Rapid Screening of Refractory Materials Containing Zirconia Fiber by X-ray Diffraction Method
摘 要
采用X射线衍射法快速筛选出含氧化锆纤维的耐火材料,并用偏光显微镜对其进行确认。探讨了扫描速度、发射狭缝和衍射角对结果的影响,优化的试验条件为:扫描速率为2°·min-1,发射狭缝为2 mm时,衍射角为30°。方法能快速地用于含氧化锆纤维的耐火材料的定性分析。
Abstract
X-ray diffraction was applied to the rapid screening of refractory materials containing zirconia fiber, and polarizing microscope was applied for further confirmation. Influential factors, including the scanning rate, emission slit and diffraction angle were discussed. The optimized experimental conditions were found as follows: scanning rate of 2°·min-1, emission slit of 2 mm and diffraction angle of 30°. The proposed method was feasible to be used in the rapid qualitative analysis of refractory materials containing zirconia fiber.
中图分类号 O657.3
所属栏目 工作简报
基金项目 山东出入境检验检疫局科研项目(2010B057)
收稿日期 2011/7/15
修改稿日期
网络出版日期
作者单位点击查看
联系人作者高源(31gy@163.com)
备注高源(1988-),男,山东青岛人,硕士研究生,主要研究方向为无机非金属材料的分析检测。
引用该论文: GAO Yuan,XU Xiao-ming,LIN Run-xiong. Rapid Screening of Refractory Materials Containing Zirconia Fiber by X-ray Diffraction Method[J]. Physical Testing and Chemical Analysis part B:Chemical Analysis, 2012, 48(8): 903~905
高源,徐小茗,林润雄. X射线衍射法快速筛选含氧化锆纤维的耐火材料[J]. 理化检验-化学分册, 2012, 48(8): 903~905
共有人对该论文发表了看法,其中:
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】余明清,范仕刚,夏淑琴,等.高绝热材料的研究[J].功能材料, 2004,35(4):1587-1589.
【2】安欣林,王晓莉.纳米二氧化锆研究进展[J].内蒙古石油化工, 2007,5(5):20-22.
【3】高频.欧盟REACH法规的研究及其应对策略[J].上海化工, 2010,35(4):16-19.
【4】廖建国.粉末X射线衍射测定法[J].国外耐火材料, 2003,28(4):36-41.
【5】田志宏,张秀华,梅鸣华,等.Dmax-ⅢB型X线衍射仪在耐火材料物相分析中的应用[J].工程与试验, 2008,12(4):32-35.
【2】安欣林,王晓莉.纳米二氧化锆研究进展[J].内蒙古石油化工, 2007,5(5):20-22.
【3】高频.欧盟REACH法规的研究及其应对策略[J].上海化工, 2010,35(4):16-19.
【4】廖建国.粉末X射线衍射测定法[J].国外耐火材料, 2003,28(4):36-41.
【5】田志宏,张秀华,梅鸣华,等.Dmax-ⅢB型X线衍射仪在耐火材料物相分析中的应用[J].工程与试验, 2008,12(4):32-35.
相关信息