High Temperature Property Comparison for Two New Hot Work Die Steels
摘 要
利用光学显微镜、扫描电镜以及能谱仪并结合热稳定性试验, 对SDCM3和SDCM4热作模具钢在热稳定性试验前后的微观组织进行研究, 采用自约束热疲劳试验方法研究了两种钢的热疲劳性能。结果表明: 与SDCM4钢相比, SDCM3钢具有更优良的热稳定性和抗热疲劳性能。
Abstract
The microstructure of SDCM3 and SDCM4 steels before and after the thermal stability test was studied using optical microscopy, scanning electron microscopy and energy dispersive spectroscopy. A comparative study on the thermal fatigue preperty of SDCM3 and SDCM4 steels was performed by the self-restricting test method. The results show that SDCM3 steel had better thermal-stability and resistance to thermal fatigue compared with SDCM4 steel.
中图分类号 TG142
所属栏目 材料性能及其应用
基金项目 上海市重点学科建设项目(S30107); 国家博士点专项科研基金资助项目(2006028006)
收稿日期 2011/10/18
修改稿日期 2012/7/20
网络出版日期
作者单位点击查看
备注黎军顽(1980-), 男, 江西赣州人, 讲师, 博士。
引用该论文: LI Jun-wan,ZHOU Lu-hai,SHAO Yan,WU Xiao-chun. High Temperature Property Comparison for Two New Hot Work Die Steels[J]. Materials for mechancial engineering, 2012, 36(12): 67~72
黎军顽,周路海,邵严,吴晓春. 两种新型热作模具钢的高温性能对比[J]. 机械工程材料, 2012, 36(12): 67~72
共有人对该论文发表了看法,其中:
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】陈英伟, 吴晓春.热作模具钢1.2367的性能研究[J].上海金属, 2009, 31(6): 1-5.
【2】崔崑.国内外模具用钢发展概况[J].金属热处理, 2007, 32(1): 1-11.
【3】PERSSON A, HOGMARK S, BERGSTROM J. Simulation and evaluation of thermal fatigue cracking of hot work tool steels [J].International Journal of Fatigue, 2004,26:1095-1107.
【4】吴玉道, 王洁民.铝压铸模具失效分析[J].机械工程材料, 1989, 13(6): 49-51.
【5】LIERUAD H P, DIAS A, GIUSTI J. Experimental simulation and theoretical modeling of crack initiation and propagation due to thermal cycling [J].High Temperature Technology,1991,8(2):137-145.
【6】NORSTROM L A, SVENSSON M, OHRBERG V. Thermal fatigue behavior of hot work tool steels [J].Met Technology,1981,8(10):376-381.
【7】许珞萍, 吴晓春, 邵光杰, 等.4Cr5MoSiV1,8407钢的热疲劳性能[J].材料工程, 2001 (2): 3-7.
【8】徐晓.H13类钢的各向异性及其热疲劳损伤因子的研究[D].上海:上海大学, 2003.
【9】施雯, 刘以宽.QRO90 SUPREME热作模具钢的性能[J].金属热处理, 1997 (1): 25-28.
【10】王小军, 徐明纲, 陈秋龙, 等.热作模具钢QRO90与8407(H13)回火稳定性对比研究[J].上海金属, 1998, 20(2): 8-11.
【2】崔崑.国内外模具用钢发展概况[J].金属热处理, 2007, 32(1): 1-11.
【3】PERSSON A, HOGMARK S, BERGSTROM J. Simulation and evaluation of thermal fatigue cracking of hot work tool steels [J].International Journal of Fatigue, 2004,26:1095-1107.
【4】吴玉道, 王洁民.铝压铸模具失效分析[J].机械工程材料, 1989, 13(6): 49-51.
【5】LIERUAD H P, DIAS A, GIUSTI J. Experimental simulation and theoretical modeling of crack initiation and propagation due to thermal cycling [J].High Temperature Technology,1991,8(2):137-145.
【6】NORSTROM L A, SVENSSON M, OHRBERG V. Thermal fatigue behavior of hot work tool steels [J].Met Technology,1981,8(10):376-381.
【7】许珞萍, 吴晓春, 邵光杰, 等.4Cr5MoSiV1,8407钢的热疲劳性能[J].材料工程, 2001 (2): 3-7.
【8】徐晓.H13类钢的各向异性及其热疲劳损伤因子的研究[D].上海:上海大学, 2003.
【9】施雯, 刘以宽.QRO90 SUPREME热作模具钢的性能[J].金属热处理, 1997 (1): 25-28.
【10】王小军, 徐明纲, 陈秋龙, 等.热作模具钢QRO90与8407(H13)回火稳定性对比研究[J].上海金属, 1998, 20(2): 8-11.
相关信息