时效处理对锻态QAl10-5-5铝青铜组织与性能的影响
Effects of Aging Treatment on Microstructure and Properties of Forged QAl10-5-5 Aluminum Bronze
摘 要
通过硬度测试、拉伸性能测试、X射线衍射分析和显微组织观察等方法研究了时效处理对锻态QAl10-5-5铝青铜组织和性能的影响。结果表明: 锻态QAl10-5-5铝青铜较好的时效处理工艺为650 ℃×2 h; 在此工艺下, 合金的硬度、抗拉强度、屈服强度、伸长率分别为212 HB, 769 MPa, 492 MPa和18.23%, 与锻态合金的相比分别提高了8.16%, 6.22%, 12.33%和13.94%; 经650 ℃×2 h时效后, 基体α相和(α+γ2)共析体组织分布均匀, 合金中均匀析出了较多细颗粒状的κ相并弥散分布。
时效处理
显微组织
性能
aluminum bronze
aging treatment
microstructure
properties
Abstract
Influences of aging treatment on microstructure and properties of forged QAl10-5-5 aluminum bronze were studied by hardness test, tensile test, X-ray diffraction analysis, microstructure observation. The results show that the aged QA110-5-5 aluminum bronze exhibited fairly good mechanical properties when aging condition was 650 ℃×2 h. Under this aging condition, the hardness, tensile strength, yield strength and elongation of the aged alloy were 212 HB, 769 MPa, 492 MPa and 18.23% respectively, which were improved by 8.16%, 6.22%, 12.33% and 13.94% respectively compared with those of the forged alloy, and more fine granular κ phase precipitated from alloy diffused well in the homogeneously distributed microstructure of matrix of α-phase and (α+γ2)eutectoid.
中图分类号 TG146.1
所属栏目 材料性能及其应用
基金项目
收稿日期 2011/8/31
修改稿日期 2012/4/30
网络出版日期
作者单位点击查看
备注龚习(1986-), 男, 湖北黄冈人, 硕士研究生。
引用该论文: GONG Xi,SONG Lian-peng,HU Jian,WANG Xing. Effects of Aging Treatment on Microstructure and Properties of Forged QAl10-5-5 Aluminum Bronze[J]. Materials for mechancial engineering, 2012, 36(9): 73～77
龚习,宋练鹏,胡健,王星. 时效处理对锻态QAl10-5-5铝青铜组织与性能的影响[J]. 机械工程材料, 2012, 36(9): 73～77
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】周志明, 谷成渝, 牟飞, 等.高强度铝青铜合金的研究进展[J] .热加工工艺, 2010, 39(11): 41-44.
【2】ZHANG W W, XIA W, WEI L P, et al. Mechanical properties and tribological behavior of a cast heat-resisting copper based alloy[J].Journal of Center South University of Technology, 2002, 9(4): 235-239.
【3】张大童, 陈瑞平, 罗宗强, 等.热处理温度对高强变形铝青铜的组织和力学性能的影响[J] .稀有金属, 2010, 34(4): 521-525.
【4】钟卫佳, 马可定, 吴维治, 等.铜加工技术实用手册[M].北京: 冶金工业出版社, 2007.
【5】何勇.QAl10-5-5铝青铜热处理工艺的研究[J].国外金属热处理, 2005, 26(2): 12-15.
【6】ZHANG W W, NGAI T L, XIA W, et al. Influence of heat treatment on tribological behaviors of novel wrought aluminum bronze[J].Trans Nonferrous Met Soc China, 2002, 12(4): 770-774.
【7】王祝堂, 田荣璋.铜合金及其加工手册[M].长沙: 中南大学出版社, 2007.
【8】宋练鹏, 尹志民, 冯然, 等.热处理对Cu-Al-Fe-Ni-Cr-Re合金组织和性能的影响[J].电力机车技术, 2002, 25(4): 10-12.
【9】BREZINA P. Heat treatment of complex aluminum bronzes [J].International Metals Reviews, 1982, 27(2): 77-120.
【10】徐国富.高速列车异步牵引电动机转子铜合金护环的研制[D].长沙: 中南大学, 2000.
【11】王荣滨.铝青铜热处理强化工艺试验研究[J].技术与工艺, 2006(5): 35-37.
【12】重有色金属材料加工手册编写组. 重有色金属材料加工手册, 第1分册[M].北京: 冶金工业出版社, 1980: 174-196.
【13】刘淑云. 铜及铜合金热处理[M].北京: 机械工业出版社, 1990: 94.
【2】ZHANG W W, XIA W, WEI L P, et al. Mechanical properties and tribological behavior of a cast heat-resisting copper based alloy[J].Journal of Center South University of Technology, 2002, 9(4): 235-239.
【3】张大童, 陈瑞平, 罗宗强, 等.热处理温度对高强变形铝青铜的组织和力学性能的影响[J] .稀有金属, 2010, 34(4): 521-525.
【4】钟卫佳, 马可定, 吴维治, 等.铜加工技术实用手册[M].北京: 冶金工业出版社, 2007.
【5】何勇.QAl10-5-5铝青铜热处理工艺的研究[J].国外金属热处理, 2005, 26(2): 12-15.
【6】ZHANG W W, NGAI T L, XIA W, et al. Influence of heat treatment on tribological behaviors of novel wrought aluminum bronze[J].Trans Nonferrous Met Soc China, 2002, 12(4): 770-774.
【7】王祝堂, 田荣璋.铜合金及其加工手册[M].长沙: 中南大学出版社, 2007.
【8】宋练鹏, 尹志民, 冯然, 等.热处理对Cu-Al-Fe-Ni-Cr-Re合金组织和性能的影响[J].电力机车技术, 2002, 25(4): 10-12.
【9】BREZINA P. Heat treatment of complex aluminum bronzes [J].International Metals Reviews, 1982, 27(2): 77-120.
【10】徐国富.高速列车异步牵引电动机转子铜合金护环的研制[D].长沙: 中南大学, 2000.
【11】王荣滨.铝青铜热处理强化工艺试验研究[J].技术与工艺, 2006(5): 35-37.
【12】重有色金属材料加工手册编写组. 重有色金属材料加工手册, 第1分册[M].北京: 冶金工业出版社, 1980: 174-196.
【13】刘淑云. 铜及铜合金热处理[M].北京: 机械工业出版社, 1990: 94.
相关信息