硅含量对TRIP600钢点焊接头质量和剪切性能的影响
Effects of Silicon Content on Quality and Sheering Property of TRIP600 Steel Spot Welding Joints
摘 要
对硅的质量分数分别为1.17%和0.56%的TRIP600钢进行了电阻点焊试验, 研究了硅含量对点焊接头质量和剪切性能的影响。结果表明: 当焊接电流为4 000～9 000 A、电极压力为3 430～4 410 N时, 高硅TRIP600钢接头的晶粒比低硅TRIP600钢的更细小, 组织更均匀, 而且前者的马氏体含量和抗剪强度也较高; 低硅TRIP钢点焊时更易粘着。
硅含量
点焊
transformation induced plasticity (TRIP) steel
silicon content
spot welding
Abstract
Resistance spot welding tests for TRIP600 steel with silicon contents of 1.17wt.% and 0.56wt.%, respectively, were carried out to study the effects of silicon content on spot welding joint quality and sheering property of TRIP600 steel. Results show that when welding current was 4 000－9 000 A, electrode pressure was 3 430－4 410 N, the TRIP600 steel joint with high silicon content had smaller grains, more uniform microstructure, higher martensite content and better shear strength than that with low silicon content. The TRIP steel with low silicon content was easily adhered during spot welding.
中图分类号 TG407
所属栏目 材料性能及其应用
基金项目
收稿日期 2012/4/5
修改稿日期 2012/12/12
网络出版日期
作者单位点击查看
备注于燕(1962-), 女, 辽宁金县人, 教授, 博士。
引用该论文: YU Yan,ZHANG Xiao-meng. Effects of Silicon Content on Quality and Sheering Property of TRIP600 Steel Spot Welding Joints[J]. Materials for mechancial engineering, 2013, 37(5): 73～75
于燕,张小盟. 硅含量对TRIP600钢点焊接头质量和剪切性能的影响[J]. 机械工程材料, 2013, 37(5): 73～75
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】闫翠, 李麟, 符仁钰, 等. TRIP钢的研究进展[J].上海金属, 2008, 30(4): 40-42.
【2】李振, 赵爱民, 曹佳丽, 等.高强中锰TRIP钢的残余奥氏体含量及其稳定性[J].机械工程材料, 2012, 36(1): 62-64.
【3】ZHANG J C, FU R Y, ZHANG M, et al. Bake hardening behavior of TRIP and DP steels[J].Journal of University of Science and Technology Beijing, 2008, 15(2): 132 -137.
【4】高绪涛, 张明明, 赵爱民.控冷工艺对热轧TRIP钢组织和性能的影响[J].机械工程材料, 2011, 35(11): 23-25.
【5】熊自柳, 蔡庆伍, 江海涛, 等.TRIP1000钢显微组织及不同组织的变形行为[J].机械工程材料, 2010, 34(10): 16-18.
【6】熊自柳, 江海涛, 蔡庆伍, 等.消除TRIP钢屈服平台的预拉伸实验及微观机理[J].北京科技大学学报, 2008, 30(4): 379-382.
【2】李振, 赵爱民, 曹佳丽, 等.高强中锰TRIP钢的残余奥氏体含量及其稳定性[J].机械工程材料, 2012, 36(1): 62-64.
【3】ZHANG J C, FU R Y, ZHANG M, et al. Bake hardening behavior of TRIP and DP steels[J].Journal of University of Science and Technology Beijing, 2008, 15(2): 132 -137.
【4】高绪涛, 张明明, 赵爱民.控冷工艺对热轧TRIP钢组织和性能的影响[J].机械工程材料, 2011, 35(11): 23-25.
【5】熊自柳, 蔡庆伍, 江海涛, 等.TRIP1000钢显微组织及不同组织的变形行为[J].机械工程材料, 2010, 34(10): 16-18.
【6】熊自柳, 江海涛, 蔡庆伍, 等.消除TRIP钢屈服平台的预拉伸实验及微观机理[J].北京科技大学学报, 2008, 30(4): 379-382.
相关信息