线材拉拔断裂原因分析
Fracture Reason Analysis of Wire Drawing
摘 要
归纳了线材拉拔断裂的常见原因, 总结了线材失效分析的步骤, 并将线材拉拔断裂分为两大类: 一是断裂源起源于外表面(包括线纹、折叠、钢坯上裂纹、皮下气泡和非金属夹杂物等); 二是断裂源产生于内部(包括中心夹杂物、中心缩孔、中心马氏体和中心网状碳化物等), 并举例进行了说明。
拉拔断裂
断口
显微组织
wire
drawing fracture
fracture
microstructure
Abstract
Common causes and failure analysis procedure of wire drawing fracture were illuminated, and fracture mode had been divided into two types, one was crack initiation sites at surface of wire rod (including cord design, folding, crack on billet steel, subcutaneous bubble, inclusion and so on), the others at interior of hard wire (including inclusion, central shrinkage cavity, central martensite, central net carbide and so on), which explained by examples.
中图分类号 TG356.4
所属栏目
基金项目
收稿日期 2010/11/9
修改稿日期
网络出版日期
作者单位点击查看
备注冯岩青(1977-), 女, 工程师,博士研究生。
引用该论文: FENG Yan-qing. Fracture Reason Analysis of Wire Drawing[J]. Physical Testing and Chemical Analysis part A:Physical Testing, 2011, 47(9): 557～561
冯岩青. 线材拉拔断裂原因分析[J]. 理化检验－物理分册, 2011, 47(9): 557～561
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】张萍, 孙宜强.72B钢盘条断裂及断口分析[J].物理测试,2006, 24(6):38-40.
【2】那靛,李飞,王全礼.SWRH82B盘条断裂原因分析[J].首钢技术,2001,2:37-39.
【3】龚桂仙,杨志婷.82B盘条断裂分析[J].武钢技术,2001, 1:29-31.
【4】牛亚然, 陈光, 黄一新.77MnA盘条断裂原因分析[J].金属成形工艺,2004, 22(1):14-16.
【5】龚桂仙,李建华.77MnA盘条断裂分析[J].科研与生产,2002, 40(5): 17-19.
【6】元丰友.SWRH82B盘条脆断原因分析[J].金属制品, 2005, 31(6): 28-29.
【7】崔约贤,王长利.金属断口分析[M].哈尔滨:哈尔滨工业大学出版社,1998.
【8】傅国如,张峥.失效分析技术[J].理化检验-物理分册,2005,41(4):212-216.
【9】傅国如,张峥.失效分析技术(续)[J].理化检验-物理分册,2005,41(4):318-323.
【2】那靛,李飞,王全礼.SWRH82B盘条断裂原因分析[J].首钢技术,2001,2:37-39.
【3】龚桂仙,杨志婷.82B盘条断裂分析[J].武钢技术,2001, 1:29-31.
【4】牛亚然, 陈光, 黄一新.77MnA盘条断裂原因分析[J].金属成形工艺,2004, 22(1):14-16.
【5】龚桂仙,李建华.77MnA盘条断裂分析[J].科研与生产,2002, 40(5): 17-19.
【6】元丰友.SWRH82B盘条脆断原因分析[J].金属制品, 2005, 31(6): 28-29.
【7】崔约贤,王长利.金属断口分析[M].哈尔滨:哈尔滨工业大学出版社,1998.
【8】傅国如,张峥.失效分析技术[J].理化检验-物理分册,2005,41(4):212-216.
【9】傅国如,张峥.失效分析技术(续)[J].理化检验-物理分册,2005,41(4):318-323.
相关信息