复合能场对铸轧AZ61镁合金板组织和力学性能的影响
Effects of Compound Energy Field on Microstructure and Mechanical Properties of Roll-Casted AZ61 Magnesium Alloy Strip
摘 要
在AZ61镁合金板的铸轧过程中引入电磁场和超声场的复合能场, 研究了复合能场对其组织和力学性能的影响。结果表明: 施加复合能场能够有效细化AZ61镁合金板的晶粒和均匀组织, 改善第二相在基础相上的分布, 减小铸轧板力学性能的各向异性; 与普通铸轧镁合金板相比, 复合能场铸轧镁合金板的抗拉强度、屈服强度、伸长率和硬度均有大幅提高, 分别为266.13 MPa, 167.67 MPa, 3.53%, 79.84 HV。
铸轧
电磁超声复合能场
显微组织
力学性能
AZ61 magnesium alloy
casting and rolling
electromagnetic and ultasonic compound energy field
microstructure
machenical property
Abstract
Electromagnetic ultrasonic compound energy-field were introduced in the casting and rolling process of AZ61 magnesium alloy strip, and the effects of compound energy field on the microstructure and mechanical property of the alloy were studied. The results show compound energy field could refine grain and homogenize microstructure for AZ61 magnesium alloy strip, and improve the distribution of the second phase on the basis phase, effectively, decrease the mechanical anisotropy of roll-casted strip. Comparing with the ordinary roll-casted magnesium alloy strip, the tensile strength, yield strength, elongation and hardness of the compouond energy field roll-casted magnesium alloy strip were increased obviously, and they were 266.13 MPa, 167.67 MPa, 3.53%, and 79.84 HV, respectively.
中图分类号 TG146
所属栏目 新材料新工艺
基金项目 国家重点基础研究发展(973)计划项目(2012CB619504)
收稿日期 2013/1/10
修改稿日期 2013/9/7
网络出版日期
作者单位点击查看
备注黄元春(1966-), 男, 四川成都人, 副教授, 博士。
引用该论文: HUANG Yuan-chun,LIU Yu,ZHANG Huan-huan,YAN Xu-yu,LI Qing. Effects of Compound Energy Field on Microstructure and Mechanical Properties of Roll-Casted AZ61 Magnesium Alloy Strip[J]. Materials for mechancial engineering, 2013, 37(11): 87～91
黄元春,刘宇,张欢欢,颜徐宇,李青. 复合能场对铸轧AZ61镁合金板组织和力学性能的影响[J]. 机械工程材料, 2013, 37(11): 87～91
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】谭湘夫, 毛大恒, 仇灵, 等.超声电磁复合场对AZ31B镁合金铸轧板带组织性能的影响[J].中国机械工程, 2010, 21(23): 2865-2867, 2876.
【2】杨明波, 潘复生, 丁培道, 等.镁合金双辊薄带连铸技术的研究现状及进展[J].铸造技术, 2007, 28(6): 862-866.
【3】许月旺.镁及镁合金深加工制品及其应用[C]//中国有色金属工业协会镁业分会第十二届年会论文集.鹤壁: [出版者不详], 2009: 225-231.
【4】EMLEY.Principles of magnesium technology[M].Oxford: Pergamon, 1966: 235-268.
【5】CHANG C F, DAS S K.Magnesium alloys and their applications [M].Oberursel: FRGDGM Information Sgesellschaft, 1992: 210-232.
【6】ESKIN G I. Broad prospects for commercial application of the ultrasonic (cavitation) melt treatment of light alloys[J].Ultrasonics Sonochemistry, 2001, 8(3): 319-325.
【7】李婷, 毛大恒, 李建平, 等.AZ31B镁合金电磁铸轧实验研究[J].热加工工艺, 2010, 39(15): 18-20.
【8】李建平, 胡建冰, 毛大恒, 等.超声波辅助铸轧AZ31镁合金板带的实验研究[J].华中科技大学学报: 自然科学版, 2010, 38(12): 126-128.
【9】冯海阔, 于思荣.超声波在冶金及金属基复合材料制备过程中的应用[J].特种铸造及有色合金, 2006, 26(1): 31-33.
【10】吴迪.AZ61镁合金双辊铸轧工艺研究[D].沈阳: 东北大学: 2008.
【11】谭湘夫, 毛大恒, 蔡安辉, 等.镁合金板带双辊连续铸轧试验研究[J].机械工程学报, 2012, 48(16): 30-35.
【12】赵啸林, 毛大恒, 李晓谦, 等.铝电磁铸轧液固区中流体行为[J].上海有色金属, 2001, 22(2): 49-53.
【13】张世斌, 李伟轩, 邓康, 等.电磁连铸对镁合金凝固和偏析的影响[J].稀有金属材料与工程, 2007, 36(12): 2236-2239.
【14】许光明, 郑佳伟, 刘勇, 等.电磁场作用下溶质元素在镁合金AZ61的分布[J].物理学报, 2007, 56(7): 4247-4251.
【15】于勇.AZ31B镁合金板材拉伸力学性能的各向异性研究[D].大连: 大连海事大学, 2009.
【2】杨明波, 潘复生, 丁培道, 等.镁合金双辊薄带连铸技术的研究现状及进展[J].铸造技术, 2007, 28(6): 862-866.
【3】许月旺.镁及镁合金深加工制品及其应用[C]//中国有色金属工业协会镁业分会第十二届年会论文集.鹤壁: [出版者不详], 2009: 225-231.
【4】EMLEY.Principles of magnesium technology[M].Oxford: Pergamon, 1966: 235-268.
【5】CHANG C F, DAS S K.Magnesium alloys and their applications [M].Oberursel: FRGDGM Information Sgesellschaft, 1992: 210-232.
【6】ESKIN G I. Broad prospects for commercial application of the ultrasonic (cavitation) melt treatment of light alloys[J].Ultrasonics Sonochemistry, 2001, 8(3): 319-325.
【7】李婷, 毛大恒, 李建平, 等.AZ31B镁合金电磁铸轧实验研究[J].热加工工艺, 2010, 39(15): 18-20.
【8】李建平, 胡建冰, 毛大恒, 等.超声波辅助铸轧AZ31镁合金板带的实验研究[J].华中科技大学学报: 自然科学版, 2010, 38(12): 126-128.
【9】冯海阔, 于思荣.超声波在冶金及金属基复合材料制备过程中的应用[J].特种铸造及有色合金, 2006, 26(1): 31-33.
【10】吴迪.AZ61镁合金双辊铸轧工艺研究[D].沈阳: 东北大学: 2008.
【11】谭湘夫, 毛大恒, 蔡安辉, 等.镁合金板带双辊连续铸轧试验研究[J].机械工程学报, 2012, 48(16): 30-35.
【12】赵啸林, 毛大恒, 李晓谦, 等.铝电磁铸轧液固区中流体行为[J].上海有色金属, 2001, 22(2): 49-53.
【13】张世斌, 李伟轩, 邓康, 等.电磁连铸对镁合金凝固和偏析的影响[J].稀有金属材料与工程, 2007, 36(12): 2236-2239.
【14】许光明, 郑佳伟, 刘勇, 等.电磁场作用下溶质元素在镁合金AZ61的分布[J].物理学报, 2007, 56(7): 4247-4251.
【15】于勇.AZ31B镁合金板材拉伸力学性能的各向异性研究[D].大连: 大连海事大学, 2009.
相关信息