Effect of Welding Rates on Friction Stir Welded Joint Shaping and Microstructure of AZ80 Magnesium Alloy
摘 要
采用搅拌摩擦焊工艺对AZ80镁合金进行焊接, 在其它工艺参数不变的条件下, 研究了焊接速度对接头成形及组织的影响。结果表明: 在搅拌头旋转速度为1 000 r·min-1、焊接速度为150 mm·min-1时可获得表面无缺陷、内部无孔洞的致密焊缝; 焊速越大, 焊核区前进侧中部组织中的动态再结晶晶粒越细小, 焊速对热机影响区和热影响区组织的影响基本相同。
Abstract
Friction stir welding was adopted to weld AZ80 magnesium alloy, the effects of welding rates on friction stir welding joint shaping and microstructure were studied under the condition of other parameters unchanging.The results show that the good surface quality and compact weld seam were obtained when the rotation rate was 1 000 r·min-1 and the welding rate was 150 mm·min-1. The dynamic recrystallization grains in the medium of advancing side of nugget zone decreased with the increase of welding rate, and the effect of welding rate on microstructure of thermo-chemical affected zone and heat affected zone was no difference.
中图分类号 TG453
所属栏目 试验研究
基金项目
收稿日期 2012/6/20
修改稿日期 2013/2/13
网络出版日期
作者单位点击查看
备注李铁龙(1974-), 男, 山西稷山人, 讲师, 博士研究生。
引用该论文: LI Tie-long,YANG Xin-qi,WANG Zhen-shan. Effect of Welding Rates on Friction Stir Welded Joint Shaping and Microstructure of AZ80 Magnesium Alloy[J]. Materials for mechancial engineering, 2013, 37(5): 26~29
李铁龙,杨新岐,王振山. 焊速对AZ80镁合金搅拌摩擦焊接头成形及组织的影响[J]. 机械工程材料, 2013, 37(5): 26~29
被引情况:
【1】赵亚东,张运真,何强, "6061-T6铝合金搅拌摩擦焊接头的组织和性能",机械工程材料 38, 93-96(2014)
【2】徐学利,王纯,侯军才,张超, "ZK60镁合金的炉中钎焊工艺",机械工程材料 39, 35-38(2015)
【3】宁朝阳,任成高, "6061-T6铝合金超声辅助搅拌摩擦焊接头的组织与力学性能",机械工程材料 39, 61-64(2015)
共有人对该论文发表了看法,其中:
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】徐河, 刘静安, 谢水生, 等.镁合金制备与加工技术[M].北京: 冶金工业出版社, 2007: 1-98.
【2】马春生, 张治民, 郭玉明.汽车镁合金轮毂等温挤旋成型工艺优化与试验[J].农业机械学报, 2012, 43(3): 223-229.
【3】杨素媛, 张保垒.厚板AZ31镁合金搅拌摩擦焊焊接接头的组织与性能[J].焊接学报, 2009, 30(5): 1-4.
【4】FORCELLESE A, GABRIELLI F, SIMONCINI M. Mechanical properties and microstructure of joints in AZ31 thin sheets obtained by friction stir welding using "pin" and "pinless" tool configurations[J].Materials & Design, 2012, 34: 219-229.
【5】AFRIN N, CHEN D L, CAO X, et al. Microstructure and tensile properties of friction stir welded AZ31B magnesium alloy[J].Materials Science and Engineering A, 2008, 472(1/2): 179-186.
【6】LIN Y C, LIU J J, LIN B Y, et al. Effects of process parameters on strength of Mg alloy AZ61 friction stir spot welds[J].Materials & Design, 2012, 35: 350-357.
【7】RAZAL ROSE A, MANISEKAR K, BALASUBRAMANIAN V. Effect of axial force on microstructure and tensile properties of friction stir welded AZ61A magnesium alloy[J].Transactions of Nonferrous Metals Society of China, 2011, 21(5): 974-984.
【8】徐卫平, 邢丽, 柯黎明, 等.镁合金搅拌摩擦焊接头晶粒取向和织构分析[J].材料科学与工艺, 2005, 13(3): 254-257.
【9】LIU D, NISHIO H, NAKATA K. Anisotrop ic property of material arrangement in friction stir welding of dissimilar Mg alloys[J].Materials & Design, 2011, 32(10): 4818- 4824 .
【2】马春生, 张治民, 郭玉明.汽车镁合金轮毂等温挤旋成型工艺优化与试验[J].农业机械学报, 2012, 43(3): 223-229.
【3】杨素媛, 张保垒.厚板AZ31镁合金搅拌摩擦焊焊接接头的组织与性能[J].焊接学报, 2009, 30(5): 1-4.
【4】FORCELLESE A, GABRIELLI F, SIMONCINI M. Mechanical properties and microstructure of joints in AZ31 thin sheets obtained by friction stir welding using "pin" and "pinless" tool configurations[J].Materials & Design, 2012, 34: 219-229.
【5】AFRIN N, CHEN D L, CAO X, et al. Microstructure and tensile properties of friction stir welded AZ31B magnesium alloy[J].Materials Science and Engineering A, 2008, 472(1/2): 179-186.
【6】LIN Y C, LIU J J, LIN B Y, et al. Effects of process parameters on strength of Mg alloy AZ61 friction stir spot welds[J].Materials & Design, 2012, 35: 350-357.
【7】RAZAL ROSE A, MANISEKAR K, BALASUBRAMANIAN V. Effect of axial force on microstructure and tensile properties of friction stir welded AZ61A magnesium alloy[J].Transactions of Nonferrous Metals Society of China, 2011, 21(5): 974-984.
【8】徐卫平, 邢丽, 柯黎明, 等.镁合金搅拌摩擦焊接头晶粒取向和织构分析[J].材料科学与工艺, 2005, 13(3): 254-257.
【9】LIU D, NISHIO H, NAKATA K. Anisotrop ic property of material arrangement in friction stir welding of dissimilar Mg alloys[J].Materials & Design, 2011, 32(10): 4818- 4824 .
相关信息