基体炭对炭/炭复合材料摩擦磨损性能的影响
Effect of Matrix Carbon on Friction and Wear Property of Carbon/Carbon Composite
摘 要
采用液相浸渍-炭化法制备了沥青基炭/炭复合材料(P-C/C)和沥青-酚醛树脂双基体炭/炭复合材料(D-C/C), 研究了它们的增密效率、抗弯强度和摩擦磨损性能的差别。结果表明: P-C/C的增密效率高于D-C/C的; 在体积密度基本相同的情况下, 两种复合材料的抗弯强度相近; D-C/C的摩擦因数较大, 磨损较严重; 基体炭结构和性能的差别是造成两种复合材料摩擦磨损性能不同的主要原因。
基体炭
酚醛树脂
煤沥青
摩擦磨损性能
carbon/carbon composite
matrix carbon
phenolic resin
coal-tar pitch
friction and wear property
Abstract
Pitch-matrix carbon/carbon composites(P-C/C) and pitch & phenolic resin matrix carbon/carbon composites (D-C/C) were prepared using liquid impregnation/carbonization method. Densification efficiency, flexural strength and friction and wear properties of two kinds of carbon/carbon composites were studied. The results show that P-C/C exhibited higher densification efficiency than D-C/C. When the volume densities of the two kinds of carbon/carbon composites were the same, no apparent difference was shown in flexural strength. D-C/C showed a higher friction coefficient and fairly serious wear. The difference of structures and properties of matrix carbon caused different friction and wear properties of these two kinds of carbon/carbon composites mainly.
中图分类号 TB332
所属栏目 试验研究
基金项目 国家“973”计划资助项目(2011CB605804)
收稿日期 2011/8/28
修改稿日期 2012/5/10
网络出版日期
作者单位点击查看
备注胡聪聪(1985-), 男, 河南漯河人, 硕士研究生。
引用该论文: HU Cong-cong,LIU Hong-bo,XIAO Shao-yi,SHAO Nan-zi. Effect of Matrix Carbon on Friction and Wear Property of Carbon/Carbon Composite[J]. Materials for mechancial engineering, 2012, 36(8): 14～17
胡聪聪,刘洪波,肖绍懿,邵南子. 基体炭对炭/炭复合材料摩擦磨损性能的影响[J]. 机械工程材料, 2012, 36(8): 14～17
被引情况:
【1】宋联美,张永振,上官宝,赵彦文, "碳/碳复合材料的载流摩擦磨损性能及机理",机械工程材料 38, 76-80(2014)
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】李贺军, 曾燮榕, 李克智, 等.我国炭/炭复合材料研究进展[J].炭素, 2001 (4):8-13.
【2】FITZER E.Future of carbon-carbon composites[J].Carbon, 1987, 25(2) :163-190.
【3】LIN T.Mechanical behavior of two-dimentional carbon/carbon composites with interfacial carbon layers[J].Carbon, 1993, 37(12):2011-2019.
【4】NEUMEISTER J, JANSSON S, LECKIE F. The effect of fiber architecture on the mechanical properties of carbon/carbon composites[J]. Acta Mater, 1996, 44(2): 573-585.
【5】易茂中, 葛毅成, 冯一雷, 等.C/C复合材料及高强石墨在高温下的滑动摩擦磨损特性研究[J].摩擦学报, 2004, 24(3):235-239.
【6】易茂中, 葛毅成, 黄伯云, 等.润滑状态对C/C复合材料摩擦磨损特性的影响[J].中国有色金属学报, 2004, 14(8):1405-1409.
【7】FITZER E, MANOCHA L M. Carbon reinforcements and carbon/carbon composites[M]. Berlin Heidelberg: Springer-Verlag, 1998:104-105.
【8】周绍建, 苏君明, 苏哲安, 等.树脂炭含量对炭/炭复合材料性能的影响[J].新型炭材料, 2001, 16(1):49-52.
【9】陈腾飞, 龚伟平, 刘根山, 等.基体炭结构对炭／炭复合材料的界面结合强度的影响[J].矿业工程, 2004, 24(1):77-79.
【10】于 澍, 张红波, 熊翔, 等.炭/炭刹车副表面硬度对摩擦磨损性能的影响[J].功能材料, 2006, 37(9):1459-1462.
【11】YEN B K, ISHIHARA T.On temperature-dependent tribological regimes and oxidation of carbon-carbon composites up to 1800℃[J].Wear, 1996, 196(1/2):254-262.
【12】胡志彪, 李贺军, 陈强, 等.碳/碳复合材料摩擦学性能及摩擦机制研究进展[J].材料工程, 2004(12):59-62.
【2】FITZER E.Future of carbon-carbon composites[J].Carbon, 1987, 25(2) :163-190.
【3】LIN T.Mechanical behavior of two-dimentional carbon/carbon composites with interfacial carbon layers[J].Carbon, 1993, 37(12):2011-2019.
【4】NEUMEISTER J, JANSSON S, LECKIE F. The effect of fiber architecture on the mechanical properties of carbon/carbon composites[J]. Acta Mater, 1996, 44(2): 573-585.
【5】易茂中, 葛毅成, 冯一雷, 等.C/C复合材料及高强石墨在高温下的滑动摩擦磨损特性研究[J].摩擦学报, 2004, 24(3):235-239.
【6】易茂中, 葛毅成, 黄伯云, 等.润滑状态对C/C复合材料摩擦磨损特性的影响[J].中国有色金属学报, 2004, 14(8):1405-1409.
【7】FITZER E, MANOCHA L M. Carbon reinforcements and carbon/carbon composites[M]. Berlin Heidelberg: Springer-Verlag, 1998:104-105.
【8】周绍建, 苏君明, 苏哲安, 等.树脂炭含量对炭/炭复合材料性能的影响[J].新型炭材料, 2001, 16(1):49-52.
【9】陈腾飞, 龚伟平, 刘根山, 等.基体炭结构对炭／炭复合材料的界面结合强度的影响[J].矿业工程, 2004, 24(1):77-79.
【10】于 澍, 张红波, 熊翔, 等.炭/炭刹车副表面硬度对摩擦磨损性能的影响[J].功能材料, 2006, 37(9):1459-1462.
【11】YEN B K, ISHIHARA T.On temperature-dependent tribological regimes and oxidation of carbon-carbon composites up to 1800℃[J].Wear, 1996, 196(1/2):254-262.
【12】胡志彪, 李贺军, 陈强, 等.碳/碳复合材料摩擦学性能及摩擦机制研究进展[J].材料工程, 2004(12):59-62.
相关信息