油轮辅锅炉过热器爆管的原因
Burst Causes for Superheater Tube of a Tank Auxiliary Boiler
摘 要
对某油轮爆裂的辅锅炉过热器管进行了成分分析、力学性能测试和显微组织观察, 以找出其爆管的原因。结果表明: 因锅炉长期超温运行, 致使钢管基体组织珠光体球化、并产生严重的蠕变损伤; 管内壁存在的结垢层加剧了过热器管的过热并促进其爆裂。
过热器管
爆管
珠光体球化
蠕变
boiler
superheater tube
bursted tube
pearlite spheroidization
creep
Abstract
The chemical composition analysis, mechanical properties testing and microstructure observing were done for a burst superheater tube in a tank auxiliary boiler to find burst causes. The results show that pearlite spheroidization and serious creep damage happened in the tube matrix due to a long time superheating, and the deposit on inner-wall of the superheater tube made superheat aggravate and promote burst.
中图分类号 TK223.3
所属栏目 物理模拟与数值模拟
基金项目 财政部科技部(财教[2009]365号)科技人员服务企业行动项目; 福建省自然科学基金资助项目(2012J01228)
收稿日期 2011/12/25
修改稿日期 2012/9/12
网络出版日期
作者单位点击查看
备注戴乐阳(1972-), 男, 江西乐安人, 副教授, 博士。
引用该论文: DAI Le-yang,LI Jing-hong. Burst Causes for Superheater Tube of a Tank Auxiliary Boiler[J]. Materials for mechancial engineering, 2013, 37(1): 101～104
戴乐阳,李经宏. 油轮辅锅炉过热器爆管的原因[J]. 机械工程材料, 2013, 37(1): 101～104
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】周顺深.炉管珠光体球化与破裂寿命的关系[J].华东电力, 1995(5): 7-11.
【2】杨瑞成, 王晖, 郑丽平, 等.12Cr1MoV钢高温时效过程中组织结构的演变[J].金属热处理, 2002, 27(9): 18-22.
【2】杨瑞成, 王晖, 郑丽平, 等.12Cr1MoV钢高温时效过程中组织结构的演变[J].金属热处理, 2002, 27(9): 18-22.
相关信息