硫化锑含量对汽车摩擦材料摩擦学性能的影响
Effect of Antimony Sulfide Content on Tribology Properties of Automotive Friction Material
摘 要
通过调整摩擦材料基础配方中硫化锑的含量, 采用直接混合工艺制备出不同组分的摩擦材料; 对其进行了摩擦磨损试验, 并观察了磨损表面形貌, 分析了其磨损机制。结果表明: 硫化锑的加入对材料摩擦学性能有很明显的改善; 当硫化锑质量分数为4%时, 摩擦材料的摩擦因数稳定性、恢复性和磨损率都为最佳, 较基础配方其摩擦因数稳定性提高了10%, 350 ℃时高温的磨损率下降了22%; 其磨损机制从未加入硫化锑时的粘着磨损转变为轻微的磨粒磨损。
酚醛树脂
摩擦材料
摩擦学性能
antimony sulfide
phenolic resin
friction material
tribology property
Abstract
By changing the content of antimony sulfide(Sb2S3) based on the basic formula, the friction materials with different composite were prepared by directly mixed process. The friction and wear test were completed and wear morphology was observed, and the wear mechanism was analyzed. The results show that the tribology properties were obviously improved by antimony sulfide. When the content of antimony sulfide was 4wt%, the stability of friction coefficient, the property of recovery and the wear rate were the best. Compared with the basic formula, the stability of friction coefficient was increased by 10%, and the wear rate was decreased by 22% at 350 ℃. The wear mechanism changed from adhesive wear of without antimony sulfide to slight abrasion wear.
中图分类号 TH117.1
所属栏目 材料性能及其应用
基金项目 贵州大学自然科学青年科研基金资助项目[(2010)053];贵州省科学技术基金资助项目[(2012)2118]
收稿日期 2011/8/30
修改稿日期 2012/6/26
网络出版日期
作者单位点击查看
备注黄智(1989-), 男, 四川自贡人, 硕士研究生。
引用该论文: HUANG Zhi,DING Xu,ZHOU Yuan-kang,CAO Yang,NIE Hua-wei. Effect of Antimony Sulfide Content on Tribology Properties of Automotive Friction Material[J]. Materials for mechancial engineering, 2012, 36(9): 58～60
黄智,丁旭,周元康,曹阳,聂华伟. 硫化锑含量对汽车摩擦材料摩擦学性能的影响[J]. 机械工程材料, 2012, 36(9): 58～60
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】HEE K W, FILIP P. Performance of ceramic enhanced phenolic matrix brake lining materials for automotive brake linings[J].Wear, 2005, 259(7/12): 1088-1096.
【2】鲁知音.汽车摩擦材料中填料的优化设计[D].贵阳: 贵州大学, 2007.
【3】高惠民.矿物复合摩擦材料[M].北京: 化学工业出版社, 2007.
【4】胡庆, 徐仁庆, 胡南秋.硫化锑在摩擦材料中的运用[C]//上海摩擦密封材料交流会论文集.北京: 中国摩擦密封材料协会, 2001.
【5】JANG H, KIM S J. The effects of antimony trisulfide(Sb2S3) and zirconium silicate(ZrSiO4) in the automotive bake friction material on friction characteristics[J].Wear, 2000, 239(2): 229-236.
【6】韩野, 田晓峰, 尹衍升.硅氧铝陶瓷纤维含量对半金属摩擦材料摩擦磨损性能的影响[J].摩擦学学报, 2008(1): 63-67.
【7】HABASHI F. Handbook of extractive metallurgy[M].Heidelberg, German: Wiley-VCH, 1997.
【8】杨永连. 烧结金属摩擦材料[J].机械工程材料, 1995, 19(6): 15-21.
【9】李双君. 金属硫化物陶瓷摩擦材料的制备与性能研究[D].武汉: 武汉理工大学, 2010.
【10】温诗铸, 黄平.摩擦学原理[M].北京: 清华大学出版社, 2008.
【2】鲁知音.汽车摩擦材料中填料的优化设计[D].贵阳: 贵州大学, 2007.
【3】高惠民.矿物复合摩擦材料[M].北京: 化学工业出版社, 2007.
【4】胡庆, 徐仁庆, 胡南秋.硫化锑在摩擦材料中的运用[C]//上海摩擦密封材料交流会论文集.北京: 中国摩擦密封材料协会, 2001.
【5】JANG H, KIM S J. The effects of antimony trisulfide(Sb2S3) and zirconium silicate(ZrSiO4) in the automotive bake friction material on friction characteristics[J].Wear, 2000, 239(2): 229-236.
【6】韩野, 田晓峰, 尹衍升.硅氧铝陶瓷纤维含量对半金属摩擦材料摩擦磨损性能的影响[J].摩擦学学报, 2008(1): 63-67.
【7】HABASHI F. Handbook of extractive metallurgy[M].Heidelberg, German: Wiley-VCH, 1997.
【8】杨永连. 烧结金属摩擦材料[J].机械工程材料, 1995, 19(6): 15-21.
【9】李双君. 金属硫化物陶瓷摩擦材料的制备与性能研究[D].武汉: 武汉理工大学, 2010.
【10】温诗铸, 黄平.摩擦学原理[M].北京: 清华大学出版社, 2008.
相关信息