汽轮机组中压内缸螺栓断裂原因分析
Fracture Reason Analysis for Intermediate Pressure Inner Casing Bolt of Steam Turbine
摘 要
通过宏观和微观观察、力学性能测试以及断口分析等方法对汽轮机组中压内缸螺栓断裂的原因进行了分析。结果表明:螺栓断裂的性质属于脆性蠕变断裂, 主要原因为螺栓的材料质量问题和承载过大。
中压内缸
螺栓
断裂
材料质量
承载
steam turbine
intermediate pressure inner casing
bolt
fracture
material quality
load
Abstract
By means of macro and micro observation, mechanical property testing, fracture analysis and so on, the fracture reason of the bolts of intermediate pressure inner casing of steam turbine has been investigated. The results showed that the fracture mechanism was brittle creep rupture and the main influencing factors of which can be confirmed as material quality issue and excessive load.
中图分类号 TK263.3
所属栏目
基金项目
收稿日期 2010/9/8
修改稿日期
网络出版日期
作者单位点击查看
备注贺锡鹏(1979-), 男, 工程师。
引用该论文: HE Xi-peng,ZHANG Lei,MA Hong,CHEN Ji-gang,LIANG Feng,TANG Li-ying. Fracture Reason Analysis for Intermediate Pressure Inner Casing Bolt of Steam Turbine[J]. Physical Testing and Chemical Analysis part A:Physical Testing, 2011, 47(7): 454～458
贺锡鹏,张磊,马红,陈吉刚,梁锋,唐丽英. 汽轮机组中压内缸螺栓断裂原因分析[J]. 理化检验－物理分册, 2011, 47(7): 454～458
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】崔约贤, 王长利.金属断口分析[M].哈尔滨: 哈尔滨工业大学出版社, 1998:76-80.
【2】DL/T 439-2006火力发电厂高温紧固件技术导则[S].
【3】欧蓉.浅析高温螺栓钢20Cr11Mo1VNbTiB粗晶现象及其控制[J].特钢技术, 2005(2):17-19.
【2】DL/T 439-2006火力发电厂高温紧固件技术导则[S].
【3】欧蓉.浅析高温螺栓钢20Cr11Mo1VNbTiB粗晶现象及其控制[J].特钢技术, 2005(2):17-19.
相关信息