铸态中碳高硼合金钢的三体磨料磨损特性
Three Body Abrasive Wear Characteristics of Cast Medium Carbon High Boron Alloy Steels
摘 要
采用光学显微镜、扫描电镜、自制的三体磨料磨损试验机研究了铸态中碳高硼合金钢的组织、性能与三体磨料磨损特性。结果表明: 随硼含量的增大, 试验钢中硬质相的体积分数增大, 试验钢硬度提高、冲击性能降低、硬质相数量和尺寸的增大都对抵抗磨料切削和犁削变形有利; 基体主要因微观切削和塑变而造成磨损, 硬质相表现出断裂磨损机制; 低载荷时变形的基体堆积较多而磨损量小, 高载荷时硼碳化合物断裂加快而使磨损量增大。
高硼合金
硼碳化合物
磨损机制
three-body abrasive wear
high boron alloy
boron carbon compound
wear mechanism
Abstract
The microstructure, performance and three body abrasive wear characteristics of the cast medium carbon high boron steels were studed by optical microscopy, scanning electron microscopy (SEM) and self-made three body abrasive wear tester. The results show that when the boron content increased, volume fraction of hard-phas, hardness and wear resistance of the test steel increased, but impact toughness reduced. The increase of hard-phase quantity and size was good to resist abrasive cutting and furrow deformation. The wear of matrix was mainly attributed to micro-cutting and plastic deformation, and the hard-phase showed fracture wear mechanism. Small wear rate was given in low load as a lot of deformed matrix cumulated, but fracture of the boron carbon compounds accelerated in high load leading to the rapid increase of wear rate.
中图分类号 TG142.1
所属栏目 材料性能及其应用
基金项目 国家自然科学基金资助项目(51171073); 云南省校科技合作专项(2010AD012); 教育部博士学科点专项基金资助项目(20115314120002)
收稿日期 2012/4/28
修改稿日期 2013/2/25
网络出版日期
作者单位点击查看
备注李日良(1987-), 男, 广西桂平人, 硕士研究生。
引用该论文: LI Ri-liang,CEN Qi-hong,JIANG Ye-hua,LI Zu-lai. Three Body Abrasive Wear Characteristics of Cast Medium Carbon High Boron Alloy Steels[J]. Materials for mechancial engineering, 2013, 37(6): 63～67
李日良,岑启宏,蒋业华,李祖来. 铸态中碳高硼合金钢的三体磨料磨损特性[J]. 机械工程材料, 2013, 37(6): 63～67
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】马陟祚, 龙锐, 魏世忠.高钒高速钢的冲击磨料磨损性能试验[J].铸造, 2005, 54(6): 549-552.
【2】邵抗振, 赵俊丽.高钒高速钢复合锤头铸造工艺及其性能[J].特种铸造及有色合金, 2009, 29(8): 748-750.
【3】陈慧敏, 王悔改, 徐流杰.回火温度对高钒高速钢耐磨性的影响[J].铸造技术, 2009, 30(8): 1010-1013.
【4】刘海峰, 刘耀辉, 于思荣.高碳高钒系高速钢的耐磨性研究[J].摩擦学学报, 2009, 20(6): 401-406.
【5】杜忠泽, 李萍, 符寒光, 等.热处理对高钒高速钢组织和性能的影响[J].金属热处理, 2009, 34(5): 32-34.
【6】李萍, 杜忠泽, 符寒光, 等.热处理温度对高钒高速钢显微组织和硬度的影响[J].机械工程材料, 2009, 33(6): 93-95.
【7】徐流杰, 魏世忠, 张永振, 等.轧辊用高钒高速钢的滚-滑动磨损性能及失效行为研究[J].摩擦学学报, 2009, 29(1): 55-60.
【8】程巨强.正火温度对ZG30CrMn2Si2NiMo组织和力学性能的影响[J].热加工工艺, 2005(6): 61-62.
【9】段江涛, 符寒光, 蒋志强, 等.抗磨Fe-B-C合金材料的研究[J].润滑与密封, 2007, 32(3): 165-168.
【10】刘赛业, 陈越, 龙锐, 等.Fe-B-C耐磨合金的研究进展及展望[J].铸造技术, 2007, 28(11): 1526-1530.
【11】本溪钢铁公司.硼钢[M].北京: 冶金工业出版社, 1977.
【12】刘海明.中碳高硼铁基耐磨合金组织与性能的研究[D].西安: 长安大学, 2008.
【13】李祖来, 蒋业华, 周荣.WC颗粒增强铁基表面复合材料的三体磨料磨损性能研究[J].中国机械工程, 2006, 17(18): 1967-1971.
【14】刘仲礼, 李言祥, 陈祥, 等.硼、碳含量对高硼铁基合金组织和性能的影响[J].钢铁, 2007, 42(6): 78-82.
【15】龚建勋, 李丹, 肖逸锋, 等.Fe-Cr-B-C堆焊合金的显微组织及耐磨性[J].材料热处理学报, 2010, 31(3): 136-141.
【16】MA S Q, XING J D, FU H G, et al. Microstructure and crystallography of borides and secondary precipitation in 18 wt.% Cr-4 wt.% Ni-1 wt.% Mo-3.5 wt.% B-0.27 wt.% C steel[J].Acta Materialia, 2012, 60: 831-843.
【17】RICHARDSON R C D. The wear of metals by hard abrasives[J].Wear, 1967, 10: 291-294.
【18】YI D W XING J D, MA S Q, et al. Three-body abrasive wear behavior of low carbon Fe-B cast alloy and its microstructures under different casting process[J].Tribol Lett, 2011, 42: 67-77.
【2】邵抗振, 赵俊丽.高钒高速钢复合锤头铸造工艺及其性能[J].特种铸造及有色合金, 2009, 29(8): 748-750.
【3】陈慧敏, 王悔改, 徐流杰.回火温度对高钒高速钢耐磨性的影响[J].铸造技术, 2009, 30(8): 1010-1013.
【4】刘海峰, 刘耀辉, 于思荣.高碳高钒系高速钢的耐磨性研究[J].摩擦学学报, 2009, 20(6): 401-406.
【5】杜忠泽, 李萍, 符寒光, 等.热处理对高钒高速钢组织和性能的影响[J].金属热处理, 2009, 34(5): 32-34.
【6】李萍, 杜忠泽, 符寒光, 等.热处理温度对高钒高速钢显微组织和硬度的影响[J].机械工程材料, 2009, 33(6): 93-95.
【7】徐流杰, 魏世忠, 张永振, 等.轧辊用高钒高速钢的滚-滑动磨损性能及失效行为研究[J].摩擦学学报, 2009, 29(1): 55-60.
【8】程巨强.正火温度对ZG30CrMn2Si2NiMo组织和力学性能的影响[J].热加工工艺, 2005(6): 61-62.
【9】段江涛, 符寒光, 蒋志强, 等.抗磨Fe-B-C合金材料的研究[J].润滑与密封, 2007, 32(3): 165-168.
【10】刘赛业, 陈越, 龙锐, 等.Fe-B-C耐磨合金的研究进展及展望[J].铸造技术, 2007, 28(11): 1526-1530.
【11】本溪钢铁公司.硼钢[M].北京: 冶金工业出版社, 1977.
【12】刘海明.中碳高硼铁基耐磨合金组织与性能的研究[D].西安: 长安大学, 2008.
【13】李祖来, 蒋业华, 周荣.WC颗粒增强铁基表面复合材料的三体磨料磨损性能研究[J].中国机械工程, 2006, 17(18): 1967-1971.
【14】刘仲礼, 李言祥, 陈祥, 等.硼、碳含量对高硼铁基合金组织和性能的影响[J].钢铁, 2007, 42(6): 78-82.
【15】龚建勋, 李丹, 肖逸锋, 等.Fe-Cr-B-C堆焊合金的显微组织及耐磨性[J].材料热处理学报, 2010, 31(3): 136-141.
【16】MA S Q, XING J D, FU H G, et al. Microstructure and crystallography of borides and secondary precipitation in 18 wt.% Cr-4 wt.% Ni-1 wt.% Mo-3.5 wt.% B-0.27 wt.% C steel[J].Acta Materialia, 2012, 60: 831-843.
【17】RICHARDSON R C D. The wear of metals by hard abrasives[J].Wear, 1967, 10: 291-294.
【18】YI D W XING J D, MA S Q, et al. Three-body abrasive wear behavior of low carbon Fe-B cast alloy and its microstructures under different casting process[J].Tribol Lett, 2011, 42: 67-77.
相关信息