明胶凝胶注模成型不锈钢浆料的制备与生坯的性能
Preparation of Stainless Powder Slurry through Gelcasting of Gelatin and Properties of Green Body
摘 要
选用316L不锈钢粉为原料、海藻酸钠为分散剂、明胶为粘结剂, 研究了固相、分散剂和粘结剂含量对浆料的流动性以及凝胶注模成型生坯抗弯强度的影响。结果表明: 当pH值为7、固相体积分数为56%、分散剂质量分数为1.0%、粘结剂质量分数为0.8%时, 浆料的黏度小于1 000 MPa·s, 按此工艺参数制备的生坯在室温下干燥后, 其抗弯强度可达到3.6 MPa。
浆料
流动性
生坯
抗弯强度
gelatin
slurry
fluidity
green body
bending strength
Abstract
The slurry was prepared by using 316L stainless steel powders as raw material, sodium alginate as dispersant and gelatin as agglomerant, the effects of solid content, dispersant content and agglomerant content on fluidity of the slurry and bending strength of the gelcasted green body were studied. Results show that the viscosity of slurry was smaller than 1 000 MPa·s when pH value of slurry was 7, solid content ratio was 56 vol%, dispersant ratio was 1.0 wt%, agglomerant ratio was 0.8 wt%, and the bending strength of the green body prepared according to above parameters could reach 3.6 MPa after being dried at room temperature.
中图分类号 TF12
所属栏目 材料性能及其应用
基金项目 国家自然科学基金资助项目(50975100); 厦门科技计划资助项目(3502Z20113020); 华侨大学科研启动费资助项目(11Y0265)
收稿日期 2011/10/17
修改稿日期 2012/7/21
网络出版日期
作者单位点击查看
备注赵席鹏(1984-), 男, 山东菏泽人, 硕士研究生。
引用该论文: ZHAO Xi-peng,JIANG Kai-yong,WANG Fei. Preparation of Stainless Powder Slurry through Gelcasting of Gelatin and Properties of Green Body[J]. Materials for mechancial engineering, 2012, 36(12): 58～61
赵席鹏,江开勇,王霏. 明胶凝胶注模成型不锈钢浆料的制备与生坯的性能[J]. 机械工程材料, 2012, 36(12): 58～61
被引情况:
【1】黄丽,赵莹莹,王卫敏,唐睿,史忠旗,王继平, "中间相炭微球为碳源制备炭材料的凝胶注模成型工艺",机械工程材料 39, 54-59(2015)
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】OMATETE O O, JANNEY M A, STREHLOW R A. Gelcasting: a new ceramic forming process[J].Am Ceram Soc Bull,1991,70(10):1641-1649.
【2】宴伯武.凝胶注模成形工艺的研究[J].中国陶瓷,2006,42(2):8-11.
【3】AKHONDI H, TAHERI-NASSAJ E, SARPOOLAKY H, et al. Gelcasting of alumina nanopowders based on gelation of sodium alginat[J].Ceramics International,2009,35(3):1033-1037.
【4】张建伟,江开勇,王霏.凝胶注模成型用316L不锈钢浆料的制备[J].机械工程材料,2009,33(10):86-89.
【5】胡正水,邓斌.果胶大分子在陶瓷凝胶注模成型工艺中的应用研究[J].材料导报,2000,10(14):54-57.
【6】谢志鹏,黄勇,陈亚丽,等.酶催化明胶原位凝固成型陶瓷坯体的研究[J].硅酸盐学报,1999,27(5):527-532.
【7】宋贤良.利用淀粉原位凝固胶态成型高性能陶瓷的研究[D].广州: 华南理工大学,2003.
【8】TARI G. Gelcasting ceramics: a review[J].Am Ceram Bull,2003,82(4):43-48.
【9】BARTULI C, BEMPORAD E, TULLIANI J M, et al. Mechanical properties of cellular ceramics obtained by gel casting: Characterization and modeling[J].Journal of the European Ceramic Society,2009,29(14):2979-2989.
【10】HIROTA K, SUGIMOTO M, KATO M, et al. Preparation of zinc oxide ceramics with a sustainable antibacterial activity under dark conditions[J].Ceramics International,2010,36(2):497-506.
【11】李艳,郭志猛,郝俊杰,等.金属粉末凝胶注模成形技术的研究现状及应用前景[J].粉末冶金工业,2006,16(5):34-37.
【12】果世驹,杨霞,陈邦峰,等.粉末316L不锈钢的高密度强化烧结[J].机械工程材料,2004,28(7):7-11.
【13】WANG F, JIANG K Y, XU X P. Gel casting of 316L stainless steel powder through mold dIS Process[J].Tsinghua Science and Technology,2009,14(S1):216-222.
【14】谢灼利,孙宏伟,郑冲.α-Al2O3稳定浆料的研究[J].无机材料学报,1998,13(6):818-822.
【15】刘卫华,贾成厂,史延涛.高碳钢凝胶注模成形工艺[J].北京科技大学学报,2006,28(4):361-364.
【16】刘卫华,贾成厂,郭志猛.铁基粉末凝胶注模成形工艺的研究[J].粉末冶金工业,2006,16(1):8-10.
【2】宴伯武.凝胶注模成形工艺的研究[J].中国陶瓷,2006,42(2):8-11.
【3】AKHONDI H, TAHERI-NASSAJ E, SARPOOLAKY H, et al. Gelcasting of alumina nanopowders based on gelation of sodium alginat[J].Ceramics International,2009,35(3):1033-1037.
【4】张建伟,江开勇,王霏.凝胶注模成型用316L不锈钢浆料的制备[J].机械工程材料,2009,33(10):86-89.
【5】胡正水,邓斌.果胶大分子在陶瓷凝胶注模成型工艺中的应用研究[J].材料导报,2000,10(14):54-57.
【6】谢志鹏,黄勇,陈亚丽,等.酶催化明胶原位凝固成型陶瓷坯体的研究[J].硅酸盐学报,1999,27(5):527-532.
【7】宋贤良.利用淀粉原位凝固胶态成型高性能陶瓷的研究[D].广州: 华南理工大学,2003.
【8】TARI G. Gelcasting ceramics: a review[J].Am Ceram Bull,2003,82(4):43-48.
【9】BARTULI C, BEMPORAD E, TULLIANI J M, et al. Mechanical properties of cellular ceramics obtained by gel casting: Characterization and modeling[J].Journal of the European Ceramic Society,2009,29(14):2979-2989.
【10】HIROTA K, SUGIMOTO M, KATO M, et al. Preparation of zinc oxide ceramics with a sustainable antibacterial activity under dark conditions[J].Ceramics International,2010,36(2):497-506.
【11】李艳,郭志猛,郝俊杰,等.金属粉末凝胶注模成形技术的研究现状及应用前景[J].粉末冶金工业,2006,16(5):34-37.
【12】果世驹,杨霞,陈邦峰,等.粉末316L不锈钢的高密度强化烧结[J].机械工程材料,2004,28(7):7-11.
【13】WANG F, JIANG K Y, XU X P. Gel casting of 316L stainless steel powder through mold dIS Process[J].Tsinghua Science and Technology,2009,14(S1):216-222.
【14】谢灼利,孙宏伟,郑冲.α-Al2O3稳定浆料的研究[J].无机材料学报,1998,13(6):818-822.
【15】刘卫华,贾成厂,史延涛.高碳钢凝胶注模成形工艺[J].北京科技大学学报,2006,28(4):361-364.
【16】刘卫华,贾成厂,郭志猛.铁基粉末凝胶注模成形工艺的研究[J].粉末冶金工业,2006,16(1):8-10.
相关信息