Q460C钢板力学性能不合格原因分析
Cause Analysis of Unqualified Mechanical Properties of Q460C Steel Plates
摘 要
利用光学显微镜和扫描电子显微镜分析了某厂生产的多个批次Q460C钢板力学性能低于GB/T 1591-2008技术要求的原因。结果表明: 钢板中心偏析造成的贝氏体组织、微裂纹、MnS以及铌和钛复合夹杂物的存在是导致该Q460C钢板力学性能不合格的主要原因; 另轧制工艺控制不当造成的魏氏体组织也会降低钢板的力学性能。
力学性能
贝氏体组织
魏氏组织
夹杂物
微裂纹
Q460C steel plate
mechanical property
bainite structure
widmanstatten structure
inclusion
tiny crack
Abstract
Reasons of mechanical properties of multiple batches of Q460C steel plates produced by a steel plant lower than the requirement of GB/T 1591-2008 were analyzed through optical microscope and scanning electron microscope. The results show that the bainite structure, tiny cracks and MnS inclusions as well as Nb and Ti compound inclusions caused by center segregation were the main reasons for the unqualified mechanical properties of Q460C steel plates. And widmanstatten structure caused by improper rolling technics also lowered the mechanical properties of the Q460C steel plates.
中图分类号 TG335
所属栏目
基金项目
收稿日期 2010/3/22
修改稿日期
网络出版日期
作者单位点击查看
备注孙胜英(1981-),女,工学硕士。
引用该论文: SUN Sheng-ying,ZHANG Zhi-jie,JIN Fang-fang,ZHANG Hai-wang. Cause Analysis of Unqualified Mechanical Properties of Q460C Steel Plates[J]. Physical Testing and Chemical Analysis part A:Physical Testing, 2011, 47(2): 120～122
孙胜英,张志杰,靳芳芳,张海旺. Q460C钢板力学性能不合格原因分析[J]. 理化检验－物理分册, 2011, 47(2): 120～122
被引情况:
【1】杨建平,李雪洁,赵亚娟, "Q345B钢板拉伸性能不合格原因分析",理化检验－物理分册 50, 448-452(2014)
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】崔忠圻. 金属学与热处理[M]. 北京:机械工业出版社,1999:211-215.
【2】王杰, 杜恒科, 赵坤. 中心偏析对高锰钢中厚板力学性能的影响[J]. 物理测试,2009,27(2): 13-17.
【2】王杰, 杜恒科, 赵坤. 中心偏析对高锰钢中厚板力学性能的影响[J]. 物理测试,2009,27(2): 13-17.
相关信息