能。结果表明: 试验钢的强韧性能均能满足GB/T 1591-2008的要求; 钢板1/4厚度处的组织比1/2厚度处的明显细化, 且采用开轧温度为780 ℃, 终轧温度为790 ℃的精轧工艺处理后, 试验钢的组织最为细小; 随着冲击试验温度的降低, 试验钢裂纹稳定扩展阶段的吸收能量和止裂吸收能量逐渐减小, 表现为冲击功降低。
大压下量
快速冷却
Q345B钢
Q420D钢
austenite unrecrystallized region heavy reduction
fast cooling
Q345B steel
Q420D steel
Abstract
The common Q345B steel plate was upgraded to Q420D steel plate by thermomechanical control process (TMCP). The microstructure and mechanical properties of the tested steel were studied by different heat rolling processes. The results show that the strength and toughness of the tested steels all could meet the requirement of GB/T 1591—2008. The microstructure at the quarter of thickness was significantly refiner than that at center of thickness. When the starting rolling temperature was 780 ℃ and the finishing rolling temperature was 790 ℃, the microstructure of the tested steel was finest. The absorbed energies for cracks stable extensive stage and for cracking preventing decreased gradually with the decrease of the impact test temperature, and the impact energy decreased.
中图分类号 TG335.5
所属栏目 试验研究
基金项目
收稿日期 2011/6/21
修改稿日期 2012/3/30
网络出版日期
作者单位点击查看
备注朱浩(1983-), 男, 江苏苏州人, 助理研究员, 硕士。
引用该论文: ZHU Hao,LUO Mi,LIU Dong-sheng. Production Technology for Economical Q420D Steel Plate[J]. Materials for mechancial engineering, 2012, 36(7): 25～27
朱浩,罗咪,刘东升. 经济节约型Q420D钢板的生产技术[J]. 机械工程材料, 2012, 36(7): 25～27
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】范建文, 左智宏, 谢瑞萍, 等. 345 MPa级表层超细晶普碳钢中厚板的工业试制[J]. 钢铁, 2008(7):59-63.
【2】HURLEY P J, HODGSON P D. Analysis and characterisation of ultra-fine ferrite produced during a new steel strip rolling process[J]. Scripta Materialia, 1999, 40(4):433-437.
【3】王根矶, 李婧, 何元春, 等.低合金厚板的减量化轧制[J]. 钢铁, 2009(8):60-63.
【4】冯光宏, 李岩, 戴蓓蓉, 等.在未再结晶区大压下后加速冷却工艺对钢板带状组织的影响[J]. 钢铁研究学报, 1999(6):14-17.
【5】王磊, 高彩茹, 王彦锋, 等.新型细晶强化Q420q宽厚板的研制[J]. 轧钢, 2008(2):3-6.
【6】朱伏先, 李艳梅, 刘彦春, 等.控轧控冷条件下Q345中厚板的生产工艺研究[J]. 钢铁, 2005(5):32-37.
【7】李婧, 赵德文, 刘相华, 等.结构用Q420E高强度厚板控轧控冷工艺研究[J]. 轧钢, 2008(6):8-11.
【8】邓伟, 高秀华, 秦小梅, 等.X80管线钢的冲击断裂行为[J]. 金属学报, 2010, 46(5):533-540.
【2】HURLEY P J, HODGSON P D. Analysis and characterisation of ultra-fine ferrite produced during a new steel strip rolling process[J]. Scripta Materialia, 1999, 40(4):433-437.
【3】王根矶, 李婧, 何元春, 等.低合金厚板的减量化轧制[J]. 钢铁, 2009(8):60-63.
【4】冯光宏, 李岩, 戴蓓蓉, 等.在未再结晶区大压下后加速冷却工艺对钢板带状组织的影响[J]. 钢铁研究学报, 1999(6):14-17.
【5】王磊, 高彩茹, 王彦锋, 等.新型细晶强化Q420q宽厚板的研制[J]. 轧钢, 2008(2):3-6.
【6】朱伏先, 李艳梅, 刘彦春, 等.控轧控冷条件下Q345中厚板的生产工艺研究[J]. 钢铁, 2005(5):32-37.
【7】李婧, 赵德文, 刘相华, 等.结构用Q420E高强度厚板控轧控冷工艺研究[J]. 轧钢, 2008(6):8-11.
【8】邓伟, 高秀华, 秦小梅, 等.X80管线钢的冲击断裂行为[J]. 金属学报, 2010, 46(5):533-540.
相关信息