叉车门架断裂原因分析
Fracture Reason Analysis of Forklift Mast
摘 要
采用化学成分分析、力学性能测试、金相检验以及断口分析等方法对某叉车门架断裂的原因进行了分析。结果表明: 由于在门架焊缝收弧部位存在凹坑缺陷和裂纹, 形成缺口效应, 产生缺口应力集中, 加之门架的不对称工作应力的作用, 最终造成门架发生了疲劳断裂失效。
缺口应力集中
疲劳断裂
forklift mast
notch stress concentration
fatigue fracture
Abstract
The fracture reason of the forklift mast was analyzed by means of chemical composition analysis, mechanical property testing, metallographic examination, fracture analysis and so on. The results showed that the pit defect and cracks existed in weld crater parts of the mast, the pit defect and cracks formed notch effect and stress concentration. Furthermore, the mast worked under the asymmetric stress, at last the fatigue fracture occurred in mast.
中图分类号 TH242
所属栏目
基金项目
收稿日期 2011/3/10
修改稿日期
网络出版日期
作者单位点击查看
备注冯凌超(1984-), 男, 助理工程师, 学士。
引用该论文: FENG Ling-chao,ZHANG Li-hua. Fracture Reason Analysis of Forklift Mast[J]. Physical Testing and Chemical Analysis part A:Physical Testing, 2011, 47(9): 579～582
冯凌超,张立华. 叉车门架断裂原因分析[J]. 理化检验－物理分册, 2011, 47(9): 579～582
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】任颂赞,张静江,陈质如,等.钢铁金相图谱[M].上海:上海科学技术文献出版社, 2003.
【2】桂立丰.机械工程材料测试手册(物理金相卷)[M]. 沈阳:辽宁科学技术出版社, 1999.
【3】上海交通大学金属断口分析编写组.金属断口分析[M].北京: 国防工业出版社, 1979.
【4】机械设计手册编委会.机械设计手册(单行本疲劳强度设计)[M].北京:机械工业出版社, 2007.
【2】桂立丰.机械工程材料测试手册(物理金相卷)[M]. 沈阳:辽宁科学技术出版社, 1999.
【3】上海交通大学金属断口分析编写组.金属断口分析[M].北京: 国防工业出版社, 1979.
【4】机械设计手册编委会.机械设计手册(单行本疲劳强度设计)[M].北京:机械工业出版社, 2007.
相关信息