304L无缝钢管二辊斜轧穿孔裂纹的形成原因
Causes of Crack Formation in 304L Seamless Steel Pipe during Double-Roll Cross Piercing Process
摘 要
采用光学显微镜、热力学计算软件、扫描电镜等分析了304L无缝钢管二辊斜轧穿孔工艺中荒管内部产生裂纹的原因。结果表明: 穿孔用钢坯中存在3%左右(体积分数)的δ铁素体相, 穿孔工艺中不均匀变形是裂纹产生的主要原因; 由于δ相和γ相变形能力不一致, 在两相界面上产生超过金属断裂强度的拉应力和切应力则促进了裂纹的形成与扩展。
穿孔
裂纹
δ铁素体
304L seamless steel pipe
piercing
cracks
δ ferrite
Abstract
The mechanism of cracking in 304L seamless steel pipe during double-roll cross piercing processing was analyzed by optical microscopy, thermal-calculation ulation software and scanning electron microscopy. The results show that about 3 vol.% δ ferrite phase in the billet and the heterogenous deformation of billet during the piercing process were the main causes of cracking. In addition, the difference of deformability between δ ferrite phase and γ phase caused both the tensile stress and the shear stress at the interface of two phases higher than the fracture strength of billet, which promoted the formation and growth of the cracks.
中图分类号 TG142.71
所属栏目 试验研究
基金项目
收稿日期 2011/11/17
修改稿日期 2012/8/20
网络出版日期
作者单位点击查看
备注王宝顺(1982—), 男, 江西吉安人, 工程师, 博士。
引用该论文: WANG Bao-shun,SHAO Yu,LI San,ZHAO Fang-xin,SHEN Hong-ying,ZHU Xin-qiang. Causes of Crack Formation in 304L Seamless Steel Pipe during Double-Roll Cross Piercing Process[J]. Materials for mechancial engineering, 2013, 37(1): 14～17
王宝顺,邵羽,李三,赵芳馨,沈红英,朱新强. 304L无缝钢管二辊斜轧穿孔裂纹的形成原因[J]. 机械工程材料, 2013, 37(1): 14～17
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】邹子和.我国不锈钢管生产技术的进展及其与国外的差距[J].钢管, 2000, 29(6): 7-14.
【2】田党.高温合金无缝管材的研制与生产[J].钢管, 2002, 31(3): 1-6.
【3】陈洪琪, 李群.大直径不锈钢管坯的穿孔试验[J].钢管, 2000, 29(4): 9-10.
【4】詹才俊, 杜志扬.厚壁毛管穿孔产生内裂和夹层的原因分析[J].钢管, 1995, 24(2): 28-31.
【5】张存信, 冯晓庭, 项炳和, 等.不锈钢无缝管加工过程中断裂原因简析[J].钢管, 2008, 37(3): 38-42.
【6】王偕蓉.00Cr17Ni14Mo2超低碳不锈钢热穿孔管裂纹缺陷分析[J].四川冶金, 1989, 39(3): 83-88.
【7】柳谋渊, 陆昕.00Cr17Ni12Mo2不锈钢管热轧层裂的研究[J].热加工工艺, 2010, 39(17): 178-180.
【8】李丹, 李冬升, 戴起勋.超超临界火电用Super304H不锈钢管的组织分析[J].金属热处理, 2010, 35(5): 93-95.
【9】郭元蓉, 陈雨, 詹勇, 等.P91热轧无缝钢管中铁素体的研究[J].钢管, 2011, 40(5): 17-20.
【10】卢玉逑, 王先进.二辊斜轧穿孔时圆坯断面的变形分布和发展[J].金属学报, 1980, 16(4): 470-479.
【11】田党.关于难变形钢和合金管坯的二辊斜轧穿孔问题[J].钢铁, 1998, 33(1): 33-36.
【12】田党, 张根良, 玉钦.二辊斜轧穿孔时高合金钢圆坯的变形分布及分层形成机制[J].钢铁, 1995, 30(1): 40-46.
【13】李胜祗, 陈大宏, 孙中建, 等.二辊斜轧穿孔时圆管坯的变形与应力分布及其发展[J].钢铁研究学报, 2000, 12(5): 26-30.
【14】VENUGOPAL S, MANNAN S L, PRASAD Y V R K. Optimization of hot workability in stainless steel type 304L using processing maps[J]. Metallurgical Transactions A, 1992, 23(11): 3093-3103.
【2】田党.高温合金无缝管材的研制与生产[J].钢管, 2002, 31(3): 1-6.
【3】陈洪琪, 李群.大直径不锈钢管坯的穿孔试验[J].钢管, 2000, 29(4): 9-10.
【4】詹才俊, 杜志扬.厚壁毛管穿孔产生内裂和夹层的原因分析[J].钢管, 1995, 24(2): 28-31.
【5】张存信, 冯晓庭, 项炳和, 等.不锈钢无缝管加工过程中断裂原因简析[J].钢管, 2008, 37(3): 38-42.
【6】王偕蓉.00Cr17Ni14Mo2超低碳不锈钢热穿孔管裂纹缺陷分析[J].四川冶金, 1989, 39(3): 83-88.
【7】柳谋渊, 陆昕.00Cr17Ni12Mo2不锈钢管热轧层裂的研究[J].热加工工艺, 2010, 39(17): 178-180.
【8】李丹, 李冬升, 戴起勋.超超临界火电用Super304H不锈钢管的组织分析[J].金属热处理, 2010, 35(5): 93-95.
【9】郭元蓉, 陈雨, 詹勇, 等.P91热轧无缝钢管中铁素体的研究[J].钢管, 2011, 40(5): 17-20.
【10】卢玉逑, 王先进.二辊斜轧穿孔时圆坯断面的变形分布和发展[J].金属学报, 1980, 16(4): 470-479.
【11】田党.关于难变形钢和合金管坯的二辊斜轧穿孔问题[J].钢铁, 1998, 33(1): 33-36.
【12】田党, 张根良, 玉钦.二辊斜轧穿孔时高合金钢圆坯的变形分布及分层形成机制[J].钢铁, 1995, 30(1): 40-46.
【13】李胜祗, 陈大宏, 孙中建, 等.二辊斜轧穿孔时圆管坯的变形与应力分布及其发展[J].钢铁研究学报, 2000, 12(5): 26-30.
【14】VENUGOPAL S, MANNAN S L, PRASAD Y V R K. Optimization of hot workability in stainless steel type 304L using processing maps[J]. Metallurgical Transactions A, 1992, 23(11): 3093-3103.
相关信息